「continuous casting method」に関連した英語例文の一覧と使い方(24ページ目) - Weblio英語例文検索

To provide a continuous casting method of steel with which the sticking of oxide in molten steel to the inner surface of an immersion nozzle can be prevented and the development of defect in a product hot-rolled to an obtained cast slab can be prevented.例文帳に追加

浸漬ノズル内面への溶鋼中の酸化物の付着を防止でき、得られた鋳片を熱間圧延した製品の欠陥の発生を防止できる鋼の連続鋳造方法の提供。 - 特許庁

The method for the continuous casting is constituted in such a manner that the molten steel is supplied into a mold by using the device for supplying the molten steel, while energizing between the internal face of the immersion nozzle 4 and the molten steel 8 passing through the inside of the immersion nozzle.例文帳に追加

この溶鋼供給装置を用い、浸漬ノズル４の内面とその内部を通過する溶鋼８との間に通電しながら溶鋼を鋳型に供給する連続鋳造方法。 - 特許庁

To provide a control method for pushing down a side weir, in which linear grooves are prevented from being generated and gown on a refractory of the side weir along the outer periphery of a cooling drum, in a twin-drum type continuous casting.例文帳に追加

双ドラム式連続鋳造において、冷却ドラムの外周に沿いサイド堰耐火物上に線状溝が生成し、成長するのを抑制するサイド堰押し込み制御方法を提供する。 - 特許庁

Moreover, the method of continuous casting of this invention has a characteristic that a solidifying shell 3 is extracted while the oscillation propagating in the direction of extracting the piece of the cast is made to occur on the inner wall surface of the mold.例文帳に追加

又、本発明の連続鋳造方法は、鋳型内壁面に鋳片引き抜き方向へ向かって伝播する振動を発生させながら凝固シェル３を引き抜くことを特徴とする。 - 特許庁

To provide a method and a machine for continuous casting of steel that can effectively remove mixed layer of mold flux and oxide scale on the surface of cast piece which causes uneven cooling in the secondary cooling zone.例文帳に追加

２次冷却帯での不均一冷却の原因となる鋳片表面のモールドフラックスと酸化スケールの混合層を有効に除去しうる鋼の連続鋳造方法および装置を提供する。 - 特許庁

(2) In the continuous casting method mentioned in the above (1), the molten metal is molten steel, and the additional metal element is the metal including one or more selected from Mg, Bi, Ag, Ca, Te, Pb, Mn, Li and the like.例文帳に追加

（２）溶融金属が溶鋼であり、添加金属元素がＭｇ、Ｂｉ、Ａｇ、Ｃａ、Ｔｅ、Ｐｂ、Ｍｎ、Ｌｉなどの１種以上を含む金属である前記（１）に記載の連続鋳造方法。 - 特許庁

To provide a continuous casting method with which a cast slab having good quality can be produced by controlling pinch force and Joule heat given to a solidified shell at the initial stage so as to uniformize these in the peripheral direction.例文帳に追加

初期凝固殻に付与するピンチ力とジュール熱を周方向で均一となる様に制御し、良好な品質の鋳片を製造することができる連続鋳造方法を提供することにある。 - 特許庁

The method for manufacturing the powder for continuous casting, is performed, with which in the case of melting and solidifying the raw material for powder, this raw material is cooled and pulverized by injecting the air without using the water.例文帳に追加

パウダー原料を溶融して凝固するに際し、水を使用することなく空気を吹き付けることによって冷却、破砕させることを特徴とする連続鋳造用パウダーの製造方法である。 - 特許庁

To provide an abnormality diagnosis method where the abnormality of an electromagnetic coil in an electromagnetic field generator installed in a continuous casting machine can be diagnosed before the reduction in the insulation of the electromagnetic coil and interphase short circuit are generated.例文帳に追加

連続鋳造機に設置された電磁場発生装置の電磁コイルの異常を、電磁コイルの絶縁低下や相間短絡に到る前に、診断することのできる異常診断方法を提供する。 - 特許庁

To provide a method for diagnosing spray nozzles by which a state of spray nozzles used for the secondary cooling of a slab in a continuous casting machine is correctly and efficiently diagnosed, and to provide a diagnosing device.例文帳に追加

連続鋳造機において鋳片の二次冷却に用いられているスプレーノズルの状態を的確かつ効率的に診断することができるスプレーノズルの診断方法および診断装置を提供する。 - 特許庁

