To provide electroplating equipment and an electroplating method by which uniform plating-film thickness on the surface of a substrate to be plated can be obtained and a stable bump shape in a plating filling part can be formed and, further, high-speed plating can be attained.例文帳に追加

被めっき基板表面の均一なめっき膜厚およびめっき充填部の安定したバンプ形状を形成することが可能で、しかも、高速めっきを可能とする電気めっき装置および電気めっき方法を提供する。 - 特許庁

To provide a plating method which can stably keep high deposition efficiency, forms few cracks in an extent of practically causing no problem, and can form a plated film of adequate quality.例文帳に追加

析出効率を高く安定に維持することができ、クラックの発生が実用上問題にならないくらいに少なくて、良好なめっき皮膜を形成することのできるめっき方法を提供すること。 - 特許庁

As to the treating method, the surface of a plated steel sheet is coated with this surface treating soln. so as to control the thickness of dry film to 0.1 to 5 μm, and after that, without executing water-washing, it is dried at 80 to 250°C sheet temp.例文帳に追加

処理方法はこの表面処理液をめっき鋼板表面に乾燥皮膜厚が０.１〜５μｍになるように塗布した後、水洗せず、板温８０〜２５０℃で乾燥する。 - 特許庁

This metal-plating method for the metallic sheet comprises the steps of: covering the metallic sheet with metallic particles having an average particle diameter of 1/3 or less of an average thickness of a film to be plated; and heating the metallic sheet to a melting point of the metallic particle or higher.例文帳に追加

平均粒径が平均めっき膜厚値の１／３以下である金属めっき微粒子を金属板に被覆させた後、該金属板を前記金属めっき微粒子の融点以上の温度に加熱し、金属板に金属めっき処理を行う。 - 特許庁

To obtain excellent workability, corrosion resistance in the worked part and rolled formability in a surface treated steel sheet using a hot dip Al-Zn based plated steel sheet in which the content of Al in a plating film is 20 to 95 mass% as a base steel sheet.例文帳に追加

めっき皮膜中のＡｌ含有量が２０〜９５mass％の溶融Ａｌ−Ｚｎ系めっき鋼板を下地鋼板とする表面処理鋼板において、優れた加工性、加工部耐食性及びロールフォーミング性を得る。 - 特許庁

To provide a method for producing a titanium material having a plated film of a noble metal, which has a high covering rate and is extremely thin, and to provide the titanium material obtained by the method.例文帳に追加

被覆率が高く、かつ極薄の貴金属めっきを施したチタン材の製造方法、及びその方法によって得られるチタン材を提供することを目的とする。 - 特許庁

To manufacture a wire rod with attractive texture for a fishhook which has improved corrosion resistance and has satisfactory luster on a plated film, and to improve a working environment in fishhook manufacturing.例文帳に追加

耐食性を向上し、かつ良好なメッキ光沢を有する釣針となる美麗な線肌の釣針用線材を製造可能にし、合わせて釣針製造における作業環境の改善を図る。 - 特許庁

To provide equipment and a method for manufacturing a dispersion plated sheet in which particles are uniformly dispersed in a plating film by a hot-dip method.例文帳に追加

溶融めっき方式により、めっき皮膜中に粒子が均一に分散した分散めっき板を製造することができる製造設備および製造方法を提供する。 - 特許庁

To form an electroless-plated metal film which constitutes an electromagnetic shield layer and has adequate adhesiveness, on the surface of a housing made from a resin, without employing such treatment as to use chemicals containing an element such as chromium, which gives a large load to the environment.例文帳に追加

樹脂筐体の表面に電磁シールド層を構成する金属無電解めっき皮膜を、クロム等の環境負荷の大きな薬品による処理を用いることなく、密着性よく形成する。 - 特許庁

A conductive plated coating film coats the first face of a support block, the second face opposite to the first face, and the first through hole and the second through hole for communicating the first face with the second face.例文帳に追加

