The formula (1): orientation α=(180-Δβ)/180, provided that Δβ expresses a half width when the X-ray diffraction intensity distribution from 0 to 360° azimuth angle direction is measured by fixing a peak scattering angle in the X-ray diffraction measurement.例文帳に追加

配向度α＝（１８０−Δβ）／１８０…（１）（但し、Δβは、Ｘ線回折測定によるピーク散乱角を固定して方位角方向の０〜３６０度までのＸ線回折強度分布を測定したときの半値幅を表す。） - 特許庁

In the expression, β is an angle defined by an incident plane of the incident X-ray and one direction in a surface of the transparent support, and I is diffraction intensity at 2θ=8° in an X-ray diffraction chart measured at the angle β.例文帳に追加

上記式中、βは、入射するＸ線の入射面と前記透明支持体面内のある１方向とのなす角度であり、Ｉは、角度βで測定したＸ線回折チャートにおける２θ＝８°での回折強度である。 - 特許庁

The raw material originated from shell or pearl is mechanochemically ground such that the factor of decrease based on diffraction intensity before grinding at a predetermined Miller index of aragonite crystal obtained by the X-ray diffraction method becomes a prescribed value.例文帳に追加

貝殻または真珠由来の原料をＸ線回折法において得られるアラゴナイト結晶の所定のミラー指数における回折強度の粉砕前を基準とした減少率を所定値とするようにメカノケミカル粉砕する。 - 特許庁

Photo detectors 55a-55d for detecting the intensity of the constituent of pixels at four corners are arranged corresponding to the pixels at the four corners of the diffraction light page information part 7a, and the diffraction light page information part 7a is applied to the photo detectors 55a-55d.例文帳に追加

回折光ページ情報部分7aの四隅の画素に対応させて、四隅の画素の成分の強度を検出する光検出器55a〜55dを配置し、これら光検出器55a〜55dに回折光ページ情報部分7aを入射させる。 - 特許庁

A carbon material for the electric double-layer capacitor electrode uses oil raw coke as a raw material, such that a graphite-like crystal structure parameter (Ip/Io) at a diffraction peak of a (002) surface of an X-ray diffraction intensity curve is >0.3 and ≤0.8.例文帳に追加

Ｘ線回折強度曲線の（００２）面の回折ピークにおける黒鉛的結晶構造パラメーター（Ｉｐ／Ｉｏ）が０．３＜Ｉｐ／Ｉｏ≦０．８である石油生コークスを原料とする電気二重層キャパシタ電極用炭素材。 - 特許庁

To provide a light intensity adjusting device capable of preventing the deterioration of an MTF by small diaphragm diffraction, of enhancing the controllability of a diaphragm, and of saving a space, and provide an optical device and a photographic device having the light intensity adjusting device.例文帳に追加

小絞り回折によるＭＴＦの劣化を防止し、絞りの制御性を向上させ、小スペース化を図ることが可能となる光量調整装置、該光量調整装置を有する光学装置および撮影装置を提供する。 - 特許庁

The magnetic particle has a magnetic property, wherein a ratio of peak intensity corresponding to Co with respect to peak intensity corresponding to CoAl_2O_4 by X-ray diffraction is 0.1-0.5, and a median diameter is 0.01-0.1 μm.例文帳に追加

Ｘ線回折によるＣｏＡｌ_２Ｏ_４に相当するピーク強度に対するＣｏに相当するピーク強度の比が０．１以上０．５以下であり、メディアン径が０．０１μｍ以上０．１μｍ以下である、磁性を有する磁性粒子とする。 - 特許庁

Supposing that the (111) face detection peak intensity is (a) and that the (200) face detection peak intensity is b when crystal structures analysis of platinum is executed by an X-ray diffraction method, the platinum electrode films 7, 8 have the ratio (b/a) of 0.01-0.1.例文帳に追加

白金電極膜７、８は、白金をＸ線回折法によって結晶構造解析した際の、（１１１）面検出ピーク強度をａとし（２００）面検出ピーク強度をｂとすると、その比率（ｂ／ａ）が０．０１〜０．１である。 - 特許庁

Considering that quartic diffracted image intensity is preferably less than at least primary diffracted image intensity, it is evident that image deterioration due to diffraction is reducible on condition that the numerical aperture is ≥70%.例文帳に追加