To provide a continuous casting method capable of preventing a γ grain boundary cracking on a cast slab surface layer part easily caused in a brittle temperature zone of a A_3 transformation temperature or lower appropriately in accordance with characteristics of steel grade.例文帳に追加

Ａ_3変態温度以下の脆化温度域において発生しやすい鋳片表層部のγ粒界割れを鋼種の特性に応じて的確に防止できる連続鋳造方法を提供する。 - 特許庁

To provide a water-cooled mold for continuous casting for producing an ingot in which crystal grains are uniformly grown by suppressing occurrence of an air gap between a mold and a protector, and to provide a method for producing the ingot.例文帳に追加

モールドとプロテクタとの間のエアーギャップの発生を抑制し、結晶粒が均一に成長した鋳塊を製造する連続鋳造用水冷鋳型及び鋳塊の製造方法を提供する。 - 特許庁

To provide a continuous casting method which does not require a large-scale reduction facility and still be able to perform smooth extraction of a dummy bar, while applying reduction on an unsolidified cast piece by protruding a bottom roll above the pass line on the bottom side of the cast piece.例文帳に追加

下部ロールを鋳片の下側パスラインよりも突出させて未凝固鋳片を圧下する際に、大規模な圧下設備を要せず、ダミーバーの円滑な引き抜きが可能な連続鋳造方法の提供。 - 特許庁

To provide a method of manufacturing anoxic copper wire and a copper alloy wire capable of obtaining a cast block of high quality without generating any porosity in the cast block, and having a large manufacturing yield when performing the continuous casting of anoxic copper and copper alloy by using a movable mold with high casting speed.例文帳に追加

無酸素銅や銅合金を鋳造速度の速い移動鋳型を用いて連続鋳造する際に、鋳塊内にポロシティが発生することなく高品質の鋳塊を得、製造歩留まりの大きい無酸素銅線や銅合金線を製造する方法を提供する。 - 特許庁

To provide a continuous casting method for molten steel by which in the case of casting a slab, etc., by applying electromagnetic stirring to molten steel in a mold, defect such as scab and blister, caused by gas bubble and inclusion caught into the surface layer part of the cast slab, is prevented and the cast slab excellent in the quality characteristic is obtained in a good yield.例文帳に追加

鋳型内の溶鋼を電磁攪拌してスラブ等を鋳造する際に、鋳片の表層部に捕捉される気泡や介在物に起因するヘゲ疵やフクレ疵等の欠陥を防止し、歩留りを良くして品質特性に優れた溶鋼の連続鋳造方法を提供する。 - 特許庁

To provide a method for inserting a continuously casting dummy bar with which various kinds of measurements are possible not only in the central part in the width direction of a continuous casting machine but also in a wide range in the width direction without influencing production efficiency, and also the productive efficiency is not reduced, and to provide a dummy bar used therefor.例文帳に追加

本発明の目的は、生産効率に影響なく、連続鋳造機の幅方向中心部だけでなく、幅方向の広い範囲で多種の測定ができ、且つ、生産効率の低下しない連続鋳造ダミーバーの挿入方法及びそれに使用するダミーバーを提供することである。 - 特許庁

To provide a continuous casting method for slab steel by which rolling reduction conditions are set not based on a solid phase ratio extremely difficult in precise estimation but based on easily understandable actual casting conditions to securely suppress central segregation with high reproducibility.例文帳に追加

精度よく予測することが極めて困難な固相率に基づくのではなく、容易に把握可能な実際の鋳造条件に基づいて圧下条件を設定することにより、高い再現性で確実に中心偏析を抑制できるスラブ鋼の連続鋳造方法を提供する - 特許庁

In the continuous casting method with which a plurality of rotational molding members 10, 11 are oppositely disposed while surrounding a casting space and the metallic cast material S1 is produced by driving these rotational molding member 10, 11 in the cast-out direction, the difference of high and low temperatures to the plurality of rotational molding members 10, 11 is given.例文帳に追加

複数の回転モールド部材10,11を鋳造空間を囲んで対向配置し、これらの回転モールド部材10,11を鋳出し方向に駆動することによって金属鋳造材Ｓ１を製造する連続鋳造方法において、複数の回転モールド部材10,11の温度に高低差を設ける。 - 特許庁

In the continuous casting method in which the cast slab pulled from a casting mold is unbent in a lower straightening zone, strains with the amount of 2% or more and less than 5% per each time are applied ten or more times to the cast slab before the cast slab reaches the lower straightening zone 9c.例文帳に追加

