「continuous-casting」に関連した英語例文の一覧と使い方(31ページ目) - Weblio英語例文検索

To enable the production of a metallic product of high quality by casting a slab reduced in surface defects and internal inclusions when performing continuous casting without blowing an inert gas from a nozzle feeding molten steel into a mold.例文帳に追加

鋳型へ溶鋼を供給するノズルから不活性ガスを吹き込まずに連続鋳造する際、表面欠陥や内部介在物の少ない鋳片を鋳造して、高品質の金属製品の製造を可能とする。 - 特許庁

To provide a dipping nozzle capable of slowing the flow of molten steel in a mold, forming the uniform flow, preventing generation of defects such as bubbles and inclusions, and realizing high-speed casting, and a continuous casting method using the dipping nozzle.例文帳に追加

鋳型内の溶鋼の流れを緩慢にし、かつ均一な流れを形成して、気泡や介在物欠陥を防止して高速鋳造を可能にする浸漬ノズル及びこれを用いた連続鋳造方法を提供する。 - 特許庁

In a continuous steel casting machine, a thickness of the objects adhering to the outer circumference of the immersion nozzle facing a long side of a mold is regulated to 15mm or less in an average thickness between from the molten steel surface to one-third of an immersion length, and the casting is performed.例文帳に追加

鋼の連続鋳造機において、鋳型長辺に面する浸漬ノズル外周部の付着物厚みを、溶鋼湯面から浸漬長さの１／３ までの平均厚さで、１５ｍｍ以下に調整して鋳造する。 - 特許庁

To provide a semi-continuous casting method of hollow ingots, which is a further cost-effective method for manufacturing hollow ingots, concerning a casting of hollow ingots utilized for manufacturing a large diameter casing or pipe.例文帳に追加

大口径ケーシングまたはパイプの製造に用いられるような中空インゴットの鋳造に関し、より費用効果の高い中空インゴットの製造方法である中空インゴットの半連続鋳造方法を提供する。 - 特許庁

To provide a marking device for a continuous casting machine capable of specifying the mold responsible for casting defective products of a short size material, and a marking method therefor.例文帳に追加

成形された短尺材製品の不良品について、どの鋳型から鋳造されたものであるかを特定することができる連続鋳造機のマーキング装置およびそのマーキング方法を提供することを課題とする。 - 特許庁

To provide a method for smelting low-carbon high-manganese steel, which enables a stable continuous casting to be operated without causing a blockage of a ladle nozzle during casting, even when employing high carbon ferromanganese as a Mn source.例文帳に追加

本発明は、Ｍｎ源に高炭素フェロマンガンを使用しても、鋳造時に取鍋ノズルの閉塞がなく、安定した連続鋳造操業が可能な低炭素、高マンガン鋼の溶製方法を提供することを目的としている。 - 特許庁

To provide a method for producing low carbon and high manganese steel with which even when using high carbon ferro-manganese as the Mn source, clogging of a nozzle does not occur at the casting time, and a stable continuous casting can be achieved.例文帳に追加

本発明は、Ｍｎ源に高炭素フェロマンガンを使用しても、鋳造時のノズル閉塞がなく、安定した連続鋳造操業が可能な低炭素、高マンガン鋼の溶製方法を提供することを目的としている。 - 特許庁

To prevent the penetration of the outside air into a tundish (molten metal container) from a gap between the tundish and its lid in a continuous casting device so as to stabilize the quality of the casting and enhance the workability for adhering the lid.例文帳に追加

連続鋳造装置におけるタンディッシュ（溶鋼容器）内にその蓋体との隙間から外気が侵入するのを防止し、鋳造品の品質を安定させるとともに、蓋体被着の作業性を向上させる。 - 特許庁

To provide an electromagnetism casting apparatus of a silicon ingot which can control that molten silicon is contaminated with a metal impurity due to the atmospheric gas which goes up the gap between the inner surface of an after heater and the outer peripheral surface of an ingot, at the time of continuous casting by an electromagnetic casting method.例文帳に追加

電磁鋳造法による連続鋳造の際に、アフターヒーターの内周面とインゴットの外周面との隙間を上昇する雰囲気ガスに起因して、溶融シリコンが金属不純物で汚染されることを抑制できるシリコンインゴットの電磁鋳造装置を提供する。 - 特許庁

