母材の強度、低温靱性および変形能が優れ、かつ現地溶接が容易な引張強さ９００ＭＰａ以上（ＡＰＩ規格Ｘ１２０以上）の超高強度ラインパイプ用鋼板および鋼管の製造方法を提供する。例文帳に追加

To provide a method for manufacturing a steel sheet and a steel pipe of which the base metal has superior strength, low-temperature toughness and deformability, for an ultrahigh-strength line pipe that can be easily welded on the actual place and has a tensile strength of 900 MPa or higher (X120 or higher in the API standards). - 特許庁

電磁鋼板の加工端部に超音波衝撃処理の後、電解研磨もしくは化学研磨方法でエッチングを行い、電磁鋼板の加工端部の疲労強度および磁気特性の両方を向上させた加工部を安定して得る。例文帳に追加

To stably provide a worked portion having both enhanced fatigue strength and magnetic characteristics in a worked end part of an electromagnetic steel sheet, by subjecting an end part to be worked of the electromagnetic steel sheet to ultrasonic impact treatment, and then etching the end part with an electrolytic grinding method or a chemical polishing method. - 特許庁

超極厚（例えば、厚さ５０ｍｍ超）の鋼板又は鋼管を、高エネルギー密度ビーム溶接で溶接する際、（ｉ）溶接部に引張応力が残留しない施工条件を見いだし、（ii）ギガサイクル域の振動環境に、長期間耐える疲労特性有し、かつ、十分な破壊靱性を有する高エネルギー密度ビーム溶接継手を提供する。例文帳に追加

To provide a joint welded by high energy density beam, which (i) obtains execution conditions of no tensile stress remaining in a weld zone and which (ii) has fatigue resistance for enduring vibration environment of gigacycle range for a long period as well as having sufficient fracture toughness, in welding a super thick (e.g., thickness in excess of 50 mm) steel plate or steel pipe by high energy density beam welding. - 特許庁

鋼鋳片の試料断面を研磨した後で、試料断面を腐食させる鋼の凝固組織検出装置であって、マイクロバブルを含む水７を収容する外槽２と、水７に３０ｋＨｚ〜３ＭＨｚの超音波を印加し水共振させる超音波発振装置５、６と、外槽２内に浸漬させるとともに試料断面を腐食させる腐食液８を収容する内槽３とからなる。例文帳に追加

The device for detecting the solidified structure of steel in which after polishing a sample section of a steel cast slab, the sample section is corroded includes an outer tank 2 containing water 7 containing micro-bubbles, ultrasonic oscillators 5, 6 resonating the water by application of ultrasonic waves of 30 kHz-3 MHz to the water 7, and an inner tank 3 immersed in the outer tank 2 and containing a corrosive liquid 8 corroding the sample section. - 特許庁

鋼管の外面にレーザを照射し、発生した超音波が鋼管内面と外面との間の肉厚内で反射、往復する多数のエコーを検出し、前記肉厚内で進行するエコーの進行時間及び反射角を定め、それらの値と超音波の伝播速度とから肉厚を計算する肉厚測定方法を改良した。例文帳に追加

The method is improved where the laser is radiated to an outer surface of a steel pipe, many echoes of the generated ultrasonic wave reflecting and reciprocating in the wall thickness between the inner surface and outer surface of the steel pipe are detected, the progress times and reflection angles of the echo travelling in the wall thickness are determined, and the wall thickness is calculated based on these values and propagation speed of the ultrasonic wave. - 特許庁

プレス成形性を向上させることにより超高張力鋼板の使用を可能にして、超高張力鋼板を使用することによる車両重量の軽量化及び車体の高強度／高剛性を達成すると共に、部品点数の削減による組立て工数の低減及び組立て精度の向上並びに容易化を図った自動車車体の骨格部材を提供する。例文帳に追加

To provide a skeleton member of automobile body which can use a high tensile steel sheet by improving press formability of the member, consequently attains reduction in vehicle weight and the high strength/high rigidity of the automobile body, and which attains reduction in assembling man-hour and improvement in assembly accuracy and facilitation of the assembly by reducing the number of components. - 特許庁

