「Sintering」に関連した英語例文の一覧と使い方(97ページ目) - Weblio英語例文検索

To provide an economical production technology of boron carbide sintered body which can fire even a dense boron carbide sintered product of complicated shape at normal pressure without pressurizing, not necessitating much addition of sintering aid in the raw materials nor necessitating special additives and special treatments, without deteriorating extremely excellent mechanical properties originally possessed by the boron carbide sintered body.例文帳に追加

炭化ホウ素焼結体が本来有する極めて優れた機械的特性を損なうことなく、複雑な形状の緻密質炭化ホウ素焼結体製品をも、原料中への多量の焼成助剤の添加や、特殊な添加物や特殊な処理を必要とすることなく、しかも、加圧せずに常圧で焼成できる経済的な製造技術の提供。 - 特許庁

To provide a graphite tray used for sintering a product of cemented carbides or cermets, each having a thermally sprayed coating of an oxide on its surface, which is almost free from oxidation phenomenon at the interface between the coating and its surface even when the coating is prevented from becoming oxygen defect type and which thereby improves the durability of the coating.例文帳に追加

酸化物の溶射皮膜を表面に有する、超硬合金またはサーメット類製品の焼結に用いるグラファイトトレーであって、被膜が酸素欠損型になるのを防止した場合においても、被膜とグラファイトとの境界面において酸化現象が起こりにくく、その結果、被膜の耐久性を向上させることができる、焼結用グラファイトトレーを提供する。 - 特許庁

To provide a method and apparatus for measuring moisture content that can always accurately measure moisture content by quickly correcting the relation between the absorbance and the moisture content even when the composition of materials is changed in the measurement of the moisture content of a sintering material that measures the moisture content by using infrared absorption by water.例文帳に追加

赤外線の水による吸収を利用して含有水分を測定する焼結原料の水分測定において、原料配合が変更になっても速やかに吸光度と含有水分量との関係を修正し、常に正確に含有水分量の測定を行うことのできる水分測定方法及び水分測定装置を提供する。 - 特許庁

Green sheets 20 for restraint are made moderately softer than green sheets 11a, 11b, 11c (green substrate 19) of a low temperature sintering ceramic by using an acrylic resin as the binder of the green sheets 20 and a butyral resin as the binder of the green sheets 11a, 11b, 11c.例文帳に追加

拘束用グリーンシート２０のバインダーとしてアクリル樹脂を用い、低温焼成セラミックのグリーンシート１１ａ，１１ｂ，１１ｃ（生基板１９）のバインダーとしてブチラール樹脂を用いることで、拘束用グリーンシート２０を低温焼成セラミックのグリーンシート１１ａ，１１ｂ，１１ｃ（生基板１９）よりも適度に柔らかくする。 - 特許庁

It is possible to manufacture the metal glass separator having excellent corrosion resistance and durability simply and in a short time by containing a metal glass powder 10 in a die 30, and sintering it while pressurizing by a punch 40 which is provided with grooved irregularities, and energizing it via the punch 40.例文帳に追加

ダイ３０内に金属ガラス粉末１０を入れ、金属ガラス粉末１０を溝形状の凹凸が設けられたパンチ４０で加圧しながらパンチ４０を通して金属ガラス粉末１０に通電して焼結させることで、耐食性及び耐久性に優れた金属ガラスセパレータを、簡便に、且つ、短時間で製造することができる。 - 特許庁

The method for producing the wustite bulk material includes a step of obtaining a powder mixture by mixing Fe powder and Fe_3O_4 powder, a step of obtaining a molded article by molding the powder mixture, a step of obtaining a wustite sintered compact by sintering the molded article, and a step of obtaining the wustite bulk material by hot pressing the wustite sintered compact.例文帳に追加

Ｆｅ粉末とＦｅ_3Ｏ_4粉末とを混合して混合粉末を得る工程、前記混合粉末を成型して成型体を得る工程、前記成型体を焼結してウスタイト焼結体を得る工程、前記ウスタイト焼結体をホットプレスしてウスタイトバルク材を得る工程を含むことを特徴とするウスタイトバルク材の製造方法。 - 特許庁

A sintered cubic boron nitride (cBN) compact for use in a tool is obtained by sintering a mixture of: (i) cubic boron nitride; (ii) aluminum oxide; (iii) one or more high melting point metal compounds; and (iv) aluminum and/or one or more non-oxide aluminum compounds.例文帳に追加

工具に使用するための立方晶窒化ホウ素（ｃｕｂｉｃ ｂｏｒｏｎ ｎｉｔｒｉｄｅ、略称ｃＢＮ）焼結体が、（ｉ）立方晶窒化ホウ素と、（ｉｉ）酸化アルミニウムと、（ｉｉｉ）１若しくはそれ以上の高融点金属化合物と、（ｉｖ）アルミニウムおよび／または１若しくはそれ以上の非酸化アルミニウム化合物との混合物を焼結することにより得られる。 - 特許庁

In this alkaline storage battery having a non-sintering-type positive electrode applying nickel hydroxide as an active material, a negative electrode, a separator and an electrolyte, at least a cobalt compound and a yttrium element compound are added into the positive material; and the cobalt compound and the yttrium element compound are oxidized by an alkaline aqueous solution to form the alkaline storage battery.例文帳に追加

水酸化ニッケルを活物質とする非焼結式の正極、負極、セパレータおよび電解液を有するアルカリ蓄電池において、前記正極中に少なくともコバルト化合物とイットリウム族元素化合物を添加し、かつ、そのコバルト化合物とイットリウム族元素化合物をアルカリ水溶液で酸化処理することによって、アルカリ蓄電池を構成する。 - 特許庁

The titanium sintered compact 1 can be produced by a method comprising the steps of: obtaining the mixed powder by mixing the titanium powder 2 and the boron nitride powder 3; obtaining a compact by compacting the mixed powder; obtaining a degreased body by degreasing the compact; and obtaining the sintered compact by sintering the degreased body.例文帳に追加

このようなチタン焼結体１は、チタン粉末２および窒化ホウ素粉末３を混合して混合粉末を得る工程と、混合粉末を成形して成形体を得る工程と、成形体を脱脂して脱脂体を得る工程と、脱脂体を焼成して焼結体を得る工程とを有する方法により製造することができる。 - 特許庁

To provide a heat resistant coated member coated with a coating film hardly causing reaction or fusion with a metal or a ceramic in the melt-sintering or the heat treatment of the metal or the ceramic under a vacuum inert atmosphere or a reduction atmosphere and having excellent heat resistance, denseness and adhesion with a carbonaceous material.例文帳に追加

真空不活性雰囲気又は還元雰囲気下において金属又はセラミックスの溶解焼結又は熱処理を行う際に、該金属又はセラミックスと反応や溶着を起こし難く耐熱性と緻密性が優れしかも炭素質材との密着性が優れた皮膜を被覆した耐熱性被覆部材を提供することである。 - 特許庁

To provide a reduction-resistant dielectric composition prepared by uniformly dispersing a sintering additive component into a main component without segregation and a ceramic electronic component using the reduction-resistant dielectric composition, having excellent reliable durability, small self-heating in high frequency current and excellent charcteristics for medium/high voltage.例文帳に追加

焼結助剤成分を偏析させることなく主成分中に均一に分散させた耐還元性誘電体組成物を提供し、耐還元性誘電体組成物を用いて耐久信頼性に優れ、高周波電流下における自己発熱が小さく、中高圧用として優れた特性を有するセラミック電子部品を提供することを目的としている。 - 特許庁

The conveyor furnace 1 for drying or sintering matters adhering onto a substrate 10 conveyed into a chamber 2 comprises air curtains 18, 19 provided at the inlets/outlets 3, 4 of the chamber 2, and a section 20 for heating the air of the air curtains 18, 19.例文帳に追加

チャンバー２に基板１０を供給して、基板１０上に付着させた付着物を乾燥又は焼結させるコンベア炉１において、チャンバー２の基板出入口３，４に設けられたエアーカーテン１８，１９と、エアーカーテン１８，１９のエアーを加熱するエアー加熱部２０とを備えることを特徴とする。 - 特許庁

To provide a method for producing a BaTiO3 dielectric substance having a high dielectric constant and a low dielectric loss by decreasing the average particle size of BaTiO3 through a pretreatment in a reducing atmosphere before a sintering process in a dielectric substance production process in this method for producing the BaTiO3 dielectric substance having the high dielectric constant and a low dielectric loss.例文帳に追加

高い誘電常数と低い誘電損失を有するBaTiO_3誘電体の製造方法に関するものであり、誘電体製造工程中に焼結工程前に還元性雰囲気で前熱処理を通じてBaTiO_3の平均粒子大きさを小さくすることで高い誘電常数と低い誘電損失を有するBaTiO_3誘電体の製造方法を提供することにある。 - 特許庁

The method of manufacturing a printed circuit board includes: a process of forming a circuit pattern by discharging conductive ink on a carrier through inkjet printing; a process of heating and sintering the circuit pattern; and a process of transferring the circuit pattern by stacking the carrier on an insulation layer such that the circuit pattern is buried in the insulation layer.例文帳に追加

本発明に係る印刷回路基板の製造方法は、インクジェット方式を用いてキャリアに導電性インクを吐出して回路パターンを形成する工程と、回路パターンを加熱して焼結する工程と、回路パターンが絶縁層に埋め込まれるように、絶縁層にキャリアを積層して回路パターンを転写する工程と、を含むことを特徴とする。 - 特許庁

To provide a silicon carbide-based joined structure capable of obtaining a uniform and reliable joined part without causing slippage and being made large in size and complicated in shape in the joining of silicon carbide component unit by a reaction sintering process, and to provide a method and an apparatus for manufacturing the silicon carbide-based joined structure.例文帳に追加

反応焼結法による炭化ケイ素部品ユニットの接合において、ずれなどを生じず均一な信頼性のある接合部を得ることができ、炭化ケイ素接合構造体の大型化、複雑形状化を図ることができる炭化ケイ素系接合構造体、炭化ケイ素系接合構造体の製造方法および炭化ケイ素系接合構造体の製造装置を提供することを目的とする。 - 特許庁

This piezoelectric ceramics is represented by a general formula: ABO_3, wherein site A is mainly composed of lead, and site B is mainly composed of zirconium and titanium, and not lower than 0.02 wt% but not higher than 0.4 wt% in total of lead oxide and vanadium oxide are added thereto as sintering agents.例文帳に追加

一般式ＡＢＯ_３で表され、Ａサイトは鉛を主成分とし、かつ、Ｂサイトはジルコニウムおよびチタンを主成分とした圧電セラミックスであり、ＡＢＯ_３の総重量に対して、焼結助剤として酸化鉛と酸化バナジウムが合計で０．０２重量％以上０．４重量％以下添加されている。 - 特許庁

The Anodized aluminum catalyst carrier having increased BET specific surface area is distinguished by that pore diameters of fine pores in an anodized aluminum surface formed by anodic oxidation are enlarged by acid treatment of the anodized aluminum surface of a metallic plate having the anodized aluminum surface and then subjects the same to hydration treatment and further sintering are executed.例文帳に追加

陽極酸化されたアルマイト表面を有する金属板の該アルマイト表面を酸処理することにより、陽極酸化によって形成されたアルマイト表面の細孔の孔径を拡大し、次いで水和処理した後焼成してなることを特徴とする、ＢＥＴ比表面積が高められたアルマイト触媒担体。 - 特許庁

After sintering and fusing abrasive grains to be fixed using nickel-based brazing metal, macro- and micro-scratches are reduced by filling or covering by spreading-coating unsintered parts which are likely to be cracked or removed from a sintered surface with recrystallized parts for reducing a defective rate of polished products, and improving service life of polishing.例文帳に追加

研磨粒子をニッケル系ブレージング金属を用いて焼結融着して固定させた後、焼結表面から割れるとか、外れ出しやすい未焼結の部分と再結晶された部分とを展着コーティング処理により充填させたり、覆ったりすることにより、マクロ及びマイクロスクラッチを画期的に減らし、被研磨製品の不良率を低めて研磨寿命を高めることができる。 - 特許庁

A slurry is produced in which iron silicide powder is dispersed in water using a polymeric surfactant dispersant of a cation system such that its solid volume proportion becomes 50% or more, this slurry is casted into a mold fabricated in a predetermined shape to form a thermoelectric conversion element through dehydration, and in due time, sintering and annealing is done on it.例文帳に追加

ケイ化鉄の粉末をカチオン系高分子界面活性剤分散剤を用いて固体体積割合が５０％以上になるように水に分散させたスラリーを作製し、このスラリーを、熱電変換素子成形用の所定形状に加工された型に流し入れて脱水成形し、然る後に、焼結と焼鈍を行う。 - 特許庁

The crystal composition 100 of the silicon nitride sintered compact is composed of a crystal phase 110 comprising α-type silicon nitride 101 being fine particles and β-type silicon nitride 103 being needle-shaped particles and a grain boundary phase 120 existing between particles of the α-type silicon nitride 101 and β-type silicon nitride 103 and containing a sintering aid component.例文帳に追加

窒化珪素焼結体の結晶組成１００は、微少な粒子であるα型窒化珪素１０１および針状の粒子であるβ型窒化珪素１０３からなる結晶相１１０と、α型窒化珪素およびβ型窒化珪素の粒子の間に存在する、焼結助剤成分を含む粒界相１２０とから構成されている。 - 特許庁

To provide a pasty resin composition containing functional inorganic powder and an organic binder, which is excellent in coating, molding and sintering, and a manufacturing method of a sintered compact having functions such as a dielectric, ferroelectric, semiconductor, body with high toughness, etc.例文帳に追加

成形体が、誘電体、強誘電体、半導体又は強靱体等の機能を発揮する焼結成形体であって、その機能性無機粉体と有機バインダーとを含有するペースト状の樹脂組成物が、塗布性、形体賦形性、焼結性に優れた焼結成形用のペースト状樹脂組成物及び機能性焼結体の製造方法を提供することである。 - 特許庁

The method for manufacturing a porous conductor includes a step S1 for forming a spherical titanium powder sintered compact by sintering a spherical titanium powder and a step S2 for forming a spherical titanium powder thermally sprayed layer which is brought into contact with an electrolyte.例文帳に追加

球状チタン粉末を焼結処理して球状チタン粉末焼結体を形成する工程Ｓ１と、前記球状チタン粉末焼結体に、前記球状チタン粉末焼結体よりも細粒の球状チタン粉末を溶射することにより、電解質に接する球状チタン粉末溶射層を形成する工程Ｓ２とを有する。 - 特許庁

This forming die of an optical element is for forming an optical element by pressing an optical material, and the die body is constituted of a tungsten carbide sintered body obtained by sintering tungsten carbide without adding a metallic binder, where the particle diameter of the tungsten carbide is set to ≤100 nm.例文帳に追加

光学素材をプレスすることにより光学素子を成形する光学素子の成形用金型であって、タングステンカーバイドを、金属バインダーを添加することなしに焼結して、この焼結されたタングステンカーバイド焼結体により金型本体を構成し、前記タングステンカーバイドの粒径を１００ｎｍ以下に設定することを特徴とする。 - 特許庁

An electrode having no shrinkage or deformation in the sintering process or a highly dense electrode with superior dimensional stability can be provided.例文帳に追加

球形状合金と不規則形状合金を混合した粉末を、スパイラル溝によって分離された羽根型で中心部に凹部を有する形状に１８０ＭＰａ〜８００ＭＰａで加圧成形し、７００℃〜１０００℃の温度で還元性雰囲気または非酸化性雰囲気中で加熱することにより焼結し、この密度が、前記加圧成形後の密度と比較して、密度向上率が５％以下とした真空遮断器用電極とする。 - 特許庁

Since nitrogen serves as a nuclei at the time of sintering and the crystal growth of iron powder is suppressed, while strength and toughness is improved, also adhesiveness with the surface treatment layer 3 is excellent, and by making the open porosity into 12% or less, surface treatment layer 3 can be formed without sealing treatment, and airtightness can be secured by this surface treatment layer 3.例文帳に追加

焼結時に窒素が核となって鉄粉の結晶の成長が抑制されるため、焼結時に窒素が核となって鉄粉の結晶の成長が抑制されるため、強度とじん性が向上すると共に、表面処理層３との密着性に優れ、開放気孔率を１２％以下とすることにより、封孔処理することなく、表面処理層３を設けることができ、この表面処理層３により気密性を確保することができる。 - 特許庁

A negative electrode 2 used in a discharge lamp such as a xenon short arc lamp is a porous body in which an electrode body 20 comprising a discharge part 21 substantially discharging and a barrel part 22 supporting it and a terminal part 23 for external connection are integrally formed by sintering a raw material made of a high melting metal (for example, tungsten) after integral injection-molding by a metal injection molding method.例文帳に追加

キセノン・ショートアークランプ等の放電灯において用いられる陰極２は、実質的に放電を行う放電部２１と、それを支持する胴部２２とからなる電極本体２０と、外部接続用の端子部２３とが、高融点金属（例えば、タングステン）からなる原料を金属射出成形法により一体的に射出成形後、焼結することで一体として形成した多孔質体である。 - 特許庁

The iron-based sintered steel material comprises a sintered body obtained by sintering a molded body formed by press-molding raw material particles that contain Fe as a main component, and is characterized by containing 0.05-06 mass% of V, 0.1-1.0 mass% of C, and the balance Fe with inevitable impurities based on 100 mass% of the whole.例文帳に追加

本発明の鉄基焼結鋼材は、Ｆｅを主成分とする原料粉末を加圧成形した成形体を焼結させた焼結体からなる鉄基焼結鋼材であって、全体を１００質量％としたときに、０．０５〜０．６質量％のＶと、０．１〜１．０質量％のＣと、残部であるＦｅおよび不可避不純物とからなることを特徴とする。 - 特許庁

In a sintering stage for a compact finally made into a magnetostriction element, when the inside of a furnace is heated-up, in a temperature region where a hydride included in the compact is thermally decomposed and gaseous hydrogen is dissipated, the atmosphere in the furnace is sucked with a vacuum pump, the pressure in the furnace is held to the negative one, and the dissipation of hydrogen from the compact is promoted.例文帳に追加

最終的に磁歪素子となる成形体の焼結工程にて、炉内を昇温するに際し、成形体に含まれる水素化物が熱分解して水素ガスが放散される温度領域にて、炉内雰囲気を真空ポンプで吸引し、炉内の圧力を負圧に維持し、成形体からの水素の放散を促進するようにした。 - 特許庁

An electrode carbon material of a nonaqueous-solvent secondary battery has no diffraction peaks by X ray diffraction in (002) plane and (004) plane, and has a six-membered ring carbon structure in the carbon material, and is obtained by carbonizing an organic polymer material, in which at least a benzen ring structure is contained in the molecule, at a sintering temperature of 800 to 2,000°C.例文帳に追加

Ｘ線回折による（００２）面および（００４）面において回折ピークを有せず、かつ六員環炭素構造を炭素材料中に有する非水溶媒二次電池の電極炭素材料であり、分子中に少なくともベンゼン環構造を有する有機高分子材料を８００〜２０００℃の焼成温度で炭素化することにより得られる。 - 特許庁

The substrate includes a resin layer 100, wiring layers 101-107 buried in the upper surface of the resin layer 100, and semi-cured vias 108, 109 having a sintering temperature equal to or lower than the softening temperature of the resin layer 100, and having one end in contact with the wiring layers 102, 106 and the other end exposed from the lower surface of the resin layer 100.例文帳に追加

樹脂層１００と、樹脂層１００の上面に埋設された配線層１０１〜１０７と、樹脂層１００の軟化温度以下の焼結温度を有し、配線層１０２，１０６に一端が接触し且つ樹脂層１００の下面から他端が露出した半硬化状態のビア１０８，１０９とを備える。 - 特許庁

In this method for manufacturing the porous sintered body, after molding the powder of stainless steel, or molding the powder of stainless steel and sintering the powder in a vacuum atmosphere, by heating the body in nitrogen gas or NH_3 (ammonia) gas, without lowering the air permeability, the hardness of the product becomes high so that substantially no dents are generated even under the load of 3 kg/mm^2.例文帳に追加

ステンレス鋼の粉末を成形した後又はステンレス鋼の粉末を成形し、真空雰囲気中で焼結した後、窒素ガス又はＮＨ３（アンモニア）ガス中で加熱を行なうことにより、通気性の低下を起こすことなく、硬さが高くなると共に３ｋｇ／ｍｍ２の荷重を載せても実質的にくぼみが発生しなくなる。 - 特許庁

To provide a method of manufacturing a decorated pottery body which is capable of arranging and sintering images having high resolution and excellent gradation characteristic on the surfaces of building materials, such as art tiles, and pottery materials, such as ceramic materials, by using a transfer sheet having excellent film formability of transfer layers while maintaining a high color development density and are particularly excellent in adhesiveness and transferability of multicolor images.例文帳に追加

転写層の造膜性に優れた転写シートを用い、美術タイル等の建材やセラミックス材などの陶材の表面に、発色濃度を高く維持しながら、高解像度で階調性に優れた画像を陶材上に配置・焼結することができ、特に多色画像の接着性・転写性に優れた絵付陶体の製造方法を提供する。 - 特許庁

The boron carbide-silicon carbide complex carbon material having oxidation resistance is applied to the whole or part of the surface of a crucible for sintering, a crucible for vacuum deposition, a die for continuous casting, a crucible for melting a metal, a roller for transporting glass, a uniformly heating pipe for annealing a steel wire material, a jig for high-temperature burning and a jig for hot press.例文帳に追加

この耐酸化性の炭化ホウ素ー炭化ケイ素複合炭素材料を、焼結用ルツボ、真空蒸着用ルツボ、連続鋳造用ダイス、溶融金属用ルツボ、ガラス管搬送用ローラー、鋼線材焼鈍用均熱管、高温焼成用治具、ホットプレス用治具の表面の全部又は一部に適用する。 - 特許庁

The production device D for a brazing filler metal sheet 1 comprises: rolling rollers 4A, 4B sticking brazing filler metal powder 2 to at least either side of a metal sheet 21; and a heating part 6 sintering or melting the powder by heating, and the heating part 6 has a laser irradiation apparatus 10 irradiating the brazing filler metal powder 2 stuck to the metal sheet 21 with laser light L.例文帳に追加

シート状の金属板２１の少なくとも一方の面にロウ材粉末２を固着させる圧延ローラ４Ａ、４Ｂと、加熱することにより該粉末を焼結または溶融させる加熱部６とを有するロウ材シート１の製造装置Ｄであって、加熱部６は、金属板２１に固着されたロウ材粉末２にレーザ光Ｌを照射するレーザ照射装置１０を有する。 - 特許庁

The method for manufacturing a silicon nitride sintered compact comprises sintering a planar silicon nitride compact, which is obtained by compacting a powdery mixture obtained by adding a magnesium compound and the oxides of at least one metal selected from the group of yttrium and lanthanide group to silicon nitride powder and has 0.3 μm or smaller surface roughness (Ra value), in pressurized nitrogen atmosphere at 1,750-1,900°C.例文帳に追加

窒化珪素粉末に、マグネシウムの化合物と、イットリウム及びランタニド族の群からなる１種以上の酸化物とを添加した混合粉末を成形してなる表面粗さ（Ｒａ値）が０．３μｍ以下である平板状の窒化珪素質成形体を用い、窒素加圧下、１７５０〜１９００℃の所定の焼成温度下で焼結する窒化珪素焼結体の製造方法。 - 特許庁

The ceramic film filter is equipped with the base material 1 formed by baking a raw material containing aggregate, the filter film 2 obtained by baking the raw material containing ceramic particles and a sintering aid II applied to the base material 1 and the seal part 3 obtained by baking the raw material containing a sealant applied to a part of the base material 1 and a part of the filter film 2.例文帳に追加

骨材を含む原料が焼成されて成る基材１と、セラミック粒子及び焼結助剤ＩＩを含む原料が基材１上に施与され焼成され成る濾過膜２と、シール剤を含む原料が基材１の一部及び濾過膜２の一部に施与され焼成されて成るシール部３とを備えたセラミック膜フィルター。 - 特許庁

This fuel electrode material is made of mixed powder containing zirconia fine powder of which the 50% diameter is 0.4-0.8 μm, zirconia coarse powder of which the 50% diameter is 25-50 μm, and nickel oxide powder of which the 50% diameter is larger than 2 μm and smaller than 5 μm, and by sintering this material, a fuel electrode is made.例文帳に追加

その５０％径が０．４〜０．８μｍの範囲内にあるジルコニア微粉体と、その５０％径が２５〜５０μｍの範囲内にあるジルコニア粗粉体と、その５０％径が２μｍより大きく５μｍより小さい範囲内にある酸化ニッケル粉体とを含む混合粉体からなる燃料極材料とし、この材料を焼結させて燃料極とする。 - 特許庁

The resin powder for molding the laser sintering laminated layer is a resin composition containing the cyclic olefin based (co)polymer (A) derived from a cyclic olefin based monomer having a specific structure and the far-infrared laser absorber (B), wherein the weight ratio of the (co)polymer (A) to the far-infrared laser absorber (B) is 99.99/0.01-70/30.例文帳に追加

特定の構造を有する環状オレフィン系単量体から誘導される環状オレフィン系（共）重合体（Ａ）と遠赤外線吸収剤（Ｂ）とを含有する樹脂組成物であって、(共)重合体（Ａ）と遠赤外線吸収剤（Ｂ）との重量比が（共）重合体Ａ：赤外線吸収剤（Ｂ）＝９９．９９：０．０１〜７０：３０であるレーザー焼結積層造形用樹脂粉末。 - 特許庁

To provide a reduction-resistant dielectric composition which includes a main component consisting of particles uniformly coated with sintering auxiliary without segregating it and additives and is used for a base-metal inner electrode laminated ceramic capacitor that can be widely used as a medium or high voltage capacitor in a circuit such as a switching power supply circuit, a DC-DC converter circuit, a lighting inverter circuit or the like.例文帳に追加

スイッチング電源回路、ＤＣ−ＤＣコンバータ回路、照明用インバータ回路等に中高圧用として広く使用される積層セラミックコンデンサにおいて、焼結助剤成分を偏析させることなく主成分粉末の粒子の周囲に均一にコ−ティングさせた卑金属内部電極積層セラミックコンデンサ用耐還元性誘電体組成物を提供することを目的としている。 - 特許庁

The antistatic air-permeable porous body is obtained by grinding a mixture composed of a crosslinked polymer and an electroconductive particle-containing thermoplastic polymer being a thermoplastic polymer into which an electroconductive particle is uniformly dispersed by shear stress at a temperature lower than the melting temperature of the electroconductive particle-containing thermoplastic polymer to give compound material powder which is partially in a polymer alloy state and sintering the compound material powder under heating.例文帳に追加

架橋ポリマーと、導電性粒子を均一に分散させた熱可塑性ポリマーである導電性粒子含有熱可塑性ポリマーとからなる混合物を、導電性粒子含有熱可塑性ポリマーの溶融温度より低い温度で剪断力によって粉砕することによって得られる部分的にポリマーアロイ状の複合体粉末を加熱焼結してなる帯電防止性通気性多孔体。 - 特許庁

A wall papering box shaped casing 12 where a front surface plate 20 is constructed with an aluminum sintering panel is provided in the vicinity of a wall surface in a room, and there are provided in the box shaped casing 12 a fresh air introduction indoor air conditioning unit 14, and a circulation passage 16 for circulating cold air blown off from a blowoff outlet 14a in the box shaped casing 12.例文帳に追加

室内の壁面近傍に、前面板２０がアルミ焼結パネルで構成された腰壁状の箱形ケーシング１２を設けるとともに、この箱形ケーシング１２内に、外気導入式の室内空調ユニット１４と、その吹出し口１４ａから吹き出される冷気を箱形ケーシング１２内において循環させる循環通路１６とを設ける。 - 特許庁

To provide a method for manufacturing a raw material for sintering, in which solid fuel powders such as coke are separated from iron ores, SiO_2- containing raw powders, and limestone raw powders; the iron ores, the SiO_2- containing raw powders, and the limestone-raw powders are granulated and subsequently making pseudo-grains step by step and coating the pseudo-grains with the solid fuel raw powders.例文帳に追加

固体燃料系粉原料を鉄鉱石，SiO_2含有粉原料，石灰石系粉原料から分離して、鉄鉱石，SiO_2含有粉原料，石灰石系粉原料を造粒し、次いで固体燃料系粉原料を添加することによって段階的に擬似粒子にすることにより、擬似粒子の表層部に粉コークスなどの固体燃料系粉原料を適切に外装することができる焼結用原料の製造方法を提供する。 - 特許庁

The metal injection molding process also comprises preparing a water soluble binder by dissolving a protein-based material and a monovalent alkali metal salt in water, further adding polyhydric alcohol, a surface active agent, and an antiseptic agent, kneading either a metal powder or a ceramic powder with the binder, forming a compact by the injection molding of the kneaded mixture, removing the binder in the formed compact, and sintering the compact.例文帳に追加

また、タンパク質系物質と一価のアルカリ金属塩を水に溶解した水溶性バインダーに更に、多価アルコール、界面活性剤、防腐剤を添加し、これに金属粉末またはセラミックス粉末とを混練し、この混練物を射出成形して成形体を形成し、この射出成形体を脱バインダー処理した後、焼結する金属射出成形法である。 - 特許庁

The method of forming a circuit pattern of a printed circuit board includes (a) a step of applying an etching liquid to the portions of an insulating board where the circuit pattern is formed, (b) a step of curing the etching liquid under adjusted curing conditions, (c) a step of coating a metal ink over the etched circuit pattern, and (d) a step of sintering the metal ink.例文帳に追加

(ａ)絶縁基板の回路パターンの形成される部分にエッチング液を塗布する段階、(ｂ)養生条件を調節してエッチング液を養生する(curing)段階、(ｃ)エッチングされた回路パターンにメタルインクを塗布する段階、及び(ｄ)メタルインクを焼成する段階を含む印刷回路基板の回路パターン形成方法。 - 特許庁

This is a manufacturing method of a cold cathode for a discharge tube, which has a cold cathode at the tip of a lead sealed through the edge of a glass tube containing rare gas and mercury and has a processes of producing a mixed powder of titanium hydride powder and a high-melting point metal powder, and manufacturing a formed body with the mixed powder, and also sintering the formed body.例文帳に追加

希ガスや水銀を封入したガラス管の端部に封装された導入線の先端部に冷陰極を具備する冷陰極放電管における冷陰極の製造方法であって、水素化チタンの粉末と高融点金属の粉末とを混合して混合粉を作製する工程と、混合粉を成形して成形体を作製する工程と、成形体を焼結する工程とを含むことを特徴とする。 - 特許庁