An aluminum material 2 is laminated on a hot-dip aluminized steel plate 1, on which an aluminum plated layer 4 containing 3-12 mass% Si and 0.5-5 mass% Fe is formed, and spot welding of the laminated material and plate is performed while pressurizing the hot-dip aluminized steel plate and aluminum or an aluminum alloy using an electrode 3 having a front end with a radius.例文帳に追加

Ｓｉ：３〜１２質量％，Ｆｅ：０.５〜５質量％を含むＡｌめっき層４が形成された溶融アルミニウムめっき鋼板１にアルミニウム材料２を重ね合わせ、先端Ｒのついた電極３で溶融アルミニウムめっき鋼板及びアルミニウム又はアルミニウム合金を加圧し、スポット溶接する。 - 特許庁

A method of producing the ferro-silicon nitride comprises producing an ingot of the ferro- silicon nitride by nitriding a raw material containing iron silicide (FeSi) and/or a Si component and an Fe component, then pulverizing the produced ingot, adding the saturated fatty acid having 10 to 24 carbon atoms or its salt into the resulting powder and further finely pulverizing the resulting mixture while keeping the temperature at 30 to 150°C.例文帳に追加

珪素鉄（ＦｅＳｉ）及び／又はＳｉ分とＦｅ分を含む原料を窒化して窒化珪素鉄のインゴットを製造し粗砕した後、炭素数１０〜２４の飽和脂肪酸又はその塩を添加し、温度３０〜１５０℃に保持しながら更に微粉砕することを特徴とする上記窒化珪素鉄粉末の製造方法。 - 特許庁

On the surface of the surface-treated steel, a protective rust layer comprising Al by 0.1 to 35% in a molar fraction expressed by Al/(Fe+Al)×100 (%), and in which the total content of goethite and X-ray amorphous components is ≥30 mass%, and free from flowing rust can be formed within one year even in a salt-deposited environment.例文帳に追加

この表面処理鋼材の表面には、塩分堆積環境下でも、Ａｌ／（Ｆｅ＋Ａｌ）×１００（％）で表わされるモル分率で ０．１〜３５％のＡｌを含有し、このゲーサイトおよびＸ線的非晶質分の合計量が３０質量％以上で、流れさびのない保護性さび層が一年以内に形成される。 - 特許庁

In the galvannealed steel sheet using steel comprising 0.2 to 2.0 mass% Si as a plating base material, the thickness of a nitrogen-concentrated layer in the surface layer part of the steel sheet is 3 to 100 μm, the concentration of Al in a plating film is 0.20 to 0.40 mass%, and the concentration of Fe is 7 to 15 mass%.例文帳に追加

０．２〜２．０質量％のＳｉを含有する鋼をめっき母材とする合金化溶融亜鉛めっき鋼板であって、鋼板表層部の窒素濃化層が３〜１００μｍであり、めっき皮膜中のＡｌ濃度が０．２０〜０．４０質量％、Ｆｅ濃度が７〜１５質量％である、合金化溶融亜鉛めっき鋼板。 - 特許庁

The separator for the molten carbonate fuel cell has a gas passage comprising 16.5-17.5 wt.% Co, 28.5-29.5 wt.% Ni, and the remaining of Fe and unavoidable impurities, and center line average roughness (Ra) (JISB0601) on the surface other than the gas passage is made to be 0.3-0.8 μm.例文帳に追加

Ｃｏが１６．５〜１７．５ｗｔ％、Ｎｉが２８．５〜２９．５ｗｔ％含有され、残部がＦｅおよび不可避の不純物からなる、ガス流路を備えた溶融炭酸塩型燃料電池用セパレータであって、前記ガス流路以外の表面の中心線平均粗さ（Ｒａ）（ＪＩＳＢ０６０１）を０．３μｍ〜０．８μｍとすること。 - 特許庁

The aluminum conductive wire is characterized by comprising a stranded wire formed by stranding aluminum alloy single wires composed of 0.1-1.0 mass% Fe, 0.05-0.5 mass% Cu, 0.05-0.4 mass% Mg, and aluminum and inevitable impurities as the remainder, wherein the total of Cu and Mg is 0.3 to 0.8 mass%.例文帳に追加