少なくとも１次の回折像強度より４次の回折像強度が低くなることが望ましいことを考慮すると、実験結果から、開口率が７０％以上であれば、回折による画像劣化を低減させ得ることが分かる。 - 特許庁

The diffraction grating 3 is so set that the decreasing rate of the intensity of the 0 order diffracted light becomes smaller the nearer the peripheral part from near the optical axis and on the other hand the intensity of each of the pair of the ±lst order diffracted light becomes smaller.例文帳に追加

回折格子３は、光軸近傍から周辺部に向かうに従い、０次回折光の強度の低下率が小さくなる一方、一対の±１次回折光それぞれの強度が小さくなるように設定されている。 - 特許庁

A reference electric field intensity calculation unit 10 calculates a reference reception height hb at a reception point where a first Fresnel zone is not shielded by the ground, and calculates diffraction loss Lf, ridge loss Lr, and phase loss Lθ by masking diffraction loss, ridge loss, and diffraction loss within a city attenuation region with respect to the reception point.例文帳に追加

基準電界強度計算部１０は、第１フレネルゾーンが大地により遮蔽されない受信点の基準受信高ｈｂを計算し、その受信点について、都市減衰領域内の回折損失、リッジ損失及び回折損失をマスクして回折損失Ｌｆ、リッジ損失Ｌｒ及び位相損失Ｌθを計算する。 - 特許庁

When analyzed by X-ray diffraction measurement, this molybdenum exhibits, in at least part of the region corresponding to a sheet-thicknesswise depth of one fifth of the whole thickness from the surface, areas which each contain such a domain where the peak intensities of the (110) and (220) diffraction planes are each lower than the peak intensity of the (211) diffraction plane.例文帳に追加

本発明のモリブデン材は、表面から板厚方向に向かって全厚の５分の１の深さに該当する領域において、Ｘ線回折測定した場合、結晶回折面（１１０）および（２２０）のそれぞれのピーク強度が、（２１１）のピーク強度未満となる領域が存在する部分を少なくとも一部に有する。 - 特許庁

To improve the measurement accuracy of the amount of adhesion of a metallic phase by improving X-ray diffraction intensity from the metallic phase contained in a plated layer in a method for measuring the amount of adhesion of the metallic phase contained in the plated layer using the X-ray diffraction method.例文帳に追加

Ｘ線回折法を用いた、めっき層に含まれる金属相の付着量を測定する方法において、めっき層に含まれる金属相からの回折Ｘ線強度を高め、金属相の付着量の測定精度を向上させる。 - 特許庁

To reduce the intensity of diffraction light spreading to parts other than a photoelectric conversion unit by diffraction effect of light incident upon an opening in the photoelectric conversion unit serving as a light-receiving unit to increase the sensitivity, thereby suppressing noise such as smear or color mixture in a solid-state image pickup device.例文帳に追加

固体撮像装置において、受光部となる光電変換部の開口部に入射した光の回折効果で光電変換部以外に広がる回折光の強度を弱め、感度向上を図り、スミアあるいは混色などのノイズを抑制する。 - 特許庁

The above problem can be solved by using a coloring agent composed of a pseudo-unidimensional crystalline organic color pigment exhibiting X-ray diffraction spectrum having the refraction line showing the maximum intensity and its n-th order ((n) is an integer of ≥2) diffraction lines as main peaks.例文帳に追加

Ｘ線回折スペクトルにおいて、最大強度を示す回折線とそのｎ次（ｎ：２以上の整数）の回折線を主要ピークとして有する擬１次元結晶性カラー有機顔料からなる着色剤により、上記の課題を解決する。 - 特許庁

As the graphitized carbon fiber, it is preferable to have <3,370 nm surface distance (d002) between graphite layers of the graphitized carbon fiber and ≥1.15 peak intensity ratio (P101/P100) of (101) diffraction peak and (100) diffraction peak.例文帳に追加

黒鉛化炭素繊維は、Ｘ線回折法による黒鉛化炭素繊維の黒鉛層間の面間隔（ｄ００２）が０．３３７０ｎｍ未満、かつ、（１０１）回折ピークと（１００）回折ピークのピーク強度比（Ｐ１０１／Ｐ１００）が１．１５以上であることが好ましい。 - 特許庁

As compared with a method for measuring the diffraction line intensity of asbestos by scanning the light detection slit 5 and the X-ray detector 8, a measuring time can be shortened largely.例文帳に追加

