This method for producing the heat shrinkable polyester artificial hair involves carrying the out melt spinning of a composition comprising (A) 80-40 wt.% of a polyalkylene terephthalate or a copolyester consisting essentially of the polyalkylene terephthalate and (B) 20-60 wt.% of a polyarylate, drawing the resultant fiber and then performing heat treatment in two stages.例文帳に追加

ポリアルキレンテレフタレート又はポリアルキレンテレフタレートを主体とした共重合ポリエステル（Ａ）８０〜４０重量％とポリアリレート（Ｂ）２０〜６０重量％を含有する組成物を用いて溶融紡糸し、延伸した後に、二段階の熱処理を行うことを特徴とする熱収縮性ポリエステル系人工毛髪の製造方法により達成される。 - 特許庁

The method for producing the opal-finished and discharge-printed synthetic fiber material includes superimposing discharge printing paste containing an alcohol-based alkylene oxide adduct and/or an amine-based alkylene oxide adduct on an opal finishing paste containing an alkali metal hydroxide, printing the superposed paste to a base fabric and then heat-treating the fabric to simultaneously apply opal finish and discharge printing.例文帳に追加

アルカリ金属水酸化物を含む抜蝕印捺糊と、アルコール系アルキレンオキサイド付加物及び／又はアミン系アルキレンオキサイド付加物を含む抜染印捺糊とを重ねて基布に印捺した後に熱処理して抜蝕加工と抜染加工とを同時に施すことを特徴とする抜蝕及び抜染加工された合成繊維材料の製造方法。 - 特許庁

This method for producing the subject fibers is characterized by comprising the following process: the flank of a bundled assembly of polyester-based fibers is covered with a material substantially insoluble to water under the condition of hydrolyzing the fibers, and the resultant fiber assembly is soaked in an alkaline treatment liquid and hydrolyzed; wherein the hydrolysis treatment is performed using a package dyeing machine.例文帳に追加

ポリエステル系繊維よりなる束状集合体の側面部を、該繊維の加水分解条件下で実質的に溶解しない素材で被覆し、しかる後、これをアルカリ性の処理液に浸漬し、加水分解するに際し、該加水分解処理をパッケージ染色機を用いて行うことを特徴とする両端先鋭化繊維の製造方法。 - 特許庁

To provide a method for jointing a metal/ceramic or a ceramic/ceramic where the strength at the joint area is optimized to be capable of guaranteeing sufficient strength at the brazed joint against stress loaded after jointing, in producing a brazed joint for a ceramic material, especially for a fiber reinforced ceramic material having a layered structure.例文帳に追加

セラミック材料とくに積層構造を有する繊維強化セラミック材料に対してろう付け接合部を製造する際に接合部領域の強度を最適化し接合後の応力に対してもろう付け接合部の十分な強度を保証することのできる金属／セラミック接合方法あるいはセラミック／セラミック接合方法の提供。 - 特許庁

The method for producing the base fabric for the airbag includes weaving the fabric by using the warp yarns comprising synthetic fiber filaments having 0.180-0.230 low-speed friction coefficient (F/M-0.1μ)例文帳に追加

合成繊維フィラメントからなる糸の対金属低速摩擦係数（Ｆ／Ｍ−０．１μ）および対金属高速摩擦係数（Ｆ／Ｍ−１００μ）がそれぞれ以下の値を有する経糸であり、原糸油剤を０．５〜２．０重量％付与され、更に処理油剤を０．３〜２．０重量％追油した経糸を使用して製織することを特徴とするエアバッグ用基布の製造方法。 - 特許庁

To provide an industrial method of production of a heat-resistant mat in which an organic binder is uniformly dispersed and which has a substantially uniform thickness, by including the organic binder disappeared by thermal decomposition in the alumina fiber mat compressed in the thickness direction.例文帳に追加

厚さ方向に圧縮されたアルミナ質繊維マット中に熱分解によって消失する有機バインダーが含有されて成る耐熱性マットの製造方法であって、有機バインダーが実質的に均一に存在して厚さが実質的に均一である耐熱性マットが得られる様に改良された工業的に有利な製造方法を提供する。 - 特許庁

Further, there is provided a method for treating or contacting substrates chosen from nonwoven fabrics, woven fabrics and composites, such as glass fiber substrates with the thermosetting aqueous binder composition, and drying and curing, as well as water-resistant products produced thereby.例文帳に追加

更に、本発明は、不織布、織物および複合体から選択される基体、例えばガラス繊維基体などを本熱硬化性水性結合剤組成物で処理し、または前述の基体を本熱硬化性水性結合剤組成物と接触させ、さらに乾燥および硬化させる方法、更には、前述の方法により製造される耐水生成物を提供する。 - 特許庁

