To provide a manufacturing process for a refractory material minimum in the quantity of free carbon or free silicon and having remarkable oxygen barrier characteristics even at a very high temperature.例文帳に追加

自由カーボンや自由シリコンの量を最小化できさらに極めて高温でも顕著な酸素バリア特性を有しているような耐火性材料の製造プロセスを提供すること。 - 特許庁

To obtain a higher oxidation inhibiting effect and to control lowering of anti-spalling property in the case of using together with metallic powder and boride as an oxidation inhibitor for a basic refractory containing carbon used for a steel-making furnace, etc.例文帳に追加

製鋼炉等に使用される炭素含有塩基性耐火物において、金属粉と硼化物とを酸化防止材として併用する場合、より高い酸化防止効果が得られなおかつ耐スポーリング性の低下も抑制すること。 - 特許庁

Since the oxygen is not contained in the cooling fluid material, the combustion of carbon contained in the refractory brick as the boring object, is prevented and the raising of the bit surface temperature can be restrained and the using service life can drastically be improved.例文帳に追加

冷却流体に酸素を含まないので、穿孔対象である耐火れんが中に含まれる炭素の燃焼を防止し、ビット表面温度の上昇を抑制することができ、使用寿命を飛躍的に向上させることができる。 - 特許庁

To provide a high-zirconia-based electrocast refractory which contains a very small amount of carbon and thereby exhibits less foaming property to molten glass, and a method of producing the same.例文帳に追加

炭素の含有率が極めて少なく、その為に溶融ガラスに対して発泡性の少ない特徴をもつ高ジルコニア質電鋳耐火物及びその製造方法を提供する。 - 特許庁

The monolithic refractory containing carbon is produced by using infusible mesophase pitch, which is obtained by heat treating mesophase pitch under an oxygen atmosphere so as to make it infusible and has an average diameter of ≤10 μm.例文帳に追加

メソフェーズピッチを酸素雰囲気下で熱処理して不融化した平均粒径１０μｍ以下の不融化メソフェーズピッチを使用する炭素含有不定形耐火物。 - 特許庁

Since a refractory material constituted of a lining lined on the inner hole part of the immersion nozzle 20 is set to ≤1 wt.% carbon content, the rough surface caused by decarburization at the cleaning with the oxygen is restrained.例文帳に追加

浸漬ノズル２０の内孔部に内張りされたライニングを構成する耐火材は、カーボン含有量１重量％以下に設定されているから、酸素洗浄に際しての脱炭による肌荒れは抑制される。 - 特許庁

To decrease remove carbon and contaminants in a melt flowing out from a gasification melting furnace, to separate slag and metal and to suppress the degradation and damage of the refractory of a homogenizing furnace.例文帳に追加

ガス化溶融炉から流出する溶融体中の微量炭素と汚染物を減少させ、かつスラグとメタルを分離すると共に、均質化炉の耐火物の劣化損傷を抑制する。 - 特許庁

To provide a high-zirconia electrocasted refractory which has features of a low degree of oxygen deficiency, of an extremely few content of carbon, consequently of little foamability by a fused glass, and to provide a manufacturing method thereof.例文帳に追加

酸素の不足度が低く、かつ炭素の含有率が極めて少なく、そのために溶融ガラスに対して発泡性の少ない特徴をもつ高ジルコニア質電鋳耐火物及びその製造方法を提供する。 - 特許庁

This hot baking repairing material characterized by comprising a refractory material, a substance capable of forming carbon bonds in a hot state, and p-t-butylphenol and/or p-octylphenol as a flow-accelerating agent.例文帳に追加

耐火材料、熱間でカーボン結合を形成する物質、流動促進剤としてｐ−ｔ−ブチルフェノール又は／及びｐ−オクチルフェノールよりなることを特徴とする熱間焼き付け補修材である。 - 特許庁