Ｆｅ ０．１〜１．０ｍａｓｓ％、Ｃｕ ０．０５〜０．５ｍａｓｓ％、Ｍｇ ０．０５〜０．４ｍａｓｓ％を含有し、ＣｕとＭｇの合計が０．３〜０．８ｍａｓｓ％、残部がアルミニウムおよび不可避不純物から成るアルミニウム合金素線を撚り合わせて形成した撚線からなることを特徴とするアルミニウム導電線。 - 特許庁

The apparatus converts the zero-valence mercuric gas to a water-soluble bivalence mercury gas to separate and remove it from the gas to be treated, wherein the apparatus has a reactive separation means 4A for making an aqueous solution, which contains a mercury oxidant composed of a trivalent irons (Fe^3+) and has pH of about 3 or below, contact with the gas to be treated.例文帳に追加

ゼロ価水銀ガスを水溶性の２価水銀ガスに変換して処理対象ガスから分離・除去する装置であって、３価の鉄（Ｆｅ^３＋）を成分とする水銀酸化剤を含みｐＨが約３以下である水溶液を、前記処理対象ガスに接触させる反応分離手段４Ａを具備する。 - 特許庁

The first thin film contains at least one element selected from Al, Cr, Mn, Sc, In, Ru, Rh, Co, Fe, Cu, Ni, Zn, Li, Si, Ge, Zr, Ti, Hf, Sn, Pb, Mo, V, Nb, C, Si, Ge, Sn and Pb as an additive M.例文帳に追加

また、前記第一の薄膜は、添加物Ｍとして、Ａｌ、Ｃｒ、Ｍｎ、Ｓｃ、Ｉｎ、Ｒｕ、Ｒｈ、Ｃｏ、Ｆｅ、Ｃｕ、Ｎｉ、Ｚｎ、Ｌｉ、Ｓｉ、Ｇｅ、Ｚｒ、Ｔｉ、Ｈｆ、Ｓｎ、Ｐｂ、Ｍｏ、Ｖ、Ｎｂ、Ｃ、Ｓｉ、Ｇｅ、Ｓｎ、Ｐｂから選ばれる少なくとも一種の元素を含むことを特徴とする追記型光記録媒体である。 - 特許庁

To solve a problem that when a content of Nd exceeds a prescribed value in terms of a composition ratio, an ingot can be manufactured by a conventional manufacturing method of an Nd-Fe-B based sintered magnet without producing αFe, but a volume ratio of an R rich phase of a nonmagnetic phase is increased and a maximum energy product and residual magnetic flux density showing magnetic characteristics is decreased.例文帳に追加

従来のNｄ−Ｆｅ−Ｂ系の焼結磁石の製造方法では、組成比でNｄの含有量が所定値を超えて多いと、αＦｅが生成しないインゴットの製造が可能であるものの、非磁性相のRリッチ相の体積比が増えて磁気特性を示す最大エネルギー積及び残留磁束密度が低下する。 - 特許庁

(3) The galvanized steel sheet superior in heat resistance and corrosion resistance according to either one of claim 1 or 2 is the one wherein the solution includes a metal salt of nitric acid (D) as an additional component, and the metal in the metal salt of nitric acid includes at least one kind selected from the group consisting of alkaline earth metals, Co, Ni, Fe, Zr, and Ti.例文帳に追加

（３）追加成分として硝酸金属塩（Ｄ）を含み、かつその硝酸金属塩中の金属が、アルカリ土類金属、Ｃｏ、Ｎｉ、Ｆｅ、ＺｒおよびＴｉからなる群から選ばれる少なくとも１種である、請求項１、２の何れか１項に記載の耐熱性と耐食性に優れるＺｎ系めっき鋼板。 - 特許庁

The ferrite stainless steel includes, by mass%, 0.03% or less of C, 2.0% or less of Si, 2.0% or less of Mn, 10-30% of Cr, at least one kind of 0.8% or less of Nb and 0.8% or less of Ti, and 0.03% or less of N, and Fe and inevitable impurities.例文帳に追加