To provide an immersion nozzle for continuously casting steel with which clogging by Al_2O_3 in molten steel is prevented and the structural stability of which is high without spoiling the cleanliness of a slab and without hindering the stability of the continuous casting operation when continuously casting the molten steel.例文帳に追加

溶鋼の連続鋳造の際に、鋳片の清浄性を損なうことなくかつ連続鋳造操業の安定性を阻害することなく、溶鋼中のＡｌ_２Ｏ_３による閉塞を防止することができ、かつ構造安定性の高い鋼の連続鋳造用浸漬ノズルを提供すること。 - 特許庁

To properly carry out the control of the flow of molten steel by properly selecting the frequency of the moving magnetic field according to casting conditions when carrying out the continuous casting while controlling the flow of molten steel in a casting mold by applying the electromagnetic force caused by the moving magnetic field to the flow discharged from an immersed nozzle.例文帳に追加

浸漬ノズルから吐出される吐出流に移動磁場による電磁力を作用させて鋳型内の溶鋼流動を制御しながら連続鋳造するに際し、移動磁場の周波数を鋳造条件に応じて適性化させて溶鋼流動の制御を適性に行なう。 - 特許庁

To provide a flux for continuous casting having suitable fusing characteristics with which the development of sintered blocks or slag bears in a mold in the case of continuously casting a steel is prevented, with which the stable casting is secured and with which the development of surface defects on a cast slab is prevented.例文帳に追加

本発明は、鋼の連続鋳造の際に発生する鋳型内での焼結塊、またはスラグベアの発生を防止し、安定な鋳造を確保するとともに、鋳片の表面欠陥発生を防止するために、適切な溶融特性を有する鋼の連続鋳造用フラックスを提供する。 - 特許庁

In the continuous casting apparatus for casting the continuously cast bar from molten aluminum alloy 255, a vibration-giving device 411 which imparts mechanical vibration to molten aluminum alloy near the solidification surface via the solidification surface of the cast bar 1 from the surface of the cast bar 1 during the casting, is arranged.例文帳に追加

アルミニウム合金溶湯２５５から連続鋳造棒を鋳造する連続鋳造装置において、鋳造中の鋳造棒１の表面から鋳造棒１の凝固面を介して凝固面近傍のアルミニウム合金溶湯に機械的振動を付与する振動付与装置４１１を設ける。 - 特許庁

To provide a cast slab supporting system just below a mold with which, in a continuous casting for casting a continuously cast slab having square shaped cross section, the internal crack produced when a cooling plate is used for supporting the cast slab just below the mold is prevented and even at the high speed casting, break-out does not occur.例文帳に追加

断面方形の連続鋳造鋳片を鋳造する連続鋳造において、鋳型直下の鋳片支持にクーリングプレートを用いたときに発生する内部割れを防止するとともに、高速鋳造時においてもブレークアウトの発生しない鋳型直下鋳片支持方式を提供する。 - 特許庁

An austenitic stainless steel sheet processed by in-line rolling reduction and heat treatment after casting in a double drum type continuous casting system, is a thin casting slab in which a high angle intercrystalline rate of the crystalline texture exceeds 85% of the whole intercrystal.例文帳に追加

双ドラム式連続鋳造で鋳造後、インラインにて圧下と熱処理を施したオーステナイト系ステンレス鋼の薄鋳片であって、該薄鋳片の結晶組織が、全結晶粒界に占める高角度結晶粒界の割合が８５％を超える結晶組織からなる薄鋳片である。 - 特許庁

(1) In the method and apparatus for continuous casting of the molten metal by supplying the molten metal into a casting mold via a tundish, metallic vapor and/or metallic powder is supplied from an immersed lance immersed in the tundish or a lance immersed in the casting mold.例文帳に追加

(1)タンディッシュを経て鋳型に溶融金属を供給する連続鋳造する方法であって、タンディッシュ内に浸漬させた浸漬ランスまたは鋳型内に浸漬させたランスから金属蒸気および／または金属粒子を供給する溶融金属の連続鋳造方法および連続鋳造装置。 - 特許庁