A refractory lining structure of a vacuum degassing container is adapted such that non-calcined magnesia carbon bricks covered with a metal sheet only on the back side is lined partly or wholly.例文帳に追加

真空脱ガス処理容器の耐火物内張り構造を、背面側のみが金属板で被覆された不焼成マグネシアカーボン煉瓦を一部あるいは全部に内張りしたものとする。 - 特許庁

The gunning mixture is prepared by mixing a phosphate of 3 to 10wt%, pitch of 1 to 10 wt%, bentonite of 0.5 to 4wt% and dolomite of 10 to 25wt% into refractory aggregates of a magnesia or magnesia carbon system.例文帳に追加

マグネシア系やマグネシア・カーボン系の耐火骨材にリン酸塩を３〜１０重量％、ピッチを１〜１０重量％、ベントナイトを０．５〜４重量％、ドロマイトを１０〜２５重量％を添加したものである。 - 特許庁

This ferro-silicon nitride-containing powder for producing a carbon-containing refractory is characterized by comprising 2-60% of aluminum nitride, ≤20% (not including 0) calculated as Fe of iron and/or an iron compound and the rest of substantially silicon nitride.例文帳に追加

窒化アルミニウム２〜６０％、鉄及び／又は鉄化合物をＦｅ分として２０％以下（０を含まず）、残部が実質的に窒化珪素からなることを特徴とする炭素含有耐火物製造用の窒化珪素鉄含有粉末。 - 特許庁

The gas blowing nozzle 10 includes a gas introducing metallic tube 11 for injecting the gas into the molten metal, and a carbon-containing refractory 12 surrounding the outer circumference of the gas introducing metallic tube 11.例文帳に追加

ガス吹込みノズル１０は、溶融金属にガスを吹込むためのガス導入用金属管１１と、ガス導入用金属管１１を外囲する炭素含有耐火物１２と、を含む。 - 特許庁

To provide a method for producing a carbon-containing monolithic refractory excellent in explosion resistance although suppressing a construction water amount and having low porosity and a dense structure.例文帳に追加

施工水分量を抑えて低気孔率で緻密な組織でありながらも、耐爆裂性に優れた炭素含有不定形耐火物の製造方法を提供する。 - 特許庁

The low carbon unfired brick is manufactured by adding a mesophase pitch of 0.5-5 mass% and a thermosetting resin of 0.5-5 mass% per total mass to a refractory raw material mixture not containing flake-like graphite of 100 mass%, kneading, forming and heating.例文帳に追加

鱗状黒鉛を含有しない耐火原料混合物１００質量％に対して、外掛けでメソフェーズピッチ０．５〜５質量％と熱硬化性樹脂０．５〜５質量％を添加し、混練、成形後、加熱して得たものである。 - 特許庁

To enable the improvement of working efficiency, the energy saving by reducing a heat treatment time or the like and the reduction of manufacturing cost in a method for manufacturing a carbon-containing refractory for SN plate with an addition of metal Si.例文帳に追加

金属Ｓｉを添加したＳＮプレート用の炭素含有耐火物の製造方法において、作業能率の向上、熱処理時間の短縮等による省エネルギー化、製造コストの削減を図ること。 - 特許庁

To provide highly durable magnesia-carbon type refractory which can suppress structural degradation under a use environment being exposed in high temperature surroundings for a long period of time, thereby maintain corrosion resistance in the initial stage of use.例文帳に追加

本発明は、長期間高温環境下に曝される様な使用環境下において、組織劣化を抑制でき、使用初期の耐食性を維持可能な高耐用性のマグネシア−カーボン質耐火物を提供することを目的とする。 - 特許庁

To provide a spraying method capable of spraying a monolithic refractory including a carbon material with a low water content, and obtaining a precise construction body which is precise and improved in corrosion resistance.例文帳に追加

