In the method for manufacturing the sintered rare earth magnet, sintering is performed to a material composed of: a flake-shaped polycrystal phase that is produced by rapidly solidifying alloy melt of a rare earth magnet composition, and whose average crystal grain size is 10-200 nm; and a low melting point phase that is formed on a surface of the polycrystal phase and whose melting point is lower than that of the polycrystal phase.例文帳に追加

希土類磁石組成の合金溶湯の急冷凝固により作製した平均結晶粒径１０〜２００ｎｍの薄片状の多結晶相と、該多結晶相の表面に形成され、該多結晶相より融点が低い低融点相とから成る原料を焼結することを特徴とする焼結希土類磁石の製造方法。 - 特許庁

A manufacturing method includes a first step of depositing at least one of Dy and Tb on at least part of a surface of an iron-boron-rare earth-based sintered magnet S and a second step of thermally treating at a predetermined temperature to diffuse at least one of Dy and Tb into the crystal intergranular phase of the magnet.例文帳に追加

鉄−ホウ素−希土類系の焼結磁石Ｓの表面の少なくとも一部に、Ｄｙ、Ｔｂの少なくとも一方を付着させる第一工程と、所定温度下で熱処理を施して焼結磁石の表面に付着したＤｙ、Ｔｂの少なくとも一方を焼結磁石の結晶粒界相に拡散させる第二工程とを実施する。 - 特許庁

A manufacturing method of an anisotropic nano-crystalline rare earth magnet includes: a step of preparing powder of a nano-crystalline and/or amorphous rare earth magnet alloy; a step of sintering the powder; a first heat treatment step of heat-treating the obtained sintered body; and a step of performing hot hard working.例文帳に追加

異方性でナノ結晶質の希土類磁石の製造方法であって、 ナノ結晶質および／または非晶質の希土類磁石合金の粉末を準備する工程、 上記粉末を焼結する工程、 得られた焼結体を熱処理する第１熱処理工程、 次いで熱間強加工を行なう工程を含むことを特徴とする希土類磁石の製造方法。 - 特許庁

The ring periphery of the ring-type sintered magnet 10 is made circular, and also for the ring internal circumference, recesses 20 and protrusions 30 are made periodically in its circumferential direction, and magnetic poles of N poles and S poles are made alternately in the circumferential direction of the ring, and the boundaries between the magnetic poles are made in the region of recesses 20 thin in magnet thickness.例文帳に追加

リング型焼結磁石１０のリング外周は円形状に形成されるとともに、リング内周はその周方向に凹部２０及び凸部３０が周期的に形成され、リング周方向にＮ極及びＳ極の磁極が交互に形成されており、磁極の境界が磁石厚さの薄い凹部２０の領域に形成されている。 - 特許庁

In this sintered porous bearing slidably supporting a rotary shaft S on a bearing surface 11 of a bearing member 1, a bond magnet 3 is integrally joined and formed by injection molding on a surface portion of the bearing member 1 so as to not contact the rotary shaft S.例文帳に追加

回転軸Ｓを軸受部材１の軸受面１１に摺動支持する焼結多孔質軸受において、軸受部材１の表面部分にボンド磁石３が射出成形により回転軸Ｓと接しないよう一体に接合形成されている。 - 特許庁

An R-Fe-B-based rare-earth sintered magnet body, which has, as the main phase, R_2Fe_14B type compound crystal grains containing a light rare-earth element RL (at least one of Nd and Pr) as a main rare-earth element, is first prepared R.例文帳に追加

まず軽希土類元素ＲＬ（ＮｄおよびＰｒの少なくとも１種）を主たる希土類元素Ｒとして含有するＲ_2Ｆｅ_14Ｂ型化合物結晶粒を主相として有するＲ−Ｆｅ−Ｂ系希土類焼結磁石体を用意する。 - 特許庁

To provide a powder filling orientation device and a press forming device using the powder filling orientation device, a powder filling orientation method and a sintered magnet manufacturing method using the powder filling orientation method, capable of obtaining a high magnetic property since a desired orientation is permitted at low cost.例文帳に追加

低コストで所望の配向が可能になり高い磁気特性が得られる、粉末充填配向装置およびそれを用いたプレス成形装置、ならびに粉末充填配向方法およびそれを用いた焼結磁石製造方法を提供する。 - 特許庁