鋳型から引き抜いた鋳片を下部矯正帯において曲げ戻す連続鋳造方法において、前記下部矯正帯９ｃに鋳片が到達するまでの間に当該鋳片に、一回当たりの歪量が２％以上５％未満の歪を十回以上付与する。 - 特許庁

To cut a continuously cast stock changed in width with excellent yield, and to prevent insufficient width of the cut slab in a slab measuring method to determine the cutting position of the continuously cast stock in a slab continuous casting to change the width of a mold during the casting.例文帳に追加

本発明は、鋳込中にモールドの幅変更を行うスラブ連続鋳造において連続鋳造材の切断位置を決定するいわゆるスラブの採寸方法に係わり、特に幅変更された連続鋳造材を歩留りよく切断し、切断したスラブの幅不足を生じさせないようにする。 - 特許庁

To provide an evaluation method for segregation in a billet and a wire rod in evaluating the segregation in a continuous casting for the billet, wherein the segregation is simply evaluated without requiring skill, and without affected by evaluation dispersion of a short period caused in the casting.例文帳に追加

ビレットの連続鋳造において、偏析を評価する際に，ビレットおよび線材での偏析を測定する方法であって、熟練を必要とせずに簡易に偏析を評価する方法を提供するとともに、鋳片に生じる短周期の偏析ばらつきに影響を受けない偏析評価方法を提供する。 - 特許庁

To achieve an improved method for manufacturing copper based precipitation hardenable alloys, such as copper-chromium (CuCr), copper-chromium-zirconium (CuCrZr) and copper-zirconium (CuZr), by using continuous casting for an elongated casting, such as a rod, instead of a cast billet and thus to shorten the manufacturing process.例文帳に追加

鋳造ビレットの代わりに、棒などの細長い鋳造物用の連続鋳造を用いて、銅クロム（CuCr）と、銅クロムジルコニウム(CuCrZr)と、銅ジルコニウム(CuZr)などの銅系析出硬化形合金を製造する改善された方法を達成し、それによって製造工程を短縮することを目的とする。 - 特許庁

In a continuous casting method for casting an aluminum-killed steel into a mold from a ladle through a tundish, related to the heat insulating agent for adding onto the molten steel surface in the tundish, a high clean aluminum-killed steel is produced by changing the necessary charging quantity according to the liquidus temperature of this heat insulating agent.例文帳に追加

取鍋からタンディッシュを経由してモールドに、アルミキルド鋼を鋳造する連続鋳造法において、タンディッシュ内溶鋼表面に添加する保温剤について、その保温剤の液相線温度に応じて必要投入量を変化させることにより、高清浄のアルミキルド鋼を製造する。 - 特許庁

To provide a continuous casting method of steel, with which both of coarse granular crystal near the center and coarse columnar crystal surrounding the granular crystal can be made to fine equi-axed crystal, and a continuously cast slab cast by using this method.例文帳に追加

本発明は、中心近傍の粗い粒状晶とそれを取り囲む粗い柱状晶を、共に微細な等軸晶にできる鋼の連続鋳造方法およびそれを用いて鋳造した連続鋳造鋳片に関す提供する。 - 特許庁

(2) The method and the apparatus are a continuous casting method and apparatus for molten metal, wherein metal vapors and/or metal particles are blown into the molten metal, which flows through a discharge hole, with an inert gas from an opening made in the discharge hole of an immersion nozzle.例文帳に追加

（２）浸漬ノズルの吐出孔に設けた開口部から、吐出孔を通過する溶融金属に金属蒸気およびまたは金属粒子を不活性ガスとともに吹き込む溶融金属の連続鋳造方法および装置。 - 特許庁

The film is formed on a slanted plate 22 by friction welding so that an aluminum rod 45 formed by a continuous casting method and an extruding method is rotated to be brought into pressure contact with the surface 40 (41) of the slanted plate 22 to be processed, while the slanted plate is rotated as well.例文帳に追加

連続鋳造法と押出し法により成形されたアルミ棒４５を回転させて斜板２２の加工面４０（４１）に圧接すると共に、斜板２２も回転させる摩擦溶着によって斜板に皮膜を形成する。 - 特許庁

To provide a method and an apparatus for inexpensively and firmly coating a copper plate with a self-fluxing alloy, and to obtain a continuous casting mold having a high wear resistance and a long life by using the copper plate coated by the above method and apparatus.例文帳に追加

自溶性合金を安価でかつ強固に銅板に被覆する方法および装置を提供すると共に、これによって得られた銅板を用いて耐摩耗性の高く長寿命である連続鋳造用鋳型を得る。 - 特許庁