カーボン素材を含む不定形耐火物を低水分で吹付けることができ、緻密で耐食性に優れた施工体を得ることができる吹付け施工方法を提供する。 - 特許庁

From 5 to 30 pts.mass substance forming a carbon bond under heat and 0.1-5 pts.mass nonaqueous solvent are compounded with 100 pts.mass grain size-controlled basic refractory aggregate.例文帳に追加

粒度調整された塩基性耐火骨材１００質量部に対し、熱間でカーボン結合を形成する物質５〜３０質量部、および非水系溶媒０．１〜５質量部を配合した。 - 特許庁

A green body having a composition composed of an aluminum powder and a refractory raw material powder is put into a sealed container, and the green body is fired in a state that silicon nitride grains or mixed grains of the silicon nitride grains and carbon grains are filled in the sealed container.例文帳に追加

アルミニウム粉末と耐火原料粉末とからなる配合物の成形体を、密閉容器に入れ、その密閉容器内に窒化珪素粒あるいは窒化珪素粒と炭素粒とを含む混合粒を充填した状態で焼成する。 - 特許庁

To provide a composition for refractories (such as brick) which gives refractories having a high residual carbon content when kneaded, increased refractory strength after firing, and low porosity.例文帳に追加

混練した耐火物（煉瓦等）の残炭率が高く、焼成後の耐火物強度が増大し、且つ、気孔率が低い耐火物耐を与える火物用組成物を提供すること。 - 特許庁

Carbon- containing refractory brick using planar aggregates containing planar aggregates of 3 to 70 wt.% and expanded flaky graphite can suitably be used.例文帳に追加

板状骨材を３〜７０重量％と膨張化鱗状黒鉛を１〜３０重量％を含有する板状骨材を使用した炭素含有耐火れんがが好適に使用できる。 - 特許庁

To provide a refractory free from the pickup of carbon content in a molten iron even in the melting of a very low carbon steel and having excellent corrosion resistance stable even against a high temperature oxidation atmospheric condition and excellent spalling resistance.例文帳に追加

極低炭素鋼の溶製時においても溶鋼の炭素含有量のピックアップがなく、高温の酸化雰囲気条件下におけるスラグアタックに対しても安定である優れた耐食性を有し、更に耐スポール性にも優れた耐火物を提供する。 - 特許庁

The refractory structure for the bottom of the blast furnace includes a plural stages of the carbon bricks 2 continuously arranged on the same perimeter so that the arrayed direction of carbon grains 4 in the bricks can be vertical and/or horizontal.例文帳に追加

高炉の炉底耐火物構造において、カーボン粒４の配列した方向を垂直及び／又は水平にしたカーボン煉瓦２が連続した複数段の同一周内に渡って配置されていることを特徴とする高炉炉底耐火物構造。 - 特許庁

At the time of subjecting undeoxidized molten metal melted by a converter and containing 0.04 to 0.06% C to vacuum decarburization by using RH degassing treatment equipment to produce ultra-low carbon steel, a magnesia-carbon brick containing, by mass, >5 to 9% C is used as a lining refractory for an RH degassing tank.例文帳に追加

転炉で溶製されCを0.04〜0.06%含有する未脱酸の溶鋼をRH脱ガス処理設備によって真空脱炭して極低炭素鋼を製造するに当たり、RH脱ガス槽用の内張り耐火物を質量比でC含有量5%超え、9%以下のマグネシア・カーボンれんがとする。 - 特許庁

The magnesia carbon refractory characteristically comprises metallic boron of 0.1-6 percent by mass, carbon of 1-40 percent by mass, one kind or two kinds or more of metallic aluminium, metallic silicon and metallic magnesium of 1-10 percent by mass in total and the balance mainly composed of magnesium oxide.例文帳に追加

質量％で、金属ホウ素0.1〜6%、炭素1〜40%を含有し、金属アルミニウム、金属シリコン、金属マグネシウムの一種又は二種以上を合計で1〜10％含有し、残部が酸化マグネシウムを主体とすることを特徴とするマグネシア・カーボン質耐火物。 - 特許庁