受光スリット５及びＸ線検出器８のスキャンによってアスベストの回折線強度を測定することに比べて、測定時間を大幅に短縮できる。 - 特許庁

The optical detector 3 detects the diaphragm 2 being displaced in two dimensions by detecting not a difference in light intensity, but a two-dimensional image of a diffraction image.例文帳に追加

光検出器３は、光強度の違いを検出するのではなく、回折像の２次元的な像の検出により、２次元的な振動板２の変位の検出を行う。 - 特許庁

To obtain tellurite-based glass having incident wave vibrational direction dependency of second harmonic wave intensity, a diffraction grating and a periodical structure of refractive index with tunable characteristic.例文帳に追加

第２高調波の強度の入射波振動方向依存性を持ち、波長可変特性を持つ回折格子や屈折率周期構造を有するテルライト系ガラスの提供。 - 特許庁

The primary particle diameter may be 5-10 μm, and the X-ray diffraction peak intensity ratio of I(111)/I(311) may be 1.5-3.0.例文帳に追加

前記一次粒子直径が５ないし１０μｍであり、前記Ｘ線回折ピーク強度のＩ（１１１）／Ｉ（３１１）が、１．５ないし３．０であることを特徴とする。 - 特許庁

Light that is reflected by the fiber Bragg diffraction gratings is separated and radiated spatially, and the spatially separated beam reaches the maximum intensity in a different polarization state.例文帳に追加

ファイバ・ブラッグ回折格子にて反射された光が空間的に分離して放射され、空間的に分離されたビームが異なる偏光状態で最大強度になる。 - 特許庁

Normally, intensity distribution of an electron beam is not of a rectangular distribution that faithfully corresponds to (a) because of diffraction phenomenon, but has a distribution containing a specified widening as in (b).例文帳に追加

通常は、回折現象のため、電子線の強度分布は（ａ）に忠実に対応するような矩形分布とならず、（ｂ）のように所定の広がりを持った分布となる。 - 特許庁

The dielectric porcelain contains barium titanate as a main component and contains prescribed amounts of vanadium, magnesium, manganese and rare earth elements, wherein the diffraction intensity of the (004) plane showing the barium titanate in a tetragonal system is higher than the diffraction intensity of the (004) plane showing the barium titanate in a cubic system, and the average particle diameter of crystal particles is 0.21 to 0.28 μm.例文帳に追加

誘電体磁器がチタン酸バリウムを主成分として、バナジウム、マグネシウム、マンガンおよび希土類元素を所定量含み、正方晶系のチタン酸バリウムを示す（００４）面の回折強度が立方晶系のチタン酸バリウムを示す（００４）面の回折強度よりも大きく、結晶粒子の平均粒径が０．２１〜０．２８μｍである。 - 特許庁

The adjustment part 190 divides the intensity distribution detected by the detector 170 into multiple regions, and adjusts an attitude of at least one of the diffraction grating 130 and the shielding grating 150, based on the intensity distribution of the multiple regions.例文帳に追加

調整部１９０は、検出器１７０で検出された強度分布を複数の領域に分割し、複数の領域の強度分布に基づいて、回折格子１３０および遮蔽格子１５０のうち少なくともいずれか一方の姿勢を調整する。 - 特許庁

By the measurement of X-ray diffraction of the yttria - alumina compound oxide film, the ratio YAG (420)/M of the peak intensity YAG (420) of the (420) plane in the garnet phase to the maximum peak intensity M of other crystalline phases is ≥2.5.例文帳に追加

イットリア−アルミナ複合酸化物膜のＸ線回折測定によって得られるガーネット相の（４２０）面のピーク強度ＹＡＧ（４２０）を、これ以外の結晶相の最大ピーク強度Ｍによって除した値ＹＡＧ（４２０）／Ｍが２．５以上である。 - 特許庁

In this catalyst for manufacturing acrylic acid, the ratio of peak intensity measured by X-ray diffraction analysis at d=4.38 Å (d4.38) to peak intensity at d=4.00 Å (d4.00) is less than 0.07.例文帳に追加

触媒のＸ線回折分析によって測定したｄ＝４．３８オングストロームにおけるピーク強度（ｄ４．３８）とｄ＝４．００オングストロームにおけるピーク強度（ｄ４．００）との比（ｄ４．３８／ｄ４．００）が０．０７未満であるアクリル酸製造用触媒。 - 特許庁