これらの鋼帯は、連続鋳造スラブの表面手入れ後、スラブ表面温度が１２００〜１２７０℃の範囲内になるように加熱して熱間圧延する際、粗圧延後の仕上げ圧延中の９５０℃を超える鋼帯表面にスプレー水をかけ、その後７８０℃を超える温度で巻取ることで確実に製造できる。例文帳に追加

The steel strips can be surely manufactured by applying spray water to the steel strip surfaces exceeding 950°C during finish rolling after rough rolling in hot rolling a continuously cast slab by heating the slab in such a manner that the slab surface temperature is held within the range from 1,200 to 1,270°C after conditioning of the slab and thereafter by coiling the steel strip at a temperature exceeding 780°C. - 特許庁

成分組成として、B:50〜150ppm、N:70〜200ppm、下記（１）式による固溶B：3〜50ppmを含有し、好ましくはC:0.01〜1.2mass%、Si: 0.10超え1.5mass%以下、Mn: 0.3〜2.0mass%、S:0.015超え0.2mass%以下、Al:0.01〜0.1mass% 、更に、Ｎｉ、Ｃｒ、Ｍｏ、Ｐｂ、Ｃａ、Ｓｅ、Ｔｅ、Ｂｉ、Ｓｎ、Ｃｕ、Ｚｒ、Ｍｇ、Ｎｂ、Ｖ、Ｔｉの一種または二種以上の鋼で、鋼中介在物として、1ｍｍ^２あたりに、円相当径で10μｍ以上のBN介在物50個以上と円相当径で3μｍ以下の微細硫化物500個以上を共に有する。例文帳に追加

This free-cutting steel has a composition comprising 50-150 ppm B, 70-200 ppm N, 3-50 ppm solution B which is determined by the expression (1), solution B=B-(N/1.7), - 特許庁

これにより、高温超伝導材料の蒸着基板として望ましい結晶配向性を有するオーステナイト系ステンレス鋼箔を製造することが可能になり、高温超伝導材料の製造コストを大幅に低減することが可能になる。例文帳に追加

Thus, an austenitic stainless steel foil having crystal orientation properties preferable for a vapor deposition substrate of a high-temperature superconducting material is produced, while greatly reducing the production cost of the material. - 特許庁

また、刃部２ｂのみをセラミック又はサーメット又は超硬合金で構成し、シャンク１は安価な鋼材で構成できることから、例えば、上記切削工具の全体をセラミック又はサーメット又は超硬合金で一体的に形成する場合に比して、切削工具をより安価に提供できる。例文帳に追加

Since the shank 1 can be constituted of an inexpensive steel material by constituting only a blade part 2b of ceramics or cermet or cemented carbide, for example, the cutting tool can be further inexpensively provided more than when integrally forming the whole cutting tool of ceramics or cermet or cemented carbide. - 特許庁

引張強さが ５７０ ＭＰａ以上の高強度鋼に対して、溶接入熱が ６００ ｋＪ／ｃｍを超える超大入熱溶接を施した場合であっても、母材は勿論のこと溶接熱影響部について、優れた靱性を安定して得る。例文帳に追加

To stably obtain excellent toughness not only in a base material but also in a weld heat affected zone even when ultrahigh heat input welding in which welding heat input exceeds 600kJ/cm is performed to high strength steel having a tensile strength of ≥570MPa. - 特許庁

該ロールは軸部材（鋼製軸心１）とその外側のスリーブ部材とを有し、該スリーブ部材が複数個の超硬合金成形体部材をロール軸方向に接合・一体化して形成されたもの（超硬合金接合スリーブ２）であることが好ましい。例文帳に追加

The roll has a shaft member (steel-made shaft center 1) with its outside sleeve member, and it is preferable that the sleeve is formed by joining/integrating a plurality of cemented carbide formed members in the roll axis direction (cemented carbide joining sleeve 2). - 特許庁

0.1-0.5質量%の炭素と、0.1-0.4質量%ケイ素と、0質量%を超え、かつ0.9質量%以下のマンガンと、0質量%を超え、かつ0.2質量%以下のクロムとを含有し、かつ残部が鉄および不可避不純物である鋼材から得られる素形材１３に浸炭窒化処理、高周波焼入れ処理、焼もどし処理及び研磨加工を施す。例文帳に追加