支持ブロックの第1面、第1面と反対側の第2面、第1面と第2面を連通する第1貫通孔及び第2貫通孔は、導電性のメッキ被膜で覆われる。 - 特許庁

To provide a surface treatment apparatus which improves an ease of maintenance such as removal of a plated film adhering to a setting holder, and prevents blooming at the edge of a cylinder head bore.例文帳に追加

セット治具に付着するめっきの除去等のメンテナンス性を向上させるとともに、シリンダヘッドボア端面の花咲きを防止する表面処理装置を提供する。 - 特許庁

To provide a spring contact probe capable of preventing invasion of dust or the like through transparent holes 16, 18 into a conductive tube 10 having transparent holes 16, 18 bored on the blocked end side and having the inner peripheral wall plated with a conductive thin film.例文帳に追加

閉塞端側に透孔１６，１８を穿設して内周壁に導電薄膜のメッキを施した導電チューブ１０内に、透孔１６，１８を介して塵埃などが侵入することのないスプリングコンタクトプローブを提供する。 - 特許庁

The treatment is executed in such a manner that the treating soln. is applied on a plated steel sheet so as to control the thickness of a dry film to 0.1 to 5 μm, and, after that, without washing by water, it is dried at 80 to 250°C sheet temp.例文帳に追加

処理は処理液をめっき鋼板に乾燥皮膜厚が０.１〜５μｍになるように塗布した後、水洗せずに板温８０〜２５０℃で乾燥する。 - 特許庁

To provide a manufacturing method of a magnetostrictive torque sensor capable of confining the sensitivity variation of a magnetostrictive film to be within a desired range, when a magnetostrictive material plated section is to be high-frequency heated for imparting magnetic anisotropy.例文帳に追加

磁気異方性の付加のため磁歪材めっき部を高周波加熱するとき、磁歪膜の感度バラツキを所望範囲に収めることができる磁歪式トルクセンサの製造方法を提供する。 - 特許庁

To provide an electroplating method and an electroplating apparatus in which a dense plated film is formed by micronizing a plating generating nucleus or a plating grain and which are capable of coping with the formation of micronized wiring on a substrate.例文帳に追加

めっき発生核やめっき粒の微細化を図ることで緻密なめっき膜を形成でき、微細化が進む基板上の配線形成に対応することが可能な電解めっき方法及び電解めっき装置を提供する。 - 特許庁

To provide a surface treating soln. for a plated steel sheet capable of forming a film excellent in corrosion resistance, adhesion after coating and resistance weldability and to provide a method for treating the same.例文帳に追加

耐食性、塗装後密着性および抵抗溶接性に優れた皮膜を形成できるめっき鋼板用表面処理液およびその処理方法を提供する。 - 特許庁

This sliding member has cracks formed in the Cr-plated film of the inner circumferential surface 3 of the rotor housing 1 so that the width of the cracks can be wider and the number of the cracks can be larger on the inner circumferential surface 3a of the major axis side than on the inner circumferential surface 3b of the minor axis side.例文帳に追加

ローターハウジング１の内周面３のＣｒめっき皮膜にクラックを形成し、長軸側内周面３ａでは短軸側内周面３ｂよりも、クラック幅が大きく且つクラック数が多くなるようにする。 - 特許庁

In the case the solar heat transmissivity T_E/NIR in a wavelength range of 0.8-2.1 μm of the paint film is as high as 20% or more, a metal base (e.g. an Al-based plated steel plate) with high R_E/NIR of 40% or more is used to utilize reflection also from the base.例文帳に追加

この塗膜の 0.8〜2.1 μｍの波長域での太陽熱透過率Ｔ_E/NIR が20％以上と高い場合には、Ｒ_E/NIR が40％以上と高い金属基板 (例、Al系めっき鋼板) を使用し、基板からの反射も利用する。 - 特許庁

The sort of plated film to be formed on an electro-conductive member 21 can be selected by means of moving the plating liquid back and forth between the plating bath tank and the plating liquid storage tank.例文帳に追加