In continuously casting molten steel whose carbon content is in the range of 0.08-0.16 mass %, a metallic tube filled with carbon powder and iron powder is melted by induction heating, and then the molten steel thus obtained is continuously added into the casting mold of a continuous casting machine through a refractory pipe.例文帳に追加

炭素含有量が０．０８〜０．１６質量％の範囲の溶鋼を連続鋳造するに際して、炭素粉と鉄粉を充填した金属管を誘導加熱溶解し、得られた溶鉄を耐火材管を経由して連続鋳造機鋳型内に連続的に添加する。 - 特許庁

When the molten steel is primarily refined by using a converter, then is secondarily refined b using a ladle refining equipment, the carbon- containing waste refractory is added into slag on the molten steel at the period when the carbon content of the molten steel in the ladle is ≥0.01 mass%.例文帳に追加

転炉を用いて溶鋼を一次脱炭精錬し、次いで取鍋精錬設備を用いて二次脱炭精錬を行なうにあたって、取鍋内の溶鋼中の炭素含有量が0.01質量％以上である時期に、溶鋼上のスラグに炭素含有耐火物屑を添加する。 - 特許庁

The refractory used for continuous casting of molten metal contains a refractory powder comprising at least one of alumina and silica as a main component, <2 mass% reinforcing fiber containing free carbon (FC) and having a length of 2-4 mm and a diameter of <10 μm, ≤3 mass% silicon, and ≤5 mass% expanded graphite.例文帳に追加

溶融金属の連続鋳造に用いられる耐火物は、アルミナ及びシリカの少なくともいずれかを含む耐火物粉末を主成分とし、フリーカーボン（ＦＣ）を含有し、長さ２mm以上４mm以下で直径１０μm未満の補強用繊維を２質量％未満と、シリコンを３質量％以下と、膨張黒鉛を５質量％以下とを含んで構成される。 - 特許庁

In the carbon-containing unburned refractory containing a refractory raw material, a carbonaceous raw material, metallic aluminum and a binder as essential structural components, the surface of the carbonaceous raw material has an amorphous metal oxide thin film covered with oxide colloid and at least a part of the binder is an organic binder.例文帳に追加

即ち、本発明の炭素含有不焼成耐火物は、耐火性原料、炭素質原料、金属アルミニウム及びバインダーを必須の構成成分とする炭素含有不焼成耐火物において、炭素質原料の表面が酸化物コロイドにより被覆された非晶質金属酸化物薄膜を有し、且つバインダーの少なくとも一部が有機バインダーであることを特徴とする。 - 特許庁

The thermal insulation coating material for the carbon- containing refractories is prepared by adding a liquid binder at 20 to 170 mass% in outer per cent to a refractory material containing hollow refractory particles in which the content of the hollow particles is 50 to 97 mass%, a portion or the whole of the balance is clay and the content of the clay is ≤30 mass%.例文帳に追加

本発明のカーボン含有耐火物の断熱コーティング材は、中空の耐火性粒子を含有し、該中空粒子の含有量が５０〜９７質量％、残部の一部または全てが粘土であり、且つ粘土の含有量が３０質量％以下である耐火材料に、液状バインダーを外掛で２０〜１７０質量％添加したことを特徴とする。 - 特許庁

The 2-furaldehyde acts as a solvent for the phenol resin, enhances the formability, easily reacts with the phenol resin under heat using the catalyst and is carbonized by firing to obtain the refractory having high fixed carbon content and excellent corrosion resistance.例文帳に追加

２−フルアルデヒドはフェノール樹脂の溶剤として作用し、成形性を高めることができると共に、２−フルアルデヒドは加熱と触媒によって容易にフェノール樹脂と反応するものであり、焼成によって炭素化し、固定炭素量が高く耐食性の良好な耐火物を得ることができる。 - 特許庁