フェライト系ステンレス鋼は、質量％で、０．０３％以下のＣと、２．０％以下のＳｉと、２．０％以下のＭｎと、１０〜３０％のＣｒと、０．８％以下のＮｂおよび０．８％以下のＴｉの少なくとも一種と、０．０３％以下のＮとを含み、残部がＦｅおよび不可避的不純物からなる。 - 特許庁

A continuously cast slab consisting of an Fe-Ni allay containing 30 to 50 mass% Ni is held at 1,000 to 1,300°C for ≥1 hr, is thereafter subjected to press forging at a draft of 5 to 40%, and is subsequently subjected to soaking treatment of holding the same at 1,100 to 1,300°C for ≥5 hr.例文帳に追加

３０〜５０質量％のＮｉを含有するＦｅ−Ｎｉ合金からなる連続鋳造スラブを、１０００〜１３００℃で１時間以上保持した後、圧下率が５〜４０％のプレス鍛造を行い、その後、１１００〜１３００℃で５時間以上保持する均熱処理を行うシャドウマスク用Ｆｅ−Ｎｉ合金素材の製造方法。 - 特許庁

This cold rolled steel strip for a leaf spring is the one having a compsn. contg. 0.10 to 0.15% C, 0.25 to 0.8% Mn, 11.5 to 13% Cr, 0 to 0.8% Ni, 0 to 0.8% Cu, and the balance Fe and also satisfying the following inequality and formula.例文帳に追加

Ｃ：０．１０〜０．１５％、Ｍｎ：０．２５〜０．８％、Ｃｒ：１１．５〜１３％、Ｎｉ：０〜０．８％、Ｃｕ：０〜０．８％を含み、残部がＦｅからなり、かつ下記式を満足している板ばね用冷間圧延鋼帯、およびこの鋼帯を焼入れし、ばね形状に成形した後、時効硬化熱処理を施す板ばねの製造方法。 - 特許庁

In the method for manufacturing the galvannealed steel sheet in which a steel sheet is subjected to hot-dip galvanizing and alloying treatment to form a Zn-Fe alloy plating film, the steel sheet is temper-rolled after the alloying treatment and then brought into contact with an acid solution of pH 0.6 to 5.8.例文帳に追加

鋼板を溶融亜鉛めっき後、よる合金化処理を施してＺｎ−Ｆｅ合金めっき皮膜を形成させる合金化溶融亜鉛めっき鋼板の製造方法において、鋼板を合金化処理後、調質圧延を施し、その後該鋼板をｐＨ０．６以上５．８以下の酸性溶液と接触させる。 - 特許庁

The first catalyst 1 having a catalyst component in which at least one metal selected from Fe, Co, and Mn and Pt are supported on zeolite and the second catalyst 2 having a catalyst component in which Pt is supported on zeolite by an ion exchange method are arranged on the upstream side and on the downstream side in an exhaust gas flow direction A.例文帳に追加

ゼオライトにＦｅ、Ｃｏ及びＭｎのうちの少なくとも１種とＰｔとが担持されてなる触媒成分を有する第１触媒１と、ゼオライトにＰｔがイオン交換法によって担持されてなる触媒成分を有する第２触媒２とを、排気ガス流れ方向Ａにおける上流側と下流側とに配置する。 - 特許庁

The heat resistant and high strength aluminum alloy is comprised primarily of a matrix phase and an Al-Fe-based intermetallic compound phase (first compound phase), and an Al-(Zr,Ti)-based intermetallic compound of L1_2 structure (second compound phase) is possible to precipitate in the matrix phase in the vicinity of the boundary with the first compound phase so as to be in a matching manner.例文帳に追加

本発明の耐熱高強度アルミニウム合金は、主に母相とＡｌ−Ｆｅ系金属間化合物相（第一化合物相）からなり、この第一化合物相との境界近傍にある母相中にＬ１_２型Ａｌ−（Ｚｒ、Ｔｉ）系金属間化合物（第二化合物相）が整合的に析出し得る。 - 特許庁