The method of evaluating the high temperature embrittlement of the continuous cast slab is the method for evaluating the occurrence of the transverse crack on the continuous cast slab, and based on the premeasured critical strain for crack formation in steel of the same steel grade as the cast slab during casting, the transverse crack sensibility in the cast slab is evaluated.例文帳に追加

本発明の連続鋳造鋳片の高温脆化評価方法は、連続鋳造鋳片の横割れの発生を評価する高温脆化評価方法であって、鋳造中の鋳片と同一鋼種において予め測定した割れ発生限界歪に基づいて、鋳片の横割れ感受性を評価する。 - 特許庁

In the method for casting the molten stainless steel by using the vertical-bending type continuous caster, by which the molten steel in a tundish is poured into a mold through an immersion nozzle by using the bending type continuous caster having the vertical part, the molten steel poured into the mold is cast while performing the electromagnetic stirring.例文帳に追加

垂直部を有する曲げ型連続鋳造機を用いてタンディッシュ内の溶鋼を浸漬ノズルを介して鋳型に注湯する垂直曲げ連鋳機を用いたステンレス溶鋼の鋳造方法において、鋳型に注湯した溶鋼を電磁攪拌しながら鋳造を行う。 - 特許庁

To provide a method for melting a nickel-containing stainless steel with which even in the case of utilizing cheap Cr-source and Ni-source at a larger quantity than conventional methods, the obtained molten nickel-containing stainless steel can be supplied into a continuous caster without breaking off, what is called, a consecutive continuous casting operation is performed.例文帳に追加

本発明は、安価なＣｒ源及びＮｉ源を従来より多量に利用しても、得られた含ニッケル・ステンレス溶鋼を所謂「連々鋳」を行う連続鋳造機へ途切れることなく供給可能な含ニッケル・ステンレス鋼の溶製方法を提供することを目的としている。 - 特許庁

CONTINUOUS CASTING METHOD OF Al-Mg-Si ALLOY AND Al-Mg-Si ALLOY INGOT, MANUFACTURING METHOD OF Al-Mg-Si ALLOY SHEET AND Al-Mg-Si ALLOY SHEET, AND MANUFACTURING METHOD OF HEAT RADIATION MATERIAL AND HEAT RADIATION MATERIAL例文帳に追加

Ａｌ−Ｍｇ−Ｓｉ系合金の連続鋳造方法およびＡｌ−Ｍｇ−Ｓｉ系合金鋳塊、Ａｌ−Ｍｇ−Ｓｉ系合金板材の製造方法およびＡｌ−Ｍｇ−Ｓｉ系合金板材、ならびに放熱部材の製造方法および放熱部材 - 特許庁

To provide a flow velocity measurement instrument in a continuous casting mold for steel where the flowing conditions of a molten steel pool in a mold for continuous casting can be directly detected at high precision, so as to suitably perform the control of the flowing, thus the improvement in the quality of a continuously cast slab can be attained, and to provide a channeling detection method performed using the same.例文帳に追加

連続鋳造用鋳型内の溶鋼プールの流動状況を直接高精度に検知することができ、これによって流動の制御を適切に行うことができ、その結果連続鋳造鋳片の品質の向上を図ることが可能な鋼の連続鋳造鋳型内流速測定装置及びこれを用いて行う偏流検知方法を提供すること。 - 特許庁

To provide a manufacturing technique of a cast slab for manufacturing an ultra-thick steel plate accompanying no lowering of the performance caused by negative segregation at the center part of the cast slab, in a continuous casting method for steel, performing rolling-reduction under state of non-solidifying.例文帳に追加

未凝固圧下を行う鋼の連続鋳造方法において、鋳片中心部の負偏析に起因する性能の低下を伴うことのない極厚鋼板を製造するための鋳片製造技術を提供する。 - 特許庁

In the continuous casting method, the immersed nozzle, in which at least a slag line portion is made of a material containing 15 mass% or more of carbon, is reused after the lapse of time more than 30 min. from the finish of pouring.例文帳に追加

少なくともスラグライン部が、カーボンを１５質量％以上含む素材で形成された浸漬ノズルを、鋳込み終了から３０分以上経過した後に再使用して連続鋳造する方法である。 - 特許庁

To provide a vertical type continuous casting method with which the grain diameter of equiaxed crystal generated at the center part of a large section cast slab for thick steel plate having ≥380 mm thickness of the cast slab, is made fine to attain improvement in the toughness.例文帳に追加