To provide: a fine-denier polyester yarn having excellent breakage preventing performance and lightness, in addition to excellent weather resistance and dimensional stability which are inherent in polyester fiber textile, and capable of being formed as a fabric suitable especially for sport gear using air pressure and requiring lightness such as a paraglider; and a method for manufacturing the same.例文帳に追加

本発明は、ポリエステル繊維織物が本来有する、優れた耐候性、および寸法安定性に加えて、耐破れ性および軽量性に優れ、パラグライダーの様に特に軽量性を重視する風圧を利用するスポーツ用具に好適な布帛とすることのできる細繊度ポリエステル糸、及びその製造方法を提供することにある。 - 特許庁

The method of producing the carbon fiber composite material is characterised in that it includes a process for mixing an elastomer 30 having an unsaturated bond or a group having an affinity to the carbon nanofiber 40 with metal particles 50, and a process for dispersing the carbon nanofiber 40 into the elastomer 30 including the metal particles 50 by a shear force.例文帳に追加

炭素繊維複合材料の製造方法は、カーボンナノファイバー４０に対して親和性を有する不飽和結合または基を有するエラストマー３０と、金属粒子５０と、を混合する工程と、金属粒子５０を含むエラストマー３０に、カーボンナノファイバー４０を剪断力によって分散させる工程と、を含むことを特徴とする。 - 特許庁

To provide a method for the production of a filled glass fiber nonwoven cloth for backing use, coated with a polyvinyl chloride resin and used as a flooring material decreasing the defect of kinked old rug of compounded NBKP (softwood pulp) and giving a backing material having a surface coated with a vinyl chloride resin and having excellent flatness.例文帳に追加

本発明は、ポリ塩化ビニルが塗布加工され床材として使用される裏打ち用抄合わせガラス繊維不織布の製造方法に関し、配合物であるＮＢＫＰのよれたボロ異物等の欠点を減少し、平坦性の良好な塩化ビニル塗布加工面が得られる裏打ち材の抄合わせガラス繊維不織布を提供する事を目的とする。 - 特許庁

In this method the conjugated polyester yarn is obtained by conjugating a yarn A mainly comprising a polyester fiber having 20-80×10-3 double refractive index with a yarn B comprising at least one or more kinds of other fibers and treating the yarn at 50-150°C under wet heating and/or dry heating in a state in which the conjugated yarn is wound around a core material.例文帳に追加

主として複屈折率が２０〜８０×１０^-3のポリエステル繊維からなるＡ糸と少なくとも１種以上の他繊維からなるＢ糸を複合して複合糸となし、該複合糸を芯材に巻いた状態で５０〜１５０℃の湿熱および／または乾熱処理を行うことを特徴とするポリエステル複合糸の製造方法。 - 特許庁

To solve the problem that a current method for processing the tip surface of an optical fiber to form a lens in order to enhance propagation efficiency of light is not used widely because it necessitates an advanced processing technique and many man-hours, and it is difficult to form lenses having a uniform characteristic in a large amount, although the shape of a connected portion is made compact.例文帳に追加

光の伝搬効率を向上するために、現在行われている光ファイバの先端面を加工してレンズを形成する方法は、結合部の形状はコンパクトになるが、高度の加工技術を必要とし多くの工数を必要とし、均一な特性のレンズを大量に形成することは困難であるため広く実用される状況には至っていない。 - 特許庁

This ink-jet printing method comprises printing a fabric comprising a synthetic fiber and cellulose with a reactive dye and a disperse dye by ink-jet system; wherein, in advance, the fabric is treated with an acidic aqueous dispersion containing a cellulose-reactive compound, a water-soluble polymer and a water-insoluble inert organic compound 40-150°C in melting point and put to drying treatment.例文帳に追加

セルロース繊維及び合成繊維から成る布帛を反応染料と分散染料を用いてインクジェット捺染するに際し、予め該布帛に繊維素反応性化合物、水溶性ポリマー、及び融点が４０℃〜１５０℃である非水溶性不活性有機化合物を含む酸性の水性分散液を付与し、そして乾燥処理を行う。 - 特許庁

This method for producing the unstretched polyethylene naphthalate fiber includes: melting the polyethylene naphthalate having 0.40-0.60 dL/g intrinsic viscosity, melt-spinning at 800-1,500 m/min spinning speed by using a spinneret having ≥1,000 number of holes of the spinneret at 250-450 g/min ejection amount of the polyethylene naphthalate.例文帳に追加