Since N element or further Fe element are added to the RuTe_2 which is a catalyst for fuel cell demonstrating a superior catalyst action capable of substituting a noble metal catalyst such as platinum with low cost, the catalyst for the fuel cell with increased oxygen reduction reaction starting potential and having a higher potential and much current can be obtained.例文帳に追加

安価で、白金等の貴金属触媒に代替しうる、優れた触媒作用を発揮する燃料電池用触媒であるＲｕＴｅ_２にＮ元素、或いは更にＦｅ元素を加えることにより、酸素還元反応開始電位が上昇し、より高い電位で多くの電流を与える燃料電池触媒が得られる。 - 特許庁

In the nonaqueous lithium ion secondary battery, a positive electrode including, as positive electrode active material, a lithium compound containing a metal element of Fe or Mn as a constituting element, and a negative electrode including, as a negative electrode active material, a carbon material capable of storing/releasing lithium ions are separately disposed within nonaqueous electrolyte.例文帳に追加

本発明の非水系リチウムイオン二次電池は、構成元素に金属元素としてＦｅ又はＭｎを含むリチウム化合物を正極活物質とする正極と、リチウムイオンを吸蔵・放出可能な炭素材料を負極活物質とする負極とを、非水電解液内で分離して配置したものである。 - 特許庁

For example, an alloy melt composed of 6 mol% Nd, 91 mol% Fe, and 3 mol% B is filled in a nozzle 21 heated with a heating coil 24 and discharged out through the nozzle tip 22 at a proper flow rate onto the surface of the rotary metal roll which rotates at a high speed for forming amorphous thin pieces 25 through a quenching method.例文帳に追加

この例として、Ｎｄ６ｍｏｌ％、Ｆｅ９１ｍｏｌ％、Ｂ３ｍｏｌ％の組成からなる合金溶湯１を、ノズル２１に注入して加熱コイル２４で加熱しながら、ノズル口２２から高速回転している回転金属ロール２３上に適量づつ排出させて急冷法でアモルファス薄片２５を作成する。 - 特許庁

Disclosed is an aluminum based alloy plated steel having excellent cut edge face corrosion resistance and worked part corrosion resistance, which has a plating film comprising, by mass, 1 to 75% Fe, and one or more selected from 0.02 to 50% Mg and 0.02 to 1% Ca, and the balance Al with inevitable impurities.例文帳に追加

質量％で、Ｆｅ：１〜７５％、Ｍｇ：０．０２〜５０％及びＣａ：０．０２〜１％のうち１種又は２種、及び、残部：Ａｌ及び不可避的不純物からなるめっき被膜を有することを特徴とする切断端面耐食性及び加工部耐食性に優れたアルミニウム系合金めっき鋼材。 - 特許庁

In the grain oriented silicon steel sheet having an insulating film containing no chromium and insulating film agent therefor, the insulating film contains a phosphate, and one or two or more kinds of 0.06-2.10 mol as metal element to be selected from among inorganic compounds of Fe, Ni, Co, Cu, Sr and Mo to phosphate of 1 mol.例文帳に追加

絶縁皮膜が燐酸塩と、この燐酸塩１モルに対しＦｅ，Ｎｉ，Ｃｏ，Ｃｕ，Ｓｒ，Ｍｏの無機化合物の中から選ばれる１種又は２種以上を、金属元素として０．０６〜２．１０モルを含有することを特徴とする、クロムを含まない絶縁皮膜を有する方向性電磁鋼板およびその絶縁被膜剤。 - 特許庁

Also, the manufacturing method includes: a process of preparing the substrate; a process of forming a layer comprising an amorphous magnetic alloy containing Co, Fe and B on the substrate; a process of forming an amorphous MgO layer on the layer comprising the amorphous magnetic alloy; and a process of performing annealing treatment.例文帳に追加