そして、メッキ浴槽とメッキ液収納浴槽でメッキ液を移動させることにより、導電部材２１に形成するメッキ膜を選択することができる。 - 特許庁

To provide: a thermally conductive member which has excellent thermal conductivity and a predetermined composite-film plated on the surface of the base material; automotive parts to which the member is applied; a manufacturing method therefor; and a plating solution to be used in the manufacturing method.例文帳に追加

優れた熱伝導性を有し、基材表面に所定の複合材めっき膜を備えた熱伝導部材、これを適用した自動車用部品、その製造方法及びその製造方法に用いるめっき液を提供すること。 - 特許庁

To find out a post-treatment film capable of suppressing the plating peeling or mold scoring generated at a time of the processing of an aluminum plated steel sheet used in household electric products and building materials and also suppressing even the adhesion of a contaminant in use environment (outdoor exposure).例文帳に追加

家電、建材用途に用いられるアルミめっき鋼板の、加工時に発生するめっき剥離や型カジリを抑制し、かつ使用環境中（屋外暴露）での汚れ付着をも抑制可能な後処理皮膜を見出す。 - 特許庁

To provide a lead wire for an electronic part, which contains no poisonous lead although it has a plated film mainly containing Sn, is inexpensive, and can surely prevent the generation of whisker; and a flat cable comprising the same.例文帳に追加

Ｓｎ主体のメッキを有しつつも、有毒な鉛を全く含有せず、低コストでウィスカの発生がより確実に防止できる電子部品用リード線及び該リード線よりなるフラットケーブルを提供せんとする。 - 特許庁

To accurately grasp the exchange timing of coating or a member by discriminating a burnt coating that allows a plating skin film thickness to fully remain and has no problems in corrosiveness from rust, where coat in an ordinal state is corroded in a fused zinc object to be plated.例文帳に追加

溶融亜鉛被めっき物において、めっき皮膜厚は十分残存し耐食性には何ら問題がないやけ皮膜と、常態皮膜が腐食した錆とを判別し、塗装または部材の取替え時期を的確に把握すること。 - 特許庁

The display work 13 is displayed magnetically attached to the line-shaped magnet members 9 of the middle cloth 3 by sticking a steel sheet 14 or putting it in a steel plated bag 15 formed of a transparent material or in a transparent resin film bag 16.例文帳に追加

展示作品１３はスチール薄板１４を貼着するか、透明な素材からなるスチール板付袋１５に入れるか、透明な樹脂フイルム袋１６に入れるかして中布３の条形磁石部材９に磁着させ展示する。 - 特許庁

To secure the thickness uniformity of a plated film and reduce a poor appearance, by devising a cross sectional shape of a cathode body and thereby inhibiting the reduction of the flowability and the mixing rate of chips.例文帳に追加

カソード電極体の断面形状を工夫することにより、チップ流動性の阻害、混合率の低下を抑制し、めっき膜厚の均一性を確保し、外観不良の低減を図る。 - 特許庁

The surface of a zinc or aluminum plated steel sheet is provided with a chromate film of 10 to 150 mg/m2 by the coating weight expressed in terms of chromium.例文帳に追加

めっき鋼板の表面のクロメート皮膜の付着量をクロム換算で１０〜１５０ｍｇ／ｍ^2 とし、６価クロム含有量を０〜２５ｍｇ／ｍ^2 、無機および有機酸根のモル量と酸価の積をクロムのモル量の２倍以下とする。 - 特許庁

To provide a method for forming a satisfactory electrodes gold-plated film superior in solderability, directly on a copper based material such as a copper circuit of a printed circuit board and a joint part of an electronic component.例文帳に追加