To efficiently form a main phase crystal grain, in which heavy rare earth element RH is condensed in an outer shell portion, inside an R-Fe-B rare earth elements sintered magnet body too and to enhance the coercive force while suppressing reduction of a residual magnetic flux density.例文帳に追加

外殻部に重希土類元素ＲＨが濃縮された主相結晶粒をＲ−Ｆｅ−Ｂ系希土類焼結磁石体の内部にも効率よく形成し、残留磁束密度の低下を抑制しつつ保磁力を向上させる。 - 特許庁

A conversion coating (not containing phosphorus) containing at least Zr, Nd, fluorine, and oxygen as constituent elements is directly applied on the surface of the R-Fe-B sintered magnet (R represents rare-earth elements, including at least Nd).例文帳に追加

Ｒ−Ｆｅ−Ｂ系焼結磁石（Ｒは少なくともＮｄを含む希土類元素）の表面に、構成元素としてＺｒ、Ｎｄ、フッ素、酸素を少なくとも含有する化成被膜（但しリンは含有しない）を直接的に有することを特徴とする。 - 特許庁

To provide a method for manufacturing a rare-earth alloy powder for a sintered magnet, which reduces an amount of oxygen taken into the powder of a cast alloy, avoids a decrease of an adulterant effect and a decrease of sinterability, and prevents a lowering of residual magnetization.例文帳に追加

鋳造合金の粉末中に取り込まれる酸素量を低減し、不純物効果の低下および焼結性の低下を回避し、残留磁化の低下を防ぐことができる焼結磁石用希土類合金粉末の製造方法の提供。 - 特許庁

To provide a process for producing a rare earth sintered magnet having excellent fluidity efficiently while enhancing dimensional precision and productivity of a molding without lowering characteristics significantly.例文帳に追加

優れた流動性を有する顆粒を効率よく作製し、成形体の寸法精度の向上及び生産性の向上を図るとともに、特性を大きく低下させることなく希土類焼結磁石を製造する方法等を提供することを目的とする。 - 特許庁

A ferrite sintered magnet 1 is produced by calcining a molding that is produced by injection molding a mixture of magnetic powder obtained by mixing a magnetic powder and a binder resin, for example, into a mold applied with a magnetic field.例文帳に追加

フェライト焼結磁石１は、例えば、磁性粉末とバインダ樹脂とを混合して得られた磁性粉末混合物を、磁場を印加した金型の内部に射出成形して成形体を作製し、この成形体を焼成することによって製造される。 - 特許庁

The powder of the hard magnetic body whose particle diameter is smaller than that of the SmFeN powder is inserted into the air gap of the SmFeN powder at the intermediate section, so that the difference of density is reduced between the peripheral edge section and intermediate section of the manufactured SmFeN system sintered magnet.例文帳に追加

中間部において、ＳｍＦｅＮの粉末の空隙にＳｍＦｅＮの粉末よりも粒径が小さい硬磁性体の粉末が入り込むので、製造されたＳｍＦｅＮ系の焼結磁石は、周縁部と中間部の密度の差が小さい。 - 特許庁

To efficiently form a main phase crystal grain in which heavy rare earth elements RH are concentrated in an outer shell even in an inner of an R-Fe-B based rare earth sintered magnet object, to improve coercive force while deterioration of residual magnetic flux density is controlled, and to improve corrosive resistance.例文帳に追加

外殻部に重希土類元素ＲＨが濃縮された主相結晶粒をＲ−Ｆｅ−Ｂ系希土類焼結磁石体の内部にも効率よく形成し、残留磁束密度の低下を抑制しつつ保磁力を向上させる。 - 特許庁

The method for manufacturing the green compact for the sintered magnet containing a rare earth element comprises sticking ultrasonic vibrators 1 and 2 onto the die body 11 of a press die 10, and pressing the magnetic powder M in a magnetic field while ultrasonically vibrating the powder filled in the press die 10.例文帳に追加

プレス型１０の外型１１に、超音波振動子１，２を貼着して、上記プレス型１０内に充填された磁性粉Ｍに超音波振動を与えながら磁場中プレスして希土類焼結磁石用の圧粉体を作製するようにした。 - 特許庁

To provide a method of manufacturing a ferrite magnet by which the pass of a dispersion medium in slurry is reduced in order to shorten hours required in a molding step and the elution of metallic ions to the dispersion medium is suppressed in order to reduce the occurrence of pin holes in a sintered compact.例文帳に追加