As an optical intensity control means, a variation on optical intensity in the 0th diffracted light of an acousto-optical element (AOM) is controlled by controlling diffraction efficiency using the AOM, and further, the 0th diffracted light is shaped by a spatial frequency filter.例文帳に追加

光強度制御手段としては、音響光学素子（ＡＯＭ）を用いて回折効率を制御することでＡＯＭの０次回折光における光強度変化量を制御し、さらに０次回折光を空間周波数フィルタで整形する。 - 特許庁

In the titanium alloy, an α phase of titanium is dispersed into a β phase of titanium so that the ratio (Iα/Iβ) between the peak intensity Iα of the α phase and the peak intensity Iβ of the β phase by X-ray diffraction in the titanium alloy is controlled to 0.03 to 0.4.例文帳に追加

チタン合金中にＸ線回折によるα相のピーク強度Ｉαとβ相のピーク強度Ｉβの比（Ｉα／Ｉβ）が０．０３以上、０．４以下となるように、チタンのβ相中にチタンのα相が分散される。 - 特許庁

A pellet is obtained by cutting polyethylene terephthalate with an intrinsic viscosity of 0.70 dl/g or higher, whose diffraction peak intensity ratio of surface (100) and surface (110) is 1.4 or higher and 2.4 or lower when measured by the X-ray diffraction of the cut surface.例文帳に追加

固有粘度が０．７０ｄｌ／ｇ以上のポリエチレンテレフタレートを切断して得られるペレットであって、そのカット面のＸ線回折により測定した（100）面と（110）面の回折ピーク強度比が１．４以上２．４以下であることを特徴とするポリエチレンテレフタレート樹脂ペレット。 - 特許庁

To provide an X-ray diffraction device which has exceedingly high resolution and also can acquire an X-ray diffraction image with high intensity, by enabling both cylindrical surface conversion processing and time delay integration processing to be performed in the same arithmetic control process.例文帳に追加

円筒面変換処理と時間遅延積分処理との両方を同じ演算制御過程内で行うことを可能にすることにより、極めて分解能が高く、しかも強度の高い回折Ｘ線像を得ることができるＸ線回折装置を提供する。 - 特許庁

Further, the stainless steel wire has a texture in which the ratio of a martensitic phase induced by wire drawing is ≤15 vol.%, and the balance austenitic phase, and the diffraction intensity of the austenitic phase by an X-ray diffraction method in the longitudinal direction satisfies both of I(200)/I(111)≥2.0 and I(220)/I(111)≥3.0.例文帳に追加

また、線引き加工によって誘起されるマルテンサイト相が15体積％以下、残部がオーステナイト相からなると共に、鋼線長手方向のX線回折法によるオーステナイト相の回折強度がI(200)/I(111)≧2.0、及びI(220)/I(111)≧3.0の双方を満たす集合組織を有する。 - 特許庁

The optical image intensity distribution formed on a resist disposed on the side of a lower layer of a diffraction pattern by performing whole image exposure from the side of an upper surface of the diffraction pattern formed by lines L and spaces S on a substrate at a predetermined pattern pitch is calculated by using a multi-mode waveguide path analytic model or fractional Fourier transform for the diffraction pattern.例文帳に追加

ラインＬとスペースＳによって所定のパターンピッチで基板上に形成された回折パターンの上面側から全面露光を行なうことによって回折パターンの下層側に配置されたレジストに形成される光学像強度分布を、回折パターンに対してマルチモード導波路解析モデル又はフラクショナルフーリエ変換を用いることにより算出する。 - 特許庁

To obtain high diffraction efficiency by remarkably minimizing the difference of refractive index on the boundary between a polymer dispersed liquid crystal (PDLC) and a glass substrate from before exposure till after exposure to decrease the light reflection intensity.例文帳に追加

露光前から露光後までにおいてＰＤＬＣ混合物とガラス基板との界面での屈折率差を極めて小さくして反射光量を減らし、高効率な回折効率を得る。 - 特許庁

Luminous flux from a light source 1 generates a pattern having prescribed intensity through a relay lens 5 on a plane of incidence of a fly's eye lens 6 by a diffraction optical element 4 as a luminous flux conversion means.例文帳に追加

光源１からの光束は，光束変換手段である回折光学素子４により，リレーレンズ５を介してフライアイレンズ６の入射面に所定の強度パターンを発生する。 - 特許庁

To restrain a reflection loss of a beam emitted from an optical fiber, in a spectroscope using a PDA detector for detecting light intensity using a diffraction grating.例文帳に追加