The continuous casting apparatus for casting a continuously-cast bar out of a molten aluminum alloy 255 has a vibration imparting device 411 which imparts the mechanical vibration to the molten aluminum alloy in a vicinity of a solidified surface from a surface of the continuously-cast bar 1 during the casting via the solidified surface of the continuously-cast bar 1.例文帳に追加

アルミニウム合金溶湯２５５から連続鋳造棒を鋳造する連続鋳造装置において、鋳造中の鋳造棒１の表面から鋳造棒１の凝固面を介して凝固面近傍のアルミニウム合金溶湯に機械的振動を付与する振動付与装置４１１を設ける。 - 特許庁

When the continuous casting is performed by using a mold powder of a cement backing material, casting is performed at the mold powder consumption of 0.23 kg/m^2 or more by adjusting properties of the mold powder and oscillation conditions, and the high speed casting is stably performed at the pouring speed of 2.5 m/min or more.例文帳に追加

セメント基材のモールドパウダを使用して連続鋳造する際に、モールドパウダの物性及びオシレーション条件を調整して、モールドパウダの消費量を０．２３ｋｇ／ｍ^2以上にして鋳造し、鋳込み速度２．５ｍ／ｍｉｎ以上の高速鋳造を安定的に行う。 - 特許庁

To provide an immersion nozzle for continuous casting which is used for pouring molten steel into a casting mold and realizes an improvement in cast billet quality or stability of casting by suppressing erosion of the immersion nozzle and inhibiting the clogging or blocking of the nozzle caused by inclusions stuck to the immersion nozzle.例文帳に追加

鋳型内に溶鋼を注湯する浸漬ノズルの溶損を抑制し、さらに、浸漬ノズルに介在物が付着してノズル詰まりやノズル閉塞を生じるのを抑制して鋳片の品質向上や鋳造の安定化を図ることができる連続鋳造用浸漬ノズルを提供する。 - 特許庁

In the continuous casting method which applies rolling reduction to a bulged cast slab until completing solidification after bulging the cast slab 2 including non-solidified part 2b, the draft at the unsteady casting time in the final stage of the casting is regulated to be <Dxa unsteady draft obtd. with the formula Dxa=D-(2Bav-Bxav).例文帳に追加

未凝固部２ｂを含む鋳片２をバルジングさせた後、凝固完了までの間でバルジングした鋳片を圧下する連続鋳造方法であって、鋳造末期の非定常鋳造時の圧下量を、下記（Ａ）式で求まる非定常圧下量Ｄｘａ以下とする鋼の連続鋳造方法。 - 特許庁

To prevent the development of skull on the inner surface of a side weir during casting by avoiding the cooling caused by the contact of the inner surface of the side weir with the end surfaces of rolls during supplying non- oxidizing gas onto a molten metal pool part before starting the casting in a twin-roll type continuous casting method.例文帳に追加

双ドラム式連続鋳造方法において、鋳造開始前の湯溜まり部への非酸化性ガス供給中におけるサイド堰内面のドラム端面との接触による冷却を回避することで、鋳造中におけるサイド堰内面での地金生成を防止する。 - 特許庁

To provide a cooling roll and a twin roll type continuous casting method which enable, in the initial stage of casting, quick formation of good sealing state and after coming into a stationary state of casting, maintaining of the good sealing state by making a side weir refractory wear by necessary amount at the necessary time.例文帳に追加

鋳造初期には、速やかに良好なシール状態を形成し、鋳造が定常状態に至った後は、必要な時に必要量サイド堰耐火物を摩耗せしめ、良好なシール状態を維持する冷却ドラムと双ドラム式連続鋳造方法を提供する。 - 特許庁

To provide a mold for continuously casting a steel slab and a continuous casting method, which can use high viscosity powder and can obtain a casting having excellent quality in which generation of surface defects and internal defects in the casting are prevented, and further oscillation of the molding, which was indispensable until now, can be indispensed with in some cases.例文帳に追加

鋼スラブの連続鋳造において、高粘性パウダーの使用を可能とするとともに、鋳片の表面欠陥及び内部欠陥などの発生を防止した優れた品質の鋳片を得ることができ、しかも場合によっては従来必須とされていた鋳型のオシレーションを不要とするスラブ連続鋳造用鋳型と連続鋳造方法を提供すること。 - 特許庁