成形工程の時間短縮のためスラリーの分散媒の抜けを改善できる、さらには焼結体のピンホール低減のため分散媒に金属イオンが溶出するのを抑制できるフェライト磁石の製造方法を提供する。 - 特許庁

In the method where the molten metal of a coarse alloy is melted, the molten metal is cast into an alloy lump, the alloy lump is subjected to coarse grinding and is thereafter subjected to fine pulverization, and the obtained powder is subjected to powder compaction, and the compacted part is sintered, so as to produce a sintered rare earth magnet alloy, the fine pulverization is performed for two or more times.例文帳に追加

粗合金の溶湯を溶製し，この溶湯を合金塊に鋳造し，この合金塊を粗粉砕したあと更に微粉砕し，得られた粉末を用いて圧粉成形し，この成形品を焼結して，焼結希土類磁石合金を製造する方法において，前記の微粉砕を２回以上実施することを特徴とする焼結希土類磁石合金の製造法である。 - 特許庁

The holding unit 12 rotates the sintered magnet 100 in a direction of an arrow C1 around a rotation shaft S1, and the grinding wheel unit 14 rotates the grinding wheel 50 in a direction of an arrow C2 around a rotation shaft S2 inclined by 90° relative to the rotation shaft S1.例文帳に追加

保持ユニット１２は回転軸Ｓ１を中心として焼結磁石１００を矢印Ｃ１方向に回転させ、砥石ユニット１４は回転軸Ｓ１に対して９０°傾く回転軸Ｓ２を中心として砥石５０を矢印Ｃ２方向に回転させる。 - 特許庁

To provide a plating method that prevents the reprecipitation of a component having eluted into a plating liquid from a rare-earth sintered magnet of an article to be plated, and inhibits the degradation of the adhesiveness and reliability of a plated film, and to provide a plating apparatus.例文帳に追加

めっき対象物である希土類焼結磁石等からめっき液に溶出した成分の再析出を防止し、めっき膜の密着性や信頼性の低下を抑制することのできるめっき方法、めっき装置を提供することを目的とする。 - 特許庁

By successively acting the lines of magnetic force in different directions to the alloy powder P in this way, the orientation of the alloy powder P is changed for a plurality of times, and the orientation properties thereof are increased, thus the R-T-B-based sintered magnet having high residual magnetic flux density Br is obtained.例文帳に追加

このように、合金粉末Ｐに対し、異なる方向の磁力線を順次作用させることで合金粉末Ｐの向きを複数回変化させ、その配向性を高め、残留磁束密度Ｂｒの高いＲ−Ｔ−Ｂ系焼結磁石を得る。 - 特許庁

To provide a lubricant removing method which efficiently removes a lubricant from a molded matter, and can obtain a high magnetic characteristic, while controlling a deformation after sintering and an occurrence of a crack; and to provide a rare earth sintered magnet manufacturing method.例文帳に追加

成形体から効率よく潤滑剤を除去し、かつ焼結後の変形及びクラックの発生を抑制しつつ、高い磁気特性を得ることのできる潤滑剤の除去方法及び希土類焼結磁石の製造方法を提供することを目的とする。 - 特許庁

After depositing and forming a film comprising Al or its alloy whose hydrogen content is ≥50 ppm on a surface of the R-Fe-B based sintered magnet, peening treatment is executed to the deposited and formed film comprising Al or its alloy.例文帳に追加

Ｒ−Ｆｅ−Ｂ系焼結磁石の表面に、水素含有量が５０ｐｐｍ以上のＡｌまたはその合金からなる被膜を蒸着形成した後、蒸着形成されたＡｌまたはその合金からなる被膜に対してピーニング処理を行うことを特徴とする。 - 特許庁

When a rare earth sintered magnet is produced by sintering a molding of material alloy fine powder containing a rare earth element, a transition metal element and boron, sintering process is performed by high frequency induction heating under high vacuum where ultimate pressure is 10^-4 Pa or below.例文帳に追加

希土類元素、遷移金属元素及びホウ素を含む原料合金微粉を成形した成形体を焼結し、希土類焼結磁石を製造するに際し、到達圧力１０^-4Ｐａ以下の真空度で高周波誘導加熱により焼結を行う。 - 特許庁

A forming body is subjected to debindering treatment by resistance heating before sintering by discharge plasma sintering, when manufacturing a rare earth sintered magnet, by sintering the forming body for forming a raw material alloy fine powder containing a rare earth element, a transition metal element, and boron.例文帳に追加