To obtain a refractory composition which can jointly use a phonol resin and tar-pitch as binder components, and has excellent formability and stability after forming, and has a high residual carbon content, and can obtain refractories having satisfactory oxidation resistance, spalling resistance and corrosion resistance.例文帳に追加

フェノール樹脂とタール・ピッチ類をバインダー成分として併用することができると共に、成形性及び成形の安定性に優れ、しかも残留炭素量が高く耐酸化性や耐スポーリング性、耐食性が良好な耐火物を得ることができる耐火物組成物を提供する。 - 特許庁

The refractory-metal material can be manufactured by applying a carbon supply source to the metallic base material and subjecting the base material to heating in a nitrogen atmosphere at 1100-1400°C and to pressurizing treatment at ≥1 MPa pressure.例文帳に追加

耐酸化層を有する高融点金属材料を製造する方法は金属母材に炭素供給源を塗布し、窒素雰囲気中で１１００〜１４００℃の温度範囲で加熱及び１ＭＰａ以上の圧力で加圧処理することにより形成する。 - 特許庁

The taphole stopper is obtained by mixing and kneading anhydrous coal tar and powdery pitch in a refractory material and the ratio of total fixed carbon in the anhydrous coal tar and the powdery pitch is controlled to 40-50 mass%.例文帳に追加

本発明の出銑孔閉塞材は、耐火材料に無水コールタールおよび粉末状のピッチとを配合し、混練した出銑孔閉塞材において、該無水コールタールおよび粉末状のピッチにおける固定炭素率の合計量を４０質量％〜５０質量％としたことを特徴とする。 - 特許庁

A furnace repairing material prepared by adding a substance forming carbon bonds in a hot state of 10-30 pts.mass and a nonaqueous solvent of 0.1-5 pts.mass to a basic refractory aggregate of 100 pts.mass and mixing is sprayed with an addition of water of 1-8 pts.mass to the wall surface of a furnace by using a spraying device.例文帳に追加

塩基性耐火骨材１００質量部に対し、熱間でカーボン結合を形成する物質１０〜３０質量部と非水系溶媒を０．１〜５質量部を添加、混合してなる窯炉用補修材を、吹付け装置を使用し、１〜８質量部の水を添加し窯炉壁面に吹付ける。 - 特許庁

To provide a composition of a refractory suitable for brick, or refractories needed with heat resistance for manufacturing iron, steel, glass and cement or an installation, or a container for an incinerator which has none of carbon residue, moreover good operability, and a good mold releasing property and surface smoothness of a compact.例文帳に追加

鉄、鋼、ガラス、セメント製造、あるいは焼却炉等の設備や容器に用いられる耐熱性が要求される煉瓦、耐火物類用途に好適な、残炭性が無く、且つ、成形時の取り扱いに優れ、離型性と硬化物の表面平滑性の良好であって、耐火物用組成物を提供すること。 - 特許庁

To provide an apparatus for diagnosing and repairing a coke oven, capable of carrying out strong repair having long life by accurately grasping position to be repaired to carry out repair, by removing attached carbon and deteriorated refractory to form healthy repaired part and making brick surface after thermal spraying repair flat.例文帳に追加

補修すべき位置を正確に把握して補修を行い、付着カーボンや劣化耐火物を除去して健全な補修部位を形成し、溶射補修後のレンガ面を平坦化し、強固で寿命の長い補修を行うことのできるコークス炉の診断補修装置及び診断補修方法を提供する。 - 特許庁

This immersion nozzle is composed of any one or more of mixture among alumina quality, zirconia quality, magnesia quality and alumina/carbon quality on the sliding surface abutted on the lower surface of the intermediate nozzle 12, and a high erosion resistant refractory 5 arranging a molten metal flowing hole 6, is fitted.例文帳に追加