また、その製造方法は、基板を準備する工程と、基板上にＣｏ、ＦｅおよびＢを含むアモルファス磁性合金からなる層を形成する工程と、アモルファス磁性合金からなる層上にアモルファスＭｇＯ層を形成する工程と、アニール処理を行う工程を有する磁気多層膜の製造方法。 - 特許庁

The aluminum alloy for casting comprises, by mass, 9.0 to 11.0% Si, 0.05 to 0.35% Mg, ≤0.1% Cu, 0.05 to 0.40% Fe, 0.3 to 0.5% Mn, 0.0020 to 0.0600% Li, and the balance aluminum with inevitable impurities.例文帳に追加

本発明の鋳造用アルミニウム合金はＳｉ：９．０〜１１．０質量％、Ｍｇ：０．０５〜０．３５質量％、Ｃｕ：０．１質量％以下、Ｆｅ：０．０５〜０．４０質量％、Ｍｎ：０．３〜０．５質量％、Ｌｉ：０．００２０〜０．０６００質量％を含み、残部がアルミニウム及び不可避不純物からなることを特徴とする。 - 特許庁

To easily and rapidly produce an inexpensive flocculant excellent in safety by using an iron-containing silica acidic aq. solution prepared by mixing an aq. solution of ferric ion coexisted with silicic acid, or the like, adding and stirring a water soluble starch and specifying the molar ratio Si/Fe and the pH to simplify the production process.例文帳に追加

水ガラス酸性化工程、モノマーシリカ重合工程、重合シリカの粘度測定が不要で、活性シリカの製造に必要な時間が非常に短時間で、かつ、ゲル化トラブルが全く起きなくて、鉱酸、アルカリ剤とも不要のため製造コストが低く、作業上の安全性が優れた無機凝集剤の製造方法を提供する。 - 特許庁

The secular discoloration of the pure titanium material for the building material is remarkably reduced even if the material is exposed to a severe environment by suppressing Fe to 0.08 mass% or less, Nb to 0.02 mass% or less and Co to 0.02 mass% or less as impurity elements contained in the pure titanium material for the building material.例文帳に追加

建材用の純チタンに含まれる不純物元素としてのＦｅを０．０８質量％以下，Ｎｂを０．０２質量％以下，Ｃｏを０．０２質量％以下に抑制することによって、厳しい環境にさらされる場合であっても、建材用純チタン材の経年変色を顕著に低減することに成功した。 - 特許庁

The high strength titanium alloy which can be worked at high temperatures consists of an α-β type titanium alloy comprising, by mass, 3 to 7% Al and 0.08 to 0.25% C as α stabilizing elements, and 2.0 to 6.0% Cr and 0.3 to 1.0% Fe as β stabilizing elements.例文帳に追加

α安定化元素としてＡｌ：３〜７％（質量％を表わす、以下同じ）およびＣ：０．０８〜０．２５％、β安定化元素としてＣｒ：２．０〜６．０％およびＦｅ：０．３〜１．０％を含有するα−β型チタン合金からなる熱間加工性に優れた高強度チタン合金を開示する。 - 特許庁

(1) In the optical recording medium containing a substrate and a recording layer over the substrate, the recording layer primarily contains Bi and O (oxygen), and further contains B and at least one element X selected from Ge, Li, Sn, Cu, Fe, Pd, Zn, Mg, Nd, Mn and Ni.例文帳に追加

（１）基板上に少なくとも記録層を形成した光記録媒体であって、記録層の構成元素の主成分がＢｉ及びＯ（酸素）であり、Ｂを含有し、更にＧｅ、Ｌｉ、Ｓｎ、Ｃｕ、Ｆｅ、Ｐｄ、Ｚｎ、Ｍｇ、Ｎｄ、Ｍｎ、Ｎｉから選択される少なくとも一種の元素Ｘを含有する光記録媒体。 - 特許庁

The magnetic recording medium wherein a magnetic layer consisting principally of ferromagnetic powder and a bonding agent is formed on a substrate is characterized in that zirconia particles are contained in the magnetic layer and the intensity ratio of Zr to Fe obtained by measuring the magnetic layer by fluorescent X-ray spectroscopy is 0.001-0.1.例文帳に追加