Carbonitriding processing, induction hardening processing, tempering processing and polishing processing are applied to a raw section 13 provided from a steel material including carbon of 0.1-0.5 mass%, silicon of 0.1-0.4 mass%, manganese of 0 mass%-0.9 mass% and chrome of 0 mass%-0.2 mass% and having a residual part of iron and an unavoidable impurity. - 特許庁

清浄鋼等の硬化でかつ確保も難しい材料を用いることなく、内面の非金属介在物を排除し、内圧疲労強度の極めて優れた、燃料噴射圧力が１８００気圧を超える超高圧燃料配管とその製造方法。例文帳に追加

To provide ultra high pressure fuel piping which eliminates non-metallic inclusions on an inner surface without the usage of an expensive material such as clean steel difficult to be secured, is excellent in inner pressure fatigue strength, and has a fuel injection pressure larger than 1,800 atm, and also to provide its manufacturing method. - 特許庁

流体が流れる管路と、この管路に沿って設置される複数の超音波トランスジューサとを備えた流量計において、ステンレス鋼や硝子などの硬質の素材で構成される管壁を介して伝搬する超音波を減衰させることにより、受信信号のＳＮと測定精度の向上を図る。例文帳に追加

To improve the SN of received signals and the measuring accuracy of a flow-meter provided with a pipeline in which a fluid flows and a plurality of ultrasonic transducers disposed along the pipeline, by attenuating ultrasonic waves propagating along a pipe wall made of a hard material such as stainless steel or glass. - 特許庁

プレストレストコンクリート構造の橋梁１において、超高強度モルタルとＰＣ鋼材とからなり、桁高に対するスパンの比が、３５超の低桁高の中央桁１０及び端部桁２０からなる橋梁１を提供する。例文帳に追加

In the bridge 1 having the prestressed-concrete structure, the bridge 1 composed of ultra-high strength mortar and a PC steel material and composed of central girders 10 having the low girder height at the ratio of a span to a girder height of 35 or more and end girders 20 is provided. - 特許庁

該ロールは軸部材（鋼製軸心１）とその外側のスリーブ部材とを有し、該スリーブ部材が複数個の超硬合金成形体部材をロール軸方向に接合・一体化して形成されたもの（超硬合金接合スリーブ２）であることが好ましい。例文帳に追加

The roll has a shaft member (steel shaft center 1) and a sleeve member on the outside of the shaft member and it is preferable that the sleeve member is what is formed by joining and integrating the plural pieces of the compact member of the cemented carbide in the axial direction of the roll (joined sleeve 2 of the cemented carbide). - 特許庁

この金属材料の疲労測定方法では、浸炭窒化焼き入れによって表面硬化した軸受鋼からなる内輪１０の軌道面１０Ａに超音波を伝播させ、この超音波の伝播速度に基いて、内輪１０の疲労を非破壊で測定できる。例文帳に追加

According to this fatigue measuring method of metal material, an ultrasonic wave is propagated to the raceway surface 10A of an inner ring 10 made of a bearing steel surface-hardened by carbonitriding and hardening, whereby the fatigue of the inner ring 10 can be non-destructively measured on the basis of the propagation speed of the ultrasonic wave. - 特許庁

ティースビット１は、耐摩耗性に優れた超硬材チップ４を先端に備えた状態で、台金となる鋳造用金属５（例えば、鋳鋼）を鋳込むことによって形成されており、超硬材チップ４の鋳造用金属５との接触面には凸部６が設けられている。例文帳に追加

A teeth bit 1 is formed by casting casting metal 5 (for example, casting steel) being base metal in a state of having on the tip a cemented carbide material tip 4 excellent in abrasion resistance, and a projecting part 6 is arranged on a contact surface with the casting metal 5 of the cemented carbide material tip 4. - 特許庁

直径０.０４〜０.１４ｍｍの多数本の超極細鋼素線を撚線してタイヤのカーカスに使用できるようにしたタイヤカーカス補強用超極細線スチールコード及びこれを適用した乗用車用ラジアルタイヤを提供する。例文帳に追加