プリント回路基板の銅回路、電子部品の接合部等の銅系材料上に、ハンダ接合性に優れた良好な無電解金めっき皮膜を直接形成できる方法を提供する。 - 特許庁

To perform minute plating under different conditions for portions on a substrate, and to obtain a plated film having satisfactory intra-plane uniformity by suppressing the influence of sheet resistance on the surface of the substrate to the minimum.例文帳に追加

基板上の部位毎に異なった条件で詳細なめっきを行うことができ、しかも、基板表面のシート抵抗の影響を最小限に抑えて面内均一性の良好なめっき膜を得ることができるようにする。 - 特許庁

This method for forming the plated film comprises the steps of: forming the surface plating layer mainly formed of Sn by using a plating solution which includes Sn ions and a compound containing an additive that is consumed during electrolysis; and heat-treating the surface plating layer at 230 to 350°C.例文帳に追加

表層めっき層として、Ｓｎイオン、および電解消費型添加剤を有する化合物を含むめっき液を用いて、Ｓｎを主成分とするめっき層を形成し、２３０〜３５０℃の温度にて熱処理を行う。 - 特許庁

To provide a plating method by which a uniform plating film is formed on numerous objects to be plated at the same time with high production efficiency without causing plating defect or the like.例文帳に追加

めっき不良などを生じることなく、一度に多量の被めっき物に対して均一なめっき膜を形成することができ、しかも生産効率に優れためっき方法を提供すること。 - 特許庁

A chip mounting section 17 formed by a plated film for mounting the LED chip 30 is formed on the front side of a second insulation substrate 11 stacked on the back side of the first insulation substrate 3.例文帳に追加

第１の絶縁基板３の裏面に積層された第２の絶縁基板１１の表面には、ＬＥＤチップ３０を搭載するめっき膜によって形成されたチップ搭載部１７が設けられている。 - 特許庁

In a method of improving solder wettability of circuit board, the surface of a plated-Ni film formed on a metallic circuit is cleaned with electrolytic water of ≥10 in pH, ≤-800 mV in equilibrium potential, and ≥10.0 mS/m in electrical conductivity.例文帳に追加

ｐＨ１０以上、酸化還元電位−８００ｍＶ以下、電気伝導度１０．０ｍＳ／ｍ以上の電解水で、金属回路に施されたＮｉめっき膜面を洗浄することを特徴とする回路基板の半田濡れ性向上方法。 - 特許庁

To provide a surface-treated steel sheet which is suitable to an Al-Zn-based alloy plated steel sheet used under non-coating in the use for building materials and the field of household electric appliances, mainly used in the outdoor environment, and contains no chromium in a film.例文帳に追加

建材や家電分野の用途、主として屋外環境において無塗装で用いられるＡｌ−Ｚｎ系合金めっき鋼板に好適で且つ皮膜中にクロムを含まない表面処理鋼板を提供する。 - 特許庁

Regarding the inkjet recording head, after the high-pressure fluid is removed, a plated film 423 is formed on the inner wall 422 of the ink channel 490 by the mixed fluid 317 obtained by mixing and stirring a second high-pressure fluid and a plating liquid.例文帳に追加

インクジェット記録ヘッドの場合、高圧流体を除去した後、さらに、第２の高圧流体とめっき液とを混合して攪拌した混合流体３１７により、インク流路４９０の内壁４２２にめっき膜４２３を形成する。 - 特許庁

To stably manufacture a hot-dip Al-Zn alloy plated steel strip which is provided with a plating film containing Al of 20-95 mass%, has superior elongation characteristics, and moreover shows an attractive appearance.例文帳に追加

めっき皮膜中のＡｌ含有量が２０〜９５mass％である溶融Ａｌ−Ｚｎ系めっき鋼板であって、伸び特性が優れしかも美麗なめっき表面外観を有するめっき鋼板を安定して製造する。 - 特許庁

To provide a holder used for electroplating electronic parts requiring high plating precision, which keeps an article to be plated into an energized condition and makes a dense and uniform film formed thereon.例文帳に追加