回折格子を用いて光強度を検出するＰＤＡ検出器を用いた分光装置において光ファイバから出射する光線の反射損失を抑制した分光装置を提供する。 - 特許庁

Alternatively, in the Mo target material, the relative intensity ratio R_(110) in the (110) plane standardized by the main peak 4 points in the X-ray diffraction of the sputter face is ≥40%.例文帳に追加

また、好ましくは、スパッタ面のＸ線回折における主ピーク４点で規格化した（１１０）面の相対強度比Ｒ_（１１０）が４０％以上であるＭｏターゲット材である。 - 特許庁

This PBN vessel to be used in producing the subject compound semiconductor single crystal is so designed that the X-ray diffraction integral intensity ratio for (100)-face and (002)-face: {I (002)/I (100) } determined for the face perpendicular to the thickness direction of the PBN vessel is set at 8-50.例文帳に追加

ＰＢＮ製容器の厚さ方向に垂直な面で測定した（１００）面と（００２）面のＸ線回折積分強度比｛Ｉ（００２）／Ｉ（１００）｝の値を８〜５０に設定した。 - 特許庁

To provide an illumination optical system capable of suppressing an influence of diffraction blurring caused by a micro reflection surface of each mirror element to low levels and forming accurately a desired pupil intensity distribution.例文帳に追加

各ミラー要素の微小な反射面に起因する回折ぼけの影響を小さく抑えて、所望の瞳強度分布を精度良く形成することのできる照明光学系。 - 特許庁

The negative electrode of a hybrid capacitor consists of a carbon material which has a degree of graphitization P_1 determined from a 11-diffraction line intensity in a range of 0.3≤P_1≤0.8 by using a CuKα beam.例文帳に追加

ハイブリッドキャパシタの負極を、ＣｕＫα線を用いて測定される１１回折線強度から求められる黒鉛化度Ｐ_１が、０．３≦Ｐ_１≦０．８である炭素材料で構成する。 - 特許庁

In the light spots 28A and 28B, their intensity can be separately adjusted, and astigmatism is also suppressed because the light spots 28A and 28B are generated from the different light sources without using diffraction grating, etc.例文帳に追加

光スポット２８Ａ，２８Ｂは、個々に強度を調整可能となり、また、回折格子等を使用することなく、別々の光源から生成されるので、非点収差が抑制される。 - 特許庁

A ratio of peak intensity at (222) plane to that of (400) plane of the indium tin oxide of the ITO transparent conductive film at an X-ray diffraction is not less than 1:1 and not larger than 4:1.例文帳に追加

成膜されるＩＴＯ透明導電膜は、Ｘ線回析において、酸化インジウム錫の（２２２）面のピーク強度と（４００）面のピーク強度の比が１：１以上４：１以下である。 - 特許庁

Intensity of zero-order diffraction light is reduced and a phase is delayed by 1/4 wavelength by an annular phase plate 5 arranged in a rear focal position of an objective lens 4, as to reflected light in the wafer 8.例文帳に追加

ウェーハ８での反射光に対し、対物レンズ４の後ろ焦点位置に配した環状の位相板５は、零次回折光の強度低減と位相の１／４波長遅延とを行う。 - 特許庁

To provide a point diffraction interferometer enabling development of relatively high-intensity radiation, utilization of an interferometer analysis, and also use of an extended source emitting spatially-incoherent radiation.例文帳に追加

比較的高強度の放射線の達成を可能にし、干渉計分析を利用可能にし、また空間的に非干渉性の放射線を放出する分散光源の使用も可能にする。 - 特許庁

Since the charge transfer timing of the CCD sensor 22 is synchronized with its scanning moving distance, the X-ray intensity at each diffraction angle can be accumulated accurately by each CCD pixel.例文帳に追加

ＣＣＤセンサ２２の電荷転送タイミングとその走査移動距離が同期しているので、個々の回折角度におけるＸ線強度を個々のＣＣＤ画素によって正確に蓄積できる。 - 特許庁

In TEM, the diffraction intensity distribution is spread out in the form of a spike, normal to the crystal plate, because the crystal is usually in the form of a plate, normal to the beam. 例文帳に追加

TEMにおいては、回折強度分布は結晶プレートに対して垂直なスパイクの形で広げられる(広がっている); なぜなら、結晶は普通、ビームに対して垂直なプレートの形だからである。 - 科学技術論文動詞集