To provide a tire carcass-reinforcing ultrafine wire steel cord capable of being used for a carcass of a tire, by together twining many strands of ultrafine steel element wires each having a diameter of 0.04-0.14 mm, and to provide a passenger car radial tire to which the same is applied. - 特許庁

蒸気タービン車室にある鋳鋼物内部の亀裂１０２を探傷するため、蒸気タービン車室の外表面等に超音波センサ１０４を設置し、保温層の凹部において熱的に結合した熱伝導体１０５および熱電素子１０６を用いて超音波センサ１０４を冷却する。例文帳に追加

The ultrasonic sensor 104 is installed on the outer surface or the like of a steam turbine wheel chamber in order to detect cracks 102 in the cast steel article present in the steam turbine wheel chamber and cooled using a heat conductor 105 and a thermocouple element 106 both of which are thermally connected in the recess of a heat insulating layer. - 特許庁

電磁超音波センサー２は、２軸ステージ５の上に設置されている光学定盤６に固定されており、２軸ステージ５の動きにより、鋼管３に超音波受信面が接触するか任意のリフトオフで接近することができるようになっている。例文帳に追加

The electromagnetic ultrasonic sensor 2 is fixed to the optical surface plate 6 arranged on a two-axis stage 5, and an ultrasonic receiving surface can be brought into contact with a steel pipe 3 or allowed to approach the steel pipe 3 with an arbitrary lift-off by the movement of the two-axis stage 5. - 特許庁

アルミニウム系材と鋼材の積層体に超音波振動を印加して接合を行うための超音波接合用チップとして、振動方向と直交する方向に湾曲した凸形状となる曲面を有するＲ型電極にしたチップを用いる。例文帳に追加

As the ultrasonic welding tip for performing welding by applying ultrasonic vibration to a stacked body of the aluminum-based material and the steel material, a tip in a form of R type electrode is used having a curved face that forms a projected shape curved in the direction orthogonal to the vibrating direction. - 特許庁

ドリル径Ｄが１０ｍｍ以下の超硬合金製あるいは超硬合金をコーティングした細径ドリルを用いて、深さ１０Ｄ以上の深穴を加工する際のバリ形成を抑制することができ、高い寸法精度が要求される機械構造部品の素材として好適な鋼材の提供。例文帳に追加

To provide steel by which the formation of burrs, occurring in the case where a deep hole with a depth of ≥10 D is bored using a small-diameter drill of ≤10 mm drill diameter D made of cemented carbide or coated with cemented carbide, can be suppressed and which can be suitably used as a material for machine structural parts requiring high dimensional accuracy. - 特許庁

超音波圧接後の接合部の表層部に大きな変形を生じることなく、凝着（スティッキング）がなく、連続接合により健全且つ信頼性のある強固な接合部を得ることを可能とし、とくにアルミニウム板と鋼板との接合に好適な超音波圧接方法を提供する。例文帳に追加

To provide an ultrasonic pressure welding method by which remarkable deformation is not caused in the surface layer part of a joint after ultrasonic pressure welding, and the sound, reliable and firm joint can be obtained by continuous joining without causing sticking, and which is particularly suitable for the joining between an aluminum sheet and a steel sheet. - 特許庁

冷凍機冷却型超電導磁石装置における超電導コイル８のコイル冷却ステージ７および熱シールド板を、銅、アルミニウム等の高熱伝導率部材と、ステンレス鋼、ＦＲＰ、チタン等の剛性部材の複合材料から構成したこと。例文帳に追加

A coil-cooling stage 7 and a heat shield plate of a superconducting coil 8 in refrigerator cooled superconducting magnet are composed of composite material of a high thermal conductivity material, such as copper and aluminum and a rigid material, such as stainless steel, FRP and titanium. - 特許庁

ロールの外層を耐摩耗性に優れた超硬合金で形成するとともに、中間層と鉄系あるいは鋼系材料からなる内層の接合境界部を強化し、強度的に信頼性の高い超硬合金製圧延用複合ロールを提供する。例文帳に追加