上記課題は、固有粘度が０．４０〜０．６０ｄＬ／ｇのポリエチレンナフタレートを溶融し、ポリエチレンナフタレートの吐出量が２５０〜４５０ｇ／分であり、紡糸口金の孔数１０００個以上の紡糸口金を用いて紡糸速度８００〜１５００ｍ／分で溶融紡糸する未延伸ポリエチレンナフタレート繊維の製造方法によって解決することができる。 - 特許庁

The producing method of the carbon incorporated cemented excelsior board is by adding an adequate quantity of magnesium chloride to 20-30% wood fiber, 3-30% carbon and 40-65% cement by weight to mix by stirring and after press molding the mixture, applying an exposing means of the carbon.例文帳に追加

また方法の発明は、木材繊維２０％〜３０％（重量）と、炭類３％〜３０％（重量）と、セメント４０％〜６５％（重量）とに、適量の塩化マグネシウム溶液を加えて撹拌混合し、この混合物を加圧成形した後、炭類の露出手段を施すことを特徴とした炭類混入の木毛セメント板の製造方法である。 - 特許庁

This fabric for the air bag comprising a synthetic fiber woven fabric is characterized in that air permeability is ≤60 cc/cm2/sec after extended in the longitudinal direction of the woven fabric and also ≤60 cc/cm2/sec after extended in the lateral direction of the woven fabric, when the air permeability is measured by a method defined in the text.例文帳に追加

本発明のエアバッグ基布は、合成繊維織物からなるエアバッグ基布において、本文中に規定する方法で測定されたときの、該織物の長さ方向に伸長した後の通気度、および、該織物の幅方向に伸長した後の通気度が、いずれも６０ｃｃ／ｃｍ^2／ｓｅｃ以下であることを特徴とするものである。 - 特許庁

To provide a sound absorbing material and its manufacturing method in which cost is low and sound absorbing characteristics are made superior compared with conventional mineral fiber type or inorganic type sound absorbing materials, reduction in the sound absorbing performance caused by the use over a long period is easily recovered by washing the sound absorbing material with water or high pressure air or the like and effective use of marine industrial wastes is accomplished.例文帳に追加

従来の鉱物繊維系吸音材あるいは無機系吸音材に比べて、安価で吸音性に優れ、しかも長期間の使用による吸音性能の低下を、水洗、高圧空気等による洗浄により容易に回復できるとともに、水産系産業廃棄物の有効利用に寄与できる吸音材及びその製造方法を提供する。 - 特許庁

The cell differentiation-inducing method comprises a step for forming an aggregate of the cells by imparting a centrifugal force or a pressure to the undifferentiated cells in a state in which one or more kinds of the undifferentiated cells are inserted into the inner space of a hollow fiber composed of a permeable membrane, and a step for inducing the differentiation of the undifferentiated cells by culturing the cell aggregate.例文帳に追加

透過性膜からなる中空糸の内腔に１種または複数種の未分化細胞を入れた状態で、この未分化細胞に遠心力又は圧力をかけることにより細胞の凝集体を形成する工程と；この細胞凝集体を培養することにより未分化細胞を分化誘導する工程とを含む細胞分化誘導方法。 - 特許庁

To provide a producing method for optical fiber preform ingot and a producing device therefor which can make soot preform to sintered glass by holding air-tightness in a furnace, prevent eccentricity and curving due to contraction on the density change and prevent the deformation in the longitudinal direction due to own weight which is easily caused in accordance with a progress of transparent glass-forming.例文帳に追加

炉内の気密性を保持してスート母材を焼結ガラス化することができ、密度変化時の収縮による偏芯や湾曲を防止し、かつ透明ガラス化の進行にともなって生じやすい自重による長手方向の変形を防止することのできる光ファイバ母材インゴットの製造方法及び製造装置を提供する。 - 特許庁

This method comprises supplying a slurry containing a fiber having ≥550 ml Canadian standard freeness (CFS) to a mold having many small holes, removing the dispersion medium of the slurry through the small holes to accumulate small hole-unpassed ingredients and to obtain a molding and drying the molding to obtain the ink absorber.例文帳に追加

多数の小孔を有する成形型に、カナダ標準フリーネス（ＣＳＦ）が５５０ｍｌ以上の繊維を原料として含有するスラリーを供給し、小孔からスラリー分散媒体を除去することによって該成形型にスラリー中の小孔不通過成分を堆積させて成形物とし、その後乾燥したものをインク吸収体とする。 - 特許庁