支持体上に強磁性粉末及び結合剤を主体とする磁性層が形成されてなる磁気記録媒体において、磁性層中にジルコニア粒子を含有し、磁性層を蛍光Ｘ線で測定したＦｅに対するＺｒの強度比が０．００１〜０．１であることを特徴とする磁気記録媒体。 - 特許庁

A magnetic pulverulent body has an ferrous-oxide phase equalizing the ε-Fe_2O_3 crystal and a space group, and having a crystal having a structure substituting Al for a part of the Fe site of the ε-Fe_2O_3 as a main phase.例文帳に追加

ε−Ｆｅ_2Ｏ_3結晶と空間群が同じであり、かつε−Ｆｅ_2Ｏ_3結晶のＦｅサイトの一部がＡｌで置換された構造の結晶を主相にもつ鉄酸化物相を有し、その鉄酸化物相におけるＡｌとＦｅのモル比をＡｌ：Ｆｅ＝ｘ：（２−ｘ）と表すとき、０＜ｘ＜１を満たす磁性粉体。 - 特許庁

This metallic separator for the solid high polymer fuel cell has a noble metal layer, such as Au, provided on a surface of a metal plate, such as an Fe group alloy, and these are turned into a clad by performing rolling work at a draft rate not less than 5%, and a flowing passage is arranged for passing fuel gas or oxidizing gas.例文帳に追加

Ｆｅ基合金等の金属板の表面上にＡｕ等の貴金属層を有し、これらが５％以上の圧下率で圧延加工をされてクラッド化されたものであり、更に燃料ガス又は酸化性ガスを通す流通路が設けられていることを特徴とする固体高分子型燃料電池用金属セパレータ。 - 特許庁

The composite magnetic material has a structure wherein a pillar structure made of a pure metal such as Fe, Co, or Ni or an alloy containing at least 20 wt.% of the metals is embedded into an inorganic insulating mother body made of oxide, nitride or fluoride or their mixture.例文帳に追加

複合磁性材料は、Ｆｅ、Ｃｏ、またはＮｉの各々の純金属ないしはそれらを少なくとも２０重量％含有する合金からなる柱状構造体が、酸化物、窒化物またはフッ化物ないしはそれらの混合物である無機質の絶縁性母体中に埋め込まれた構造を有する。 - 特許庁

A magnetic toner comprising a magnetic material containing an element except for Fe and a binder resin containing a vinyl resin having a carboxyl group and a vinyl resin having an epoxy group is used in combination with an image forming device equipped with a photoreceptor having a surface layer containing fluorocarbon resin particles dispersed in a polymer having an allylate structure.例文帳に追加

Ｆｅ以外の元素を含む磁性体と、カルボキシル基含有ビニル樹脂及びエポキシ基含有ビニル樹脂を含む結着樹脂とからなる磁性トナーを、ありレート構造を有する重合体にフッ素系樹脂粒子を分散させた表面層を有する感光体を備えた画像形成装置に組み合わせて用いる。 - 特許庁

The metal powder for powder metallurgy includes Zr and Si so that following conditions of (A) and (B) are satisfied, wherein the remainder is constituted of a metal material including at least one kind selected from the group comprising Fe, Co and Ni, and inevitable elements.例文帳に追加

本発明の粉末冶金用金属粉末は、ＺｒおよびＳｉを以下の（Ａ）および（Ｂ）の条件を満たすように含み、その残部が、Ｆｅ、ＣｏおよびＮｉからなる群から選択される少なくとも１種を含む金属材料および不可避元素で構成されていることを特徴とする粉末冶金用金属粉末。 - 特許庁

The method for producing the compound oxide nanoparticle black pigment comprises producing nanoparticles of the compound oxide through a supercritical hydrothermal process from an aqueous solution, as a source material, that contains each metal salt of Cu, Mn and Fe in a compounding ratio of Cu:Mn:Fe, by mole, of 1:1:0.6 or 1:1:0.3.例文帳に追加