この浸漬ノズルは、中間ノズル１２の下面に当接する摺動面に、アルミナ質、ジルコニア質、マグネシア質、アルミナ−カーボン質のいずれかまたは２以上の混合物よりなり、溶融金属流通孔６が設けられた高耐食性耐火物５が取り付けられている。 - 特許庁

At the time of subjecting undeoxidized molten steel melted by a converter and containing 0.04 to 0.06% to vacuum decarburization by using RH degassing treatment equipment, a magnesia-carbon brick containing, by mass, >3 to 7% C is used as a lining refractory for an RH degassing tank, and RH degassing treatment is performed by controlling killing treatment time to ≤20 min.例文帳に追加

転炉で溶製されCを0.04〜0.06%含有する未脱酸の溶鋼をRH脱ガス処理設備によって真空脱炭するに当たり、RH脱ガス槽用の内張り耐火物を質量比でC含有量3%超、7%以下のマグネシア・カーボンれんがとするとともに、キルド処理時間を20min以下としてRH脱ガス処理を行う。 - 特許庁

To provide a refining method of molten steel under reduced pressure, by which, in the case of melting extra-low carbon molten steel, good gas bubble activating surface is formed by fining the gas bubble and decarburizing reaction is promoted by renewing the bubble activating surface and the service life of an immersion tube, etc., can be prolonged by preventing the local wear in a refractory.例文帳に追加

極低炭素の溶鋼を溶製する際に、気泡の微細化による良好な気泡活性面を形成し、気泡活性面を更新することにより脱炭反応を促進し、耐火物の局部損耗を防止して浸漬管等の寿命を延長できる溶鋼の減圧精錬方法を提供する。 - 特許庁

To improve texture compactness and spalling resistance and improve resistance to oxidation by adding a specific amount of carbon black having a specified specific surface area to a compound comprising refractory aggregate and a metal and further adding an organic binder thereto and kneading and forming the mixture and subjecting the formed product to heat treatment.例文帳に追加

スライディングノズル用上部ノズルれんが、下部ノズルれんが及びプレートれんがにおいて、特に２００〜７００℃の中間温度域における耐酸化性の向上を図り、従来使用中のれんが外周部に生じていたボロツキ現象を軽減し、その結果れんが自体の耐用性を向上させる。 - 特許庁

In the lining structure of carbon-containing refractory brick using planar aggregates, the planar aggregates are arranged so that the large faces thereof are made almost parallel, and the planar aggregates are arranged so as to be made perpendicular to the working faces, and so as to be made perpendicular even to joints in which damage is required to be reduced.例文帳に追加

板状骨材を使用した炭素含有耐火れんがのライニング構造において、板状骨材の互いの大きい面同士がほぼ平行になるように配列されており、その板状骨材が稼動面に対して直角で、しかも、損傷を軽減させたい目地に対しても直角になるように配列されている。 - 特許庁

To provide a molten steel vacuum-refining method excellent in decarburization by which the decarburizing speed under reduced pressure is improved and the decarburization is executed in a short time and the temp. drop of molten steel and the wearing of refractory are restrained and an extra- low carbon molten steel can easily be produced.例文帳に追加

減圧下における脱炭速度を高めて短時間で脱炭し、溶鋼の温度低下や耐火物の損耗を抑制して、極低炭素の溶鋼を容易に溶製することのできる脱炭に優れた溶鋼の減圧精錬方法を提供する。 - 特許庁

The reused lining refractory 24 set in the range of the lower part from molten metal surface SF at the stationary time in the plurality of lining refractories 20 set in the converter 1, uses a magnesia-carbon brick applying at least a part of non-additional metallic Al and the additional metallic Si in an antioxidant.例文帳に追加

転炉１内に配設する複数の内張り耐火物２０のうち静止時の鋼浴面ＳＦより下方の範囲に配設する再使用内張り耐火物２４は、酸化防止剤の金属Ａｌを未添加および金属Ｓｉを添加の少なくとも一方を施したマグネシア−カーボンレンガを使用する。 - 特許庁