This data transfer method performs data frame transfer according to the fiber channel protocol between a first storage controller and a second storage controller in the remote copy system provided with the first storage controller and the second storage controller which is connected to the first storage controller through a communication means to receive data from the first storage controller.例文帳に追加

第１の記憶制御装置と、第１の記憶制御装置に通信手段を介して接続され、第１の記憶制御装置からデータを受信する、第２の記憶制御装置を備えるリモートコピーシステムにおける、第１の記憶制御装置と第２の記憶制御装置との間で、ファイバチャネルプロトコルにしたがって、データフレームの転送を行うデータ転送方法である。 - 特許庁

In order to achieve the object, this apparatus for measuring optical rotation characteristic of a living body adopts a method of causing wavelength-turnable laser beam synchronized with pulses to enter the living body through a plane of polarization preserving optical fiber limited in its length so that the output light periodically changes in lateral circularly polarized light state.例文帳に追加

上記の目的を達成するために、本発明に係わる生体の旋光特性測定装置では、脈拍に同期した波長可変レーザ光をその出力光が左右円偏光状態が周期的に変化するように長さが限定された偏波面保存光ファイバを介して生体に入射させる方法を採用して課題を解決した。 - 特許庁

In the biomass pretreatment method, a cellulosic biomass which is derived from plants, such as paper mulberry or kenaf, having ≥70 mass% of a cellulose content in a drying state and preferably having the length of fiber bundle of ≥20 mm, is treated with an oxidizing agent such as sodium hypochlorite to oxidize and hydrophilize lignin in the biomass, and then is dissolved in a water phase to remove lignin from the biomass.例文帳に追加

例えば、コウゾやケナフのように、乾燥状態におけるセルロース含有量が７０質量％以上で、さらに好ましくは繊維束の長さが２０ｍｍ以上である植物由来のセルロース系バイオマスを、次亜塩素酸ナトリウムのような酸化剤でバイオマス中のリグニンを酸化して親水化し、水相に溶解させ、バイオマスからリグニンを除去する。 - 特許庁

To provide an ultrafine fiber nonwoven fabric which contains ultrafine fibers, is especially suitable as a sheet for washing skins, a wiping cloth for cleaning or catching fine dusts, a pressure sore-preventing base material, or a filter for removing fine dusts, has excellent shape retainability and excellent flexibility; and is excellent in touch with skins, and to provide a method for producing the same.例文帳に追加

極細繊維を含有した不織布に関し、特には皮膚洗浄用シート、微細な塵埃を清拭、捕捉するためのワイピングクロス、床ずれ防止基材、微細な塵埃を除去するためのフィルタとして好適な、保形性に優れ且つ柔軟性に優れるとともに、皮膚への触感に優れた極細繊維不織布、およびその製造方法を提供する。 - 特許庁

The antifouling fabric consisting mainly of a synthetic fiber is provided by attaching an anionic hydrophilic resin on its surface, and having ≤2 DE color difference between the colors of a non stain-attached part and stain-remaining part after one time washing as prescribed in the JIS L0217-103 by attaching the mud after 50 times repeated washings prescribed in the same method.例文帳に追加

主として合成繊維からなる布帛であって、アニオン性親水性樹脂が表面に付着されており、ＪＩＳ Ｌ０２１７−１０３法に規定される繰り返し洗濯５０回後に泥を付着させ、同法に規定される洗濯１回後の汚れ未付着部分と汚れ残り部分の色彩色差ＤＥが２以下である防汚性布帛。 - 特許庁

The method of producing the reinforced fiber preform includes a step of preparing a composition 12 including at least a first cylindrical part 21 and a second cylindrical part 22 in a seamless manner using the braider BR, and a step of forming a flange part 31 by deforming the first cylindrical part 21 and projecting the wall of the first cylindrical part 21 to the second cylindrical part 22.例文帳に追加

少なくとも第１筒状部２１と第２筒状部２２とを含む組成物１２を、ブレイダー装置ＢＲを用いて継ぎ目無く作製する工程と、第１筒状部２１を変形させ、第１筒状部２１の壁を第２筒状部２２に対して突出させてフランジ部３１を形成する工程と、を備える強化繊維プリフォームの作製方法とする。 - 特許庁

To allow transmission of a signal in MIMO method which is transmitted/received between a slave station terminal and an MIMO master station with less number of optical fiber circuits by subordinate modulation using less number of light sources than the number of antennas, for each uplink and downlink, between the master station in which an MIMO transmission/reception device is installed and an antenna station.例文帳に追加

ＭＩＭＯ送受信機が設置された親局とアンテナ局との間を上り・下りそれぞれアンテナ数