この複合酸化物ナノ粒子黒色顔料を製造する方法は、Ｃｕ、Ｍｎ、Ｆｅの各金属塩をＣｕ：Ｍｎ：Ｆｅのモル比が１：１：０．６または１：１：０．３となる配合比で含む水溶液を原料として、超臨界水熱プロセスにより上記複合酸化物のナノ粒子を生成する。 - 特許庁

The positive electrode 23 includes, as an active material, a lithium-transmission metal-phosphor composite oxide having an olivine structure, wherein the transition metal is one or more selected from Fe, Mn, Ni and Co, and part of the phosphor is substituted by X that is one or more selected from B and Al in a predetermined ratio.例文帳に追加

この正極２３は、活物質として、オリビン型構造を有するリチウム−遷移金属−リン複合酸化物であって、遷移金属はＦｅ、Ｍｎ、Ｎｉ、Ｃｏから選ばれた１種以上であり、リンの一部はＢ、Ａｌから選ばれた１種以上であるＸに所定の割合で置換されている複合酸化物を含んでいる。 - 特許庁

To obtain an alloy wire rod for heat resistant spring in which the suppression of material cost is attained, an Fe based alloy wire is adopted therefor, further, high temperature oxidation is reduced even in a high temperature atmosphere exceeding 600°C, and further, stable thermal settling resistance can be obtained, and to obtain a heat resistant spring product using the alloy wire.例文帳に追加

材料費の抑制を図ることを第一の目的とし、その為にＦｅ基合金線を採用するとともに、６００℃を越えるような高温環境中でも高温酸化が少なく、また安定した耐熱へたり性を得る耐熱ばね用の合金線材並びに該合金線による耐熱バネ製品を得ることを目的とする。 - 特許庁

In the joint material for welding in which a layer of aluminum alloy having a step is disposed at least at an outermost end on one side, a content of an Fe component in the aluminum alloy is set to be 0.18 wt.% or less, and a content of an Mn component is set to be 0.63 wt.% or less.例文帳に追加

段差を有するアルミニウム合金の層が少なくとも片側の最外端に配置された溶接用継手材において、該アルミニウム合金中のＦｅ成分の含有量が０．１８ｗｔ％以下であり、かつ、Ｍｎ成分の含有量が０．６３ｗｔ％以下であることを特徴とする前記溶接用継手材。 - 特許庁

In the ferromagnetic ceramic composition, to the fundamental composition of an Sr_2FeMoO_6 double perovskite structure, while making the content of Fe in the B site lower than a theoretical composition value by a prescribed range, by adding Ca, while introducing this Ca into the B site, a part of the Ca is precipitated into crystal grain boundaries.例文帳に追加

この強磁性セラミック組成物は、Ｓｒ_２ＦｅＭｏＯ_６のダブルペロブスカイト構造の基本組成に対して、ＢサイトのＦｅを理論組成値よりも所定の範囲減らしながら、Ｃａを添加することにより、このＣａをＢサイトに導入しながら、Ｃａの一部を結晶粒界に析出させたものである。 - 特許庁

The transflective film is composed of the Ag base alloy made by compositely adding a specified small amount of Cu and P to Ag at the ratio of Cu≥P and, further as necessary, by additionally adding at least one kind of In, Sn, Zn, Au, Pt and Pd and/or at least one kind of Ni, Fe and Bi in a small amount.例文帳に追加

Ａｇに特定少量のＣｕとＰをＣｕ≧Ｐの比で複合添加し、さらに必要に応じてＩｎ、Ｓｎ、Ｚｎ、Ａｕ、ＰｔおよびＰｄの少なくとも１種および／またはＮｉ、ＦｅおよびＢｉの少なくとも１種を少量追加添加してなるＡｇ基合金から構成された半反射型半透過膜。 - 特許庁

To obtain a multilayer bearing in which the adhesive strength between an aluminum based bearing alloy and a steel back plate is secured by an intermediate layer composed of an aluminum alloy so as to prevent the formation of a brittle Al-Fe based compound on the boundary between the intermediate layer and the steel back plate in solution treatment, the strength of the bearing alloy is increased, and fatigue resistance is excellent.例文帳に追加