希土類元素、遷移金属元素及びホウ素を含む原料合金微粉を成形した成形体を焼結し、希土類焼結磁石を製造するに際し、成形体を抵抗加熱により脱バインダー処理した後、放電プラズマ焼結により焼結を行う。 - 特許庁

Neodymium-iron-boron based, samarium-iron-nitrogen based or the like rare-earth magnet powder is formed arcuately by a powder metallurgical process, sintered at a high temperature and formed arcuately, and the four arcuate magnets 2 are arranged in a mold at intervals.例文帳に追加

ネオジウム−鉄−ボロン系、サマリウム−鉄−窒素系等の希土類磁性粉を粉末冶金法により円弧状に成形し、これを高温で焼結して円弧状の成形焼結品とし、この４個の円弧状磁石２を成形型内に間隔を設けて配置する。 - 特許庁

When a rare earth sintered magnet is produced by sintering a molding of material alloy fine powder containing a rare earth element, a transition metal element and boron, de-binding process is performed by ohmic-resistance heating and then sintering is performed by high frequency induction heating.例文帳に追加

希土類元素、遷移金属元素及びホウ素を含む原料合金微粉を成形した成形体を焼結し、希土類焼結磁石を製造するに際し、抵抗加熱により脱バインダー処理を行った後、高周波誘導加熱により焼結を行う。 - 特許庁

To cut a hard sintered rare earth magnet alloy having a metallic structure for surrounding a very hard ferromagnetic crystal grain composed of a crystal of a relatively large intermetallic compound by a grain boundary phase into a small part having a smooth surface with an excellent yield.例文帳に追加

比較的大きな金属間化合物の結晶からなる非常に硬質な強磁性結晶粒が粒界相で囲われている金属組織を有した硬質な焼結希土類磁石合金を歩留りよく且つ滑らかな表面をもつ小さな部品に切断する。 - 特許庁

At the time of manufacturing the magnet, the fine alloy powder is molded by adding at least one kind of fine Al powder having a mean particle diameter of ≤300 nm, fine Cu powder having a mean particle diameter of ≤80 nm, and fine Ag powder having a mean particle diameter of ≤100 nm to the fine alloy powder, and the molded body is sintered.例文帳に追加

その際、原料合金微粉に対し、平均粒径が３００ｎｍ以下のＡｌ微粉、平均粒径が８０ｎｍ以下のＣｕ微粉、平均粒径が１００ｎｍ以下のＡｇ微粉のうち少なくとも一種を添加して成形し、焼結を行う。 - 特許庁

To provide a production method of an R-Fe-B-based sintered magnet on the surface of which an anticorrosive coating, e.g. a metal coating or a resin coating, having excellent corrosion resistivity and excellent adhesion can be formed and in which a part of RL is substituted with RH.例文帳に追加

優れた耐食性を有するとともに、優れた密着性をもって金属被膜や樹脂被膜などの耐食性被膜を表面に形成することができる、ＲＬの一部がＲＨによって置換されてなるＲ−Ｆｅ−Ｂ系焼結磁石の製造方法を提供すること。 - 特許庁

A rare-earth permanent magnet has a sintered body having main-phase crystal grains composed of an R_2T_14B_1 (where R represents at least one kind of rare-earth elements and T at least one kind of transition-metal elements) phase and a grain-boundary phase containing R more than the main-phase crystal grains.例文帳に追加

Ｒ_２Ｔ_１４Ｂ_１（ただし、Ｒは希土類元素の少なくとも１種であり、Ｔは遷移金属元素の少なくとも１種である。）相からなる主相結晶粒と前記主相結晶粒よりＲを多く含有する粒界相とを有する焼結体を備える希土類永久磁石である。 - 特許庁

The burned body with a processed part is thermally treated at a temperature of 750 to below 1000°C for the formation of a ferrite sintered magnet having a magnetoplumbite crystal structure phase as a main phase.例文帳に追加

また、フェライト焼結磁石用原料粉末を成形し、焼成し、加工し、得られた加工部分を有する焼成体を750℃以上1000℃未満の温度で熱処理することを特徴とするマグネトプランバイト型結晶構造相を主相とするフェライト焼結磁石の製造方法を用いる。 - 特許庁