To provide a composite rolling roll made of cemented carbide, which composite rolling roll has an outer layer made of cemented carbide having excellent wear resistance, and has a reinforced joining boundary portion between an intermediate layer and an inner layer composed of iron or steel material, and has reliable strength. - 特許庁

インボリュート歯形歯車の歯面仕上げ用丸形シェービングカッタ４において、本発明では、歯部８及び本体９を同一種超硬材で構成し、かつ一体構造化することにより、シェービングカッタ４全体を高速度工具鋼製から超硬材製に置き換えたものである。例文帳に追加

This round shaving cutter 4 for tooth flank finishing of the involute toothed gear is constituted by manufacturing the whole of the shaving cutter 4 itself of a super hard material instead of high speed tool steel by constituting a tooth part 8 and a main body 9 of the same super hard material and integrally structuring them. - 特許庁

鋼系材料からなる内層の外周に、ＷＣ系超硬合金からなる外層を金属接合した超硬合金製圧延用複合ロールであって、該内層が材種の異なる複数個の内層部分材を互いに略同心円状に金属接合して構成されることを特徴とする。例文帳に追加

In the sintered hard alloy-made combined roll for rolling in which an outer layer consisting of a WC-based sintered hard alloy is metal-joined with an outer circumference of the inner layer consisting of a ferrous material, the inner layer is constituted by metal-joining a plurality of inner layer components of different materials alternately with each other in a substantially concentric shape. - 特許庁

該ロールは軸部材（鋼製軸心１）とその外側のスリーブ部材とを有し、該スリーブ部材が複数個の超硬合金成形体部材をロール軸方向に接合・一体化して形成されたもの（超硬合金接合スリーブ２）であることが好ましい。例文帳に追加

The roll has a shaft member (steel shaft center 1) and a sleeve member on the outside of the shaft member and it is preferable that the sleeve member is what is formed by joining and integrating the plural pieces of the compact member of the cemented carbide (joined sleeve 2 of the cemented carbide). - 特許庁

高架構造物等の鋼床版に使用されるデッキ下面に超音波探触子を当てて、このデッキ下面とトラフリブとの溶接箇所からデッキ内へと進展する亀裂を探傷する超音波探傷において、亀裂により発生するエコーを精度良く検出し、かつ検査作業を容易化する。例文帳に追加

To precisely detect the echo produced by a crack to facilitate inspection work in ultrasonic flaw detection for detecting the crack developed into the deck, which is used in the steel floor panel of a high-level structure, or the like, from the welded place of the undersurface of the deck and a trough rib by applying an ultrasonic probe to the undersurface of the deck. - 特許庁

板厚が５０ｍｍを超える場合においても高強度（引張強度：５１０〜７００ＭＰａ）を満足し、且つ−１０℃におけるＫｃａ値で７０００ＭＰａ・ｍｍ^1/2を超える様な脆性亀裂伝播停止特性に優れた構造用厚鋼板を提供する。例文帳に追加

To provide a thick steel plate for a structure, which satisfies high strength (tensile strength: 510-700 MPa) and has such superior brittle fracture propagation stopping properties as to exceed 7,000 MPa*mm^1/2 by a Kca value at -10°C, even if the plate thickness is more than 50 mm. - 特許庁

本発明の超硬合金製複合ロールは、鋼系または鉄系材料からなる内層の外周に超硬合金からなる外層が金属接合してなり、外層がロール軸方向で少なくとも２種類以上の異なる材質からなることを特徴とする。例文帳に追加

This composite roll made of the sintered hard alloy in which the outer layer consisting of the sintered hard alloy is metallically joined on the outer peripheral surface of the inner layer consisting of steel or iron base material and the outer layer consists of at least two or more of different materials in the axial direction. - 特許庁

セラミックス被覆鋼の製造方法は、窒化チタンアルミニウム又は窒化クロムの薄膜を鋼基材上に成膜する成膜工程１１と、成膜された鋼基材を少なくとも７６０℃を超える高温、より好ましくは７６０℃〜１０６０℃で加熱処理する加熱処理工程と、を有することを特徴とする。例文帳に追加