溶体化処理時に、アルミニウム合金からなる中間層と鋼裏金との界面に脆いＡｌ−Ｆｅ系化合物が生成されないように、中間層によるアルミニウム基軸受合金と鋼裏金との接着強度を確保し、軸受合金の強度を高め、耐疲労性に優れた多層軸受を得る。 - 特許庁

This epoxy resin composition for sealing the semiconductors is characterized as consisting essentially of (A) an epoxy resin, (B) a phenol resin, (C) a curing accelerator, (D) an inorganic filler and (E) a metal complex prepared by coordinating a ligand selected from naphthenic acid, acetylacetonato, phthalocyanine and thiocyanic acid with a metal element selected from Co, Cu, Zn, Ni, Mn and Fe.例文帳に追加

（Ａ）エポキシ樹脂、（Ｂ）フェノール樹脂、（Ｃ）硬化促進剤、（Ｄ）無機充填材、（Ｅ）Ｃｏ、Ｃｕ、Ｚｎ、Ｎｉ、Ｍｎ、Ｆｅから選択される金属元素にナフテン酸、アセチルアセトナート、フタロシアニン、チオシアン酸から選択される配位子が配位した金属錯体を必須成分とすることを特徴とする半導体封止用エポキシ樹脂組成物。 - 特許庁

More preferably, the copper alloy phase has a composition comprising, by mass%, 10 to 59% of Cu, and 1 to 5% of at least one element among Sn, Zn, Ni and P, the iron oxide phase occupies 3 to 20% of the matrix part except the pores by a cross-sectional area ratio, and the ferrite phase of the balance consists of Fe and unavoidable impurities.例文帳に追加

より好ましくは前記銅合金相は、Ｃｕ：１０〜５９質量％と、Ｓｎ、Ｚｎ、Ｎｉ、Ｐのうち少なくとも１種：１〜５質量％とからなり、酸化鉄相は気孔を除く基地部分の断面面積比で３〜２０％であり、残部のフェライト相はＦｅおよび不可避不純物からなる。 - 特許庁

The semiconductor laminated structure including impurities 16, where a group III-V compound crystal layer 17 is one or a plurality of Fe (iron), Cr (chromium), Mn (manganese), V (vanadium), C (carbon), O (oxygen) or B (boron).例文帳に追加

Ｓｉ基板１１の上方にエピタキシ成長によって設置されたIII−Ｖ族化合物結晶層１７が、Ｆｅ（鉄）あるいはＣｒ（クロム）あるいはＭｎ（マンガン）あるいはＶ（バナジウム）あるいはＣ（炭素）あるいはＯ（酸素）あるいはＢ（ホウ素）のうちの一つあるいはその複数である不純物１６を含む半導体積層構造とする。 - 特許庁

≥97% and ≤100×10-4/m2, respectively, is manufactured by firing the alumina powder whose purity and total amount of the impurity metals which are Si, Mg, Fe and alkali metals including Na, K and Li component are ≥99.9 wt.% and <100 ppm, respectively.例文帳に追加

純度が９９．９重量％以上であって、かつ不純物成分として、Ｓｉ成分、Ｍｇ成分、Ｆｅ成分、並びにＮａ成分、Ｋ成分、及びＬｉ成分を含むアルカリ金属成分が合計で１００ｐｐｍ未満であるアルミナ粉末を焼成することにより高純度のアルミナ焼結体を得ることができた。 - 特許庁

Then, the nano powder is heated to at least heating temperature in the first heat treatment for performing second heat treatment, thus forming the carbon layer coated transition metal nano structure having a metal core made of the transition metal of Fe, Co, or Ni and a carbon layer formed while the periphery of the metal core is coated.例文帳に追加

次いで、前記ナノ粉末を前記第１の熱処理における加熱温度以上に加熱して第２の熱処理を行い、Ｆｅ、Ｃｏ又はＮｉの遷移金属からなる金属コア及び前記金属コアの周囲を覆うようにして形成された炭素層を有する炭素層被覆遷移金属ナノ構造体を形成する。 - 特許庁