鋳片厚みが380mm以上の厚鋼板用大断面鋳片の中心部に生ずる等軸晶の粒径を微細化し、靭性改善を図ることができる垂直型連続鋳造方法を提供する。 - 特許庁

To provide the manufacture method for the aluminum alloy supporting body for the planography plate, avoiding that a cast metal plate is fixed to a cooling roller during the continuous casting of the aluminum alloy plate, the cast metal plate becomes defective, and the yield is lowered.例文帳に追加

アルミニウム合金板の連続鋳造中、鋳造板が冷却ローラに固着して鋳造板が不良となり、得率を低下させる平版印刷版用アルミニウム合金支持体の製造方法を提供する。 - 特許庁

To provide a steel product in which precipitates are finely dispersed and grain growth is suppressed and also to provide a continuous casting method by which alloying elements can be added, uniformly in high yield, into a cast slab in order to obtain the steel product.例文帳に追加

析出物を微細分散させ結晶粒成長を抑制した鋼材、およびその鋼材を得るために合金元素を均一かつ高歩留まりで鋳片内に添加できる連続鋳造方法を提供する。 - 特許庁

To obtain a method and an apparatus with which in the case of producing a magnesium-based metal sheet material with a continuous casting, the sheet material can be produced in good yield by preventing the development of defect, such as crack.例文帳に追加

マグネシウム系金属の板材を連続的な鋳造によって製造する際に、クラックなどの欠陥の発生を防止し、歩留まりよく板材を製造することのできる方法と装置の実現を目的とする。 - 特許庁

To provide a cooling metallic material at the top part of molten steel in continuous casting which can more quickly and safely be dipped into the top part of the molten steel in comparison with the conventional method even in the handling work of a worker.例文帳に追加

本発明は、作業者の手作業であっても、従来より迅速且つ安全に溶鋼トップに浸漬可能な連続鋳造における溶鋼トップの冷却金物を提供することを目的としている。 - 特許庁

To provide an observing method and its device for surely predicting break-out by continuously observing a surface temperature and a surface characteristic of a slab drawn out from a mold, in a continuous casting of steel.例文帳に追加

鉄鋼の連続鋳造において、鋳型から引き出されるスラブの表面温度および表面性状を連続して監視することにより、的確にブレークアウトを予知する監視方法および装置を提供する。 - 特許庁

To provide a heat insulating material with which the contamination of molten steel caused by air-oxidation and the reaction of the heat insulating material can surely be prevented, and a continuous casting method for obtaining a cast slab excellent in cleanliness.例文帳に追加

本発明は、空気酸化と保温材の反応に起因する溶鋼汚染を確実に防止できる保温材と清浄性の優れた鋳片を得るための連続鋳造方法を提供することを課題とする。 - 特許庁

To provide a dummy bar for continuous casting and a sealing method using this with which the sealing state is maintained by following with the change of a cross sectional area in a mold and the workability is good and the working efficiency is improved.例文帳に追加

鋳型内の断面積変化に追従してシール状態を維持すると共に、作業性を良好とし、作業効率も向上できる連続鋳造用ダミーバー及びこれを用いたシール方法を提供する。 - 特許庁

To provide a heat-retaining material capable of surely preventing contamination of molten steel, which is caused by air oxidation and reaction of a heat-retaining material; and to provide a continuous casting method for obtaining cast slab excellent in cleanliness.例文帳に追加

本発明は、空気酸化と保温材の反応に起因する溶鋼汚染を確実に防止できる保温材と清浄性の優れた鋳片を得るための連続鋳造方法を提供することを課題とする。 - 特許庁

(3) The continuous casting method described in the above (1) or (2), wherein the molten metal is the molten steel and the additional metallic element(s) is one or more kinds selected from magnesium, bismuth, calcium, tellurium, lead, manganese, yttrium and thallium, is provided.例文帳に追加

（３）前記溶融金属が溶鋼であり、前記添加金属元素がマグネシウム、ビスマス、カルシウム、テルル、鉛、マンガン、イッテルビウムおよびタリウムのうちの１種以上である前記（１）または（２）に記載の連続鋳造方法。 - 特許庁

To provide a continuous casting method for steel wherein the parting of a liquid seal is not caused by pressing force applied to a nozzle joint, and air suction from the nozzle joint is surely prevented over a long period.例文帳に追加

ノズル接合部に与えられる押付け力による液体シールの分断がなく、長期間にわたってノズル接合部からの大気の吸い込みを確実に防止できる鋼の連続鋳造方法を提供する。 - 特許庁