The method for producing a ceramics coating steel comprises: a film deposition stage 11 where a thin film of titanium aluminum nitride or chromium nitride is deposited on a steel base material; and a heating treatment stage where the film-deposited steel base material is subjected to heating treatment at a high temperature at least exceeding 760°C, more preferably, at 760 to 1,060°C. - 特許庁

レーザ・アークハイブリッド溶接により溶接される、主たる組織がマルテンサイトである引張強さが１１００ＭＰａ以上の超高張力鋼板において、鋼板、継手の良好な靭性を確保し、かつ、溶接熱影響部の軟化を抑制して、継手の引張強さも合わせて１１００ＭＰａ以上を確保できる高張力鋼板の製造方法を提供することを課題とする。例文帳に追加

To provide a method for manufacturing a high-tensile steel plate for ensuring excellent toughness of the steel plate and a joint, suppressing softening of a welded heat affected zone, and also ensuring the tensile strength of the joint of ≥1,100 MPa, in the super-high-tensile steel plate which is welded by the laser beam arc hybrid welding and whose main structure is martensite and which has tensile strength of ≥1,100 MPa. - 特許庁

超硬鋼、ステンレス鋼、工具鋼、セラミックのいずれか１つを材料とする刃物本体２に刃先３を形成してなるパン、菓子類のスライサー用刃物、野菜類のカット用刃物、乾物類のカット用刃物等の食品用刃物１において、刃物本体２の少なくとも刃先３の表面にカーボン硬質被膜８を形成した。例文帳に追加

A food cutter 1 including a slicing cutter for bread and confectionery, a cutting knife for vegetables and a cutting knife for dried goods, which has a cutting edge 3 formed on a cutter mainbody 2 of either hard steel, stainless steel, tool steel or ceramic, comprises a carbon hard coating formed on the surface of at least the cutting edge 3 of the cutter mainbody 2. - 特許庁

垂直部を有する曲げ型連続鋳造機を用いてタンディッシュ内の溶鋼を浸漬ノズルを介して鋳型に注湯する垂直曲げ連鋳機を用いたステンレス溶鋼の鋳造方法において、浸漬ノズルの吐出口の深さをメニスカスから３００ｍｍ超に浸漬し、且つ、鋳型に注湯した溶鋼を電磁攪拌する。例文帳に追加

In the method for casting the molten stainless steel by using the vertical-bending type continuous caster, pouring the molten steel in a tundish into a mold through an immersion nozzle, the depth of a spouting part in the immersion nozzle is dipped into > 300 mm from a meniscus and the molten steel poured into the mold is electromagnetically stirred. - 特許庁

上下フランジとウエブとを有する形鋼において、少なくとも上下フランジは、圧延方向のヤング率が２１５ＧＰａ超２９０ＧＰａ以下である高ヤング率鋼板で構成され、この高ヤング率鋼板を、その圧延方向が上下フランジの長手方向となるようにウエブに固着させている。例文帳に追加

In the shape steel comprising upper and lower flanges and a web, at least the upper and lower flanges are composed of high Young's modulus steel sheets whose Young's modulus in the rolling direction is >215 to 290 GPa, and the high Young's modulus steel sheets are fixed to the web in such a manner that the rolling direction thereof comes to the longitudinal direction of the upper and lower flanges. - 特許庁

（Ａ）鋼材の表面に塩分を付着させる工程 （Ｂ）鋼材に対して、乾燥工程及び湿潤工程を繰り返すことを１サイクルとし、乾燥工程の相対湿度＝４０％超７０％以下、湿潤工程の相対湿度＝８０％以上、湿潤率＝９５％以上１００％以下で行われることとし、このサイクルを少なくとも１回行う工程 （Ｃ）鋼材の表面を、洗浄水により洗浄する工程例文帳に追加

In the method, each process of the above (A), (B) and (C) will be performed once or more. - 特許庁