To obtain an R-T-B system sintered magnet having the high coercive force by further uniforming the crystal micro-structure of a raw material alloy produced with a strip casting method and making fine of the crushed power and narrow of the size distribution obtained from the raw material alloy.例文帳に追加

ストリップキャスト法で作製された原料合金の結晶組織をより均一なものとすることにより、この原料合金から得られる粉砕粉末を微細かつ粒度分布を狭くすることにより、保磁力の高いＲ−Ｔ−Ｂ系焼結磁石を得ることを目的とする。 - 特許庁

To provide a method of manufacturing a magnetically anisotropic rare earth sintered magnet and an efficient method of manufacturing products of various shapes that are effective for improving the performance of rare earth magnets, and can safely use extremely active powder in which the degree of oxidation is low and the particle diameter is extremely small.例文帳に追加

希土類磁石の高性能化に有効な、酸化の程度が低く粉末粒径が小さい極めて活性な粉末を安全に使用できる、磁気異方性希土類焼結磁石の製造方法を提供し、かつ種々の形状の製品を能率よく生産できる方法を提供する。 - 特許庁

To provide a method for manufacturing a ring type sintered magnet, which uniformizing a packed density of a magnetic powder in a ring-shaped preform body obtained by magnetic-field-orienting compaction across the whole area, with a simple method and a simple structure, and to provide a manufacturing apparatus therefor.例文帳に追加

磁場配向成形によって得られるリング状予備成形体内の磁性粉末の充填密度を、簡便な方法及び構造で全体にわたって均一にすることができるリング型焼結磁石の製造方法及び製造装置を提供することを目的とする。 - 特許庁

To reduce the strain of distribution of magnetization in rotating direction and, further, reduce cogging torque by forming recessed and projected part in the direction of outer diametral circumference and skewing the recessed and projected part into the axial direction thereof, in an ring type sintered magnet constituted of a rare earth or the like having a powerful magnetic force.例文帳に追加

強力な磁力を有する希土類等から構成されるリング型焼結磁石であって、外径円周方向に凹凸部を形成し、その凹凸部を軸方向にスキューすることにより、回転方向の磁化分布の歪を低減した上でさらにコギングトルクを低減することを目的とする。 - 特許庁

With an oxide of Fe, Co, and Mn, a hydroxide, a carbonate, or a nitrate as a raw material, a sintered magnet including a structure where a magnetic phase in a fine prism shape and a nonmagnetic phase in a prism shape are disposed alternately by utilizing spinodal decomposition is obtained, thus solving the problem.例文帳に追加

Ｆｅ、ＣｏおよびＭｎの酸化物、水酸化物、炭酸塩または硝酸塩を原料とし、スピノーダル分解を利用して微細な角柱状の磁性相と角柱状の非磁性相とが交互に配列された構造を有する焼結磁石を得ることにより、上記の課題を解決する。 - 特許庁

The rare-earth sintered magnet is manufactured by sintering a raw material composed of fine alloy powder containing R (wherein, R is one, two, or more kinds of rare-earth elements including Y), T (wherein, T is one, two, or more kinds of transition metal elements containing Fe or Fe and Co as essential elements), and B.例文帳に追加

Ｒ（Ｒは希土類元素の１種又は２種以上、但し希土類元素はＹを含む概念である）、Ｔ（ＴはＦｅ又はＦｅ、Ｃｏを必須とする１種又は２種以上の遷移金属元素）及びＢを含む原料合金微粉を焼結し、希土類焼結磁石を製造する。 - 特許庁

In the R-T-B-based rare earth permanent magnet having a high coercive force by containing many heavy rare earth elements, the average crystal particle diameter of a sintered body and the amount of contained oxygen are controlled, and further an element such as Nb is contained.例文帳に追加

重希土類元素を多く含むことにより保磁力の高いタイプのＲ−Ｔ−Ｂ系希土類永久磁石において、焼結体の平均結晶粒径及び含有酸素量を制御すること、さらにはＮｂ等の元素を含有させることにより、従来にない優れた着磁特性が得られることを確認した。 - 特許庁

In the R-T-B-based rare earth permanent magnet that contains a large amount of heavy rare earth element and hence has a high coercive force, the average crystal grain size of a sintered body and the amount of oxygen contained are suppressed, and an element such as Nb is contained, thus confirming that new and superior magnetization characteristics can be obtained.例文帳に追加