高いめっき精度が求められる電子部品などに電気めっきを施す場合において、被めっき物への通電状態を維持し、緻密で均一な被膜を形成することが可能な電気めっき治具を提供すること。 - 特許庁

To provide a copper-zinc alloy electroplating bath in which a cyan compound is not contained and from which a plated film having excellent corrosion resistance is formed, and to provide a wire for a steel cord.例文帳に追加

シアン化合物を含むことなく、耐腐食性の良好なめっき被膜の得られる銅−亜鉛合金電気めっき浴およびスチールコード用ワイヤを提供する。 - 特許庁

To facilitate the electroplating at a constant electrolytic current density, and to reduce the dispersion in the thickness of a deposited film of a plating metal even when the area of individual works to be plated is scattered.例文帳に追加

常に一定の電解電流密度での電解めっきを容易に可能とし、個体間の被めっき対象部の面積にバラツキがあっても、めっき金属の析出膜厚のバラツキを低減させる。 - 特許庁

To provide a plating pretreatment method capable of obtaining high reliability on the adhesiveness of the plating pattern, and a manufacturing method of a pattern-plated film.例文帳に追加

めっきパターンの密着性に関して高い信頼性を得ることができるめっき前処理方法およびパターンめっきされたフィルムの製造方法を提供する。 - 特許庁

To facilitate plating by adopting a face-up system which easily removes generated hydrogen during plating from a surface to be plated, and furthermore form a more uniform plating film on the surface of a material to be treated.例文帳に追加

めっき時に発生する水素を容易に被めっき面から離脱させて、めっきが容易はフェースアップ方式を採用し、しかも被処理材の被めっき面により均一なめっき膜を容易に形成できるようにする。 - 特許庁

The metal to be plated of the lead member 5 is formed of nickel, and the sacrifice electrode is formed of zinc and tin, and a gold plating film 9 controlled to a desired thickness by immersing the lead member and the sacrifice electrode in gilding liquid is free from any pin hole, and excellent in adhesivity.例文帳に追加

ここでリード部材５の被めっき金属素材にニッケル、犠牲電極に亜鉛および錫が利用され金めっき液に浸漬して所望厚さに制御された金めっき膜９を無ピンホールで密着性良好なめっきを得る。 - 特許庁

The chip capacitors 20 is electrically connected to first the second electrodes 21 and 22 coated with a copper plating film 29 through via holes 46 plated with copper.例文帳に追加

チップコンデンサ２０は、銅めっき膜２９を被覆した第１、第２電極２１，２２に銅めっきによりなるバイアホール４６で電気的接続を取ってある。 - 特許庁

To obtain excellent processability and processed part corrosion resistance in a coated steel panel using a molten Al-Zn type plated steel panel, which has a plating film with an Al content of 20-95 mass %, as a substrate steel panel.例文帳に追加

めっき皮膜中のＡｌ含有量が２０〜９５ｍａｓｓ％の溶融Ａｌ−Ｚｎ系めっき鋼板を下地鋼板とする塗装鋼板において、優れた加工性と加工部耐食性を得る。 - 特許庁

To provide a plating apparatus which employs the dipping method in which air bubbles can escape relatively easily, and is capable of automatically forming a plated metal film suitable for protruding electrodes such as bumps, and which does not occupy a large space.例文帳に追加

気泡の抜けが比較的よいディップ方式を採用し、広い占有面積を占めることなく、バンプ等の突起状電極に適した金属めっき膜を自動的に形成できるようにする。 - 特許庁

To impart appearance and corrosion resistance equivalent to those obtained through chromate conversion treatment to a zinc-based member to be plated, by using a reactive chromium-free chemical conversion treatment which can uniformly form a rust preventive film even on a member having a complicated shape.例文帳に追加

複雑形状の部材にも均一に防錆皮膜を形成できる反応型のノンクロム化成処理により、亜鉛系めっき部材に対して、クロメート処理に匹敵するような外観と耐食性を付与する。 - 特許庁