C：0.08〜0.016％の中炭素鋼を、鋳型厚さが240mmを超え、鋳型長さが1.1m以下の連続鋳造機により鋳造するに際し、塩基度が1.2〜2.5で、凝固温度が1200〜1280℃のモールドフラックスを使用し、浸漬ノズルの吐出孔よりも下方に設置された磁場印加装置を用いて磁場強度が0.15Ｔ以上の静磁場を鋳型内溶鋼に印加し、鋳造速度を1.3〜2.0m/minとして、下記式により表される不均一凝固指数(A)が0.7未満となるように鋳造する中炭素鋼の連続鋳造方法である。例文帳に追加

The continuous casting method for the medium-carbon steel is characterized in that, when the medium-carbon steel containing 0.08-0.16% - 特許庁

０．２質量％を超えるＣを含むマルテンサイト系ステンレス鋼からなる鋳造素材を所定の形状に精密鋳造成形し、該鋳造素材に対して熱間静水圧プレス処理を施しつつソーキング処理を施すことにより、マルテンサイト系ステンレス鋳鋼部品を形成するマルテンサイト系ステンレス鋳鋼部品の製造方法である。例文帳に追加

The method of manufacturing the steel casting parts made of martensitic stainless steel is provided, by which the cast material composed of the martensitic stainless steel containing 0.2 mass% C or higher is molded into the prescribed shape by the precision casting and a soaking treatment is applied to the cast material while applying a hot isostatic pressing treatment thereto, thereby obtaining the steel casting parts made of martensitic stainless steel. - 特許庁

高速度工具鋼、高クロム合金工具鋼等の工具鋼および超硬合金のいずれかを刃物母材とする木材切削用刃物は、逃げ面および掬い面のいずれか一面または両面に金属成分のみの原子％が、Ａｌが１０％以上８０％以下であり、残りＣｒで構成される窒化物または炭窒化物の被膜を有する。例文帳に追加

The wood cutting cutter using tool steel such as high-speed tool steel or high chromium alloy tool steel or an ultra-hard alloy as a cutter matrix material has a coat of a nitride composed of 10-80% of aluminum in an atomic percentage of only a metal component and residual Cr on at least one surface of a flank and a rake surface. - 特許庁

ワークの少なくとも一部に鋼球を投射してショットピーニングを行うにあたり、鋼球が移動する閉鎖空間を包囲する部材の一部をワークにより構成し、上記閉鎖空間内で超音波振動によって鋼球を連続的に移動させ、ワークの少なくとも一部に−３００ＭＰａ以上の圧縮残留応力を付与する。例文帳に追加

A part of a member to surround a closed space in which a steel ball moves is constituted of a workpiece in shot peening by projecting the steel ball to at least a part of the workpiece, and compression residual stress of more than -300 MPa is given to at least a part of the workpiece by continuously moving the steel ball by supersonic wave vibration in the closed space. - 特許庁

粗加工工程に板厚プレス装置を備えた熱間圧延設備による熱延鋼帯の製造方法において、熱間スラブの板厚プレス加工を行う際に長手方向に均一な歪を加えることにより熱延鋼帯の材質や超微細組織を有する高張力熱延鋼帯の組織を長手方向に均一にする。例文帳に追加

To make the material of a hot-rolled steel strip and the structure of a hot-rolled high-tensile steel strip having hyperfine structure uniform in the longitudinal direction by adding uniform strain in the longitudinal direction when performing the thickness press working of a hot slab in a manufacturing method of the hot-rolled steel strip with hot rolling equipment provided with a thickness press device in a roughing stage. - 特許庁

また、内部の欠陥を検出すべき鋼材Ｗを回転可能に支持する複数組のローラＲと、上記鋼材Ｗの表面に水膜を介して配置される上記ギャップ法用のアレイ探触子２と、上記鋼材Ｗの表面に水室（１４）を介して配置される局部水浸法用のアレイ探触子１０と、を含む、超音波探傷装置１も含まれる。例文帳に追加

The ultrasonic flaw detection method includes also the ultrasonic flaw detector including a plurality of sets of rollers R for supporting the steel material W to detect the internal defect, the array probes 2 for the gap method arranged on a surface of the steel material W via a water film, and the the array probes 10 for the local submerging method arranged on the surface of the steel material W via a water chamber 14. - 特許庁