To provide a mold for continuously casting a steel slab and a continuous casting method, which can use high viscosity powder and can obtain a casting having excellent quality in which generation of surface defects and internal defects in the casting has been prevented, and further oscillation of the molding, which was indispensable until now, can be dispensed with the oscillation.例文帳に追加

鋼スラブの連続鋳造において、高粘性パウダーの使用を可能とするとともに、鋳片の表面欠陥及び内部欠陥などの発生を防止した優れた品質の鋳片を得ることができ、しかも場合によっては従来必須とされていた鋳型のオシレーションを不要とするスラブ連続鋳造用鋳型と連続鋳造方法を提供すること。 - 特許庁

To provide a mold for continuously casting a steel slab and a continuous casting method, which can use high viscosity powder and can obtain a casting having excellent quality in which generation of surface defects and internal defects in the casting has been prevented, and further oscillation of the molding, which was indispensable until now, can be dispensed with in some cases.例文帳に追加

鋼スラブの連続鋳造において、高粘性パウダーの使用を可能とするとともに、鋳片の表面欠陥及び内部欠陥などの発生を防止した優れた品質の鋳片を得ることができ、しかも場合によっては従来必須とされていた鋳型のオシレーションを不要とするスラブ連続鋳造用鋳型と連続鋳造方法を提供すること。 - 特許庁

To provide a continuous casting method of steel, which method can manufacture a cast ingot having excellent internal quality by surely controlling the discharge flow from an immersed nozzle.例文帳に追加

浸漬ノズルからの吐出流を確実に制御して、内部品質に優れた鋳片を製造するための鋼の連続鋳造方法を提供する。 - 特許庁

As the film 31 obtained has no twitch, crease, curl or the like, and foreign articles are hardly stuck on the rollers R1-R3, a continuous film-casting can be stably performed.例文帳に追加

得られるフィルム３１は、ツレ、シワ、カール等がなく、また、ローラＲ１〜Ｒ３には異物が付着しにくいので、安定して連続製膜を行うことができる。 - 特許庁

To provide a continuous casting method for steel which allows the easy precipitation of crystal phases into mold powder and ensures effective slow cooling by the mold powder.例文帳に追加

モールドパウダー中に結晶相が析出しやすく、モールドパウダーにより緩冷却を有効に行なうことができる鋼の連続鋳造方法を提供する。 - 特許庁

Equipment designing is performed in such a manner that a hollow slab press-welding system is made possible in a drawing locus composed of a 3/4 circumference and rectilinear propagation by curved type continuous casting.例文帳に追加

湾曲式連続鋳造で３／４円周と直進から成る引抜軌跡において中空鋳片圧接方式が可能な設備設計を行う。 - 特許庁

A slab T having proper unit weight of >20 tons is cast with a continuous casting machine 1 and fed to a roughing mill 3 without heating the slab T.例文帳に追加

連続鋳造機１は２０ｔを越える適宜の単重のスラブＴを鋳造し、スラブＴは加熱されることなく粗圧延機３に給送される。 - 特許庁

To automatically make a production plan by planning the optimum steel tapping date in a unit of a sequentially continuous casting set.例文帳に追加

連々鋳セット単位の最適な出鋼日を立案し、生産計画を自動化することを可能にした鋳造の操業計画策定方法を提供する。 - 特許庁

On the inner wall surface of the mold 1 in the slab continuous casting machine, a wear-resistant layer 1a is formed by performing high speed gas flame thermal spray of a powdery mixture of W and Co thereto.例文帳に追加

スラブ連続鋳造機のモールド１の内壁面に、ＷＣとＣｏの混合粉体を高速ガスフレーム溶射させて耐磨耗層１ａを形成させる。 - 特許庁

To provide the continuous casting method for a cast slab capable of reducing center porosity without causing any surface crack when reducing the cast slab.例文帳に追加

鋳片を圧下するに際し、表面ひび割れを発生させることなく、中心ポロシティを低減することができる、鋳片の連続鋳造方法を提供する。 - 特許庁

To provide an immersion nozzle with which the sticking of alumina on the inner surface of the nozzle is prevented and development of surface defect is prevented, and a continuous casting method.例文帳に追加