重希土類元素を多く含むことにより保磁力の高いタイプのＲ−Ｔ−Ｂ系希土類永久磁石において、焼結体の平均結晶粒径及び含有酸素量を制御すること、さらにはＮｂ等の元素を含有させることにより、従来にない優れた着磁特性が得られることを確認した。 - 特許庁

In this method of manufacturing the sintered permanent magnet, the molding 10 obtained by forming the raw powder material into a ring and a cylindrical restraint jig 1 are provided, the restraint jig 1 is inserted in the inside diameter (d) of the molding 10, and the shape of the molding 10 is maintained by the outside diameter D0 of the restraint jig 1.例文帳に追加

原料粉末をリングに成形し得られた成形体１０と、筒形状の拘束治具１とを備え、成形体１０の内径ｄに拘束治具１を挿入し、焼成工程において、拘束治具１の外径Ｄ_0で成形体１０の形状が保持される焼結型永久磁石の製造方法。 - 特許庁

To solve a problem that when a content of Nd exceeds a prescribed value in terms of a composition ratio, an ingot can be manufactured by a conventional manufacturing method of an Nd-Fe-B based sintered magnet without producing αFe, but a volume ratio of an R rich phase of a nonmagnetic phase is increased and a maximum energy product and residual magnetic flux density showing magnetic characteristics is decreased.例文帳に追加

従来のNｄ−Ｆｅ−Ｂ系の焼結磁石の製造方法では、組成比でNｄの含有量が所定値を超えて多いと、αＦｅが生成しないインゴットの製造が可能であるものの、非磁性相のRリッチ相の体積比が増えて磁気特性を示す最大エネルギー積及び残留磁束密度が低下する。 - 特許庁

The manufacturing method of rare earth sintered magnet comprises the steps of inputting particles formed of a primary alloy particles of the predetermined composition and an organic solution, obtaining a molding body by impressing a magnetic field to the particles for pressure molding, and sintering the molding body.例文帳に追加

本発明の希土類焼結磁石の製造方法は、所定組成の一次合金粒子と有機液体で構成された顆粒を金型キャビティに投入する工程と、顆粒に磁場を印加し、かつ加圧成形することにより成形体を得る工程と、成形体を焼結する工程と、を備えることを特徴としている。 - 特許庁

In the method for manufacturing the sintered rare earth magnet alloy by refining a molten crude alloy, casting the molten alloy into an alloy ingot, subjecting the alloy ingot to crushing and further to pulverization, compacting the resultant powder and then sintering the resultant green compact, the above pulverization is carried out two or more times.例文帳に追加

粗合金の溶湯を溶製し，この溶湯を合金塊に鋳造し，この合金塊を粗粉砕したあと更に微粉砕し，得られた粉末を用いて圧粉成形し，この成形品を焼結して，焼結希土類磁石合金を製造する方法において，前記の微粉砕を２回以上実施することを特徴とする焼結希土類磁石合金の製造法である。 - 特許庁

Subsequently, the sintered magnet body on its surface is coated with an RHM alloy layer composed of the RH (wherein RH is one or two or more rare earth elements selected from among Dy, Ho and Tb) and metal M (wherein M is one or two or more metal elements selected from among Al, Cu, Co, Fe and Ag), the metal M forming RHM so as to induce a melting point lowering.例文帳に追加

次に、焼結磁石体の表面にＲＨ（但し、ＲＨは、Ｄｙ、Ｈｏ、Ｔｂから選ばれる希土類元素の１種又は２種以上）と、ＲＨＭとなり融点を下げる金属Ｍ（但し、ＭはＡｌ、Ｃｕ、Ｃｏ、Ｆｅ、Ａｇから選ばれる金属元素の１種または２種以上）とからなるＲＨＭ合金層を被覆する。 - 特許庁

This method for producing raw powder for a rare earth sintered magnet is provided with: a stage where primary alloy grains having a prescribed composition are added with a first organic liquid and a liquid component having saturated vapor pressure higher than that of the first organic liquid to obtain a mixture; and a stage where granules composed of the primary alloy grains are producing using the mixture.例文帳に追加

本発明は、所定組成の一次合金粒子に対して第１の有機液体と第１の有機液体よりも飽和蒸気圧の高い液成分を添加して混合物を得る工程と、混合物を用いて一次合金粒子から構成された顆粒を作製する工程とを備える希土類焼結磁石用原料粉体の製造方法である。 - 特許庁