ノズル内面にアルミナが付着するのを防止し、製品の表面欠陥の発生を防止する浸漬ノズルおよび連続鋳造方法を提供する。 - 特許庁

The mold for continuous casting is peculiarly provided with a cooling water shut-off material (spray guard) 11 at least on the lower end surface 5 at the long wall side of a base body in the mold.例文帳に追加

鋳型の基体の少なくとも長辺側下端面５に冷却水遮蔽体11を具備していることを特徴とする連続鋳造用鋳型。 - 特許庁

To provide a method for preventing degradation of cleanability of steel caused by inclusions in a tundish in changing a ladle during the continuous casting.例文帳に追加

連続鋳造における取鍋交換の際に生じるタンディッシュ内の介在物の巻き込みによる鋼の清浄度の悪化を防ぐ方法を提供する。 - 特許庁

METHOD FOR CHANGING WIDTH OF CAST SLAB DURING CONTINUOUS CASTING, SYSTEM FOR CHANGING WIDTH OF CAST SLAB, UNIT FOR MAKING POSITIONAL PATTERN TABLE OF SHORT SIDES IN MOLD AND COMPUTER PROGRAM AND RECORDING MEDIUM例文帳に追加

連続鋳造中の鋳片幅変更方法、鋳片幅変更システム、鋳型短辺の位置パターン表生成装置、コンピュータプログラム、及び記録媒体 - 特許庁

The immersion nozzle 1e for the continuous casting is made of a refractory having electroconductivity and equipped on the inner face with a rectifier 12b provided with an electrode 3b.例文帳に追加

電気伝導性を有する耐火物からなり電極１３ｂが設けられた整流部１２ｂを内面に備える連続鋳造用浸漬ノズル１ｅ。 - 特許庁

To provide a continuous casting method of a pipe material with a screwed center hole, with which the pipe materials with screwed center holes can be mass-produced and the manufacturing cost can drastically be reduced.例文帳に追加

ねじ孔管材を大量生産することができ、製作コストを大幅に低減することができるねじ孔管材の連続鋳造法を提供する。 - 特許庁

To provide a curved multipoint straightening continuous casting equipment capable of performing multipoint straightening with high productivity by simple remodeling on a small scale.例文帳に追加

簡易かつ小規模の改造により高生産性を有する多点矯正化が可能となる湾曲型多点矯正連続鋳造設備を提供する。 - 特許庁

To provide a method for subjecting a slab of high internal quality having reduced center segregation and center porosities to soft reduction continuous casting only by the addition of a simple apparatus.例文帳に追加

簡単な装置の追加だけで中心偏析やセンターポロシティの少ない内部品質の良好な鋳片を軽圧下連続鋳造する方法を提案する。 - 特許庁

To provide a continuous casting method for steel which can continuously cast steel such as a molten steel at high speed without causing the occurrence of crack defects or the like.例文帳に追加

割れ欠陥の発生等を招くことなく溶鋼などの鋼を高速で連続鋳造することのできる鋼の連続鋳造方法を提供する。 - 特許庁

Many slits 3 having high aspect ratio (depth/width) and curved surface state hollow parts 4, are formed on the outer peripheral surface of a barrel part of the roll for continuous casting.例文帳に追加

連続鋳造用ロールの胴部外周面に、アスペクト比（深さ／幅）が高く先端に曲面状の空洞部４を持つスリット３を、多数形成する。 - 特許庁

To provide a roll segment of continuous casting equipment which is easy in a roll arrangement control and does not generate cracks of a cast slab and the damage of a cast slab guide device.例文帳に追加

ロール配列管理が容易で、鋳片の割れや鋳片案内装置への損傷を生じることのない連続鋳造設備のロールセグメントを提供する。 - 特許庁

To provide a continuous casting device in which product quality and production efficiency are improved without increasing complication of the device structure nor increasing the number of components.例文帳に追加

連続鋳造装置において、装置構造の複雑化や部品点数の増加を招くことなく、製品品質及び製造効率を向上させる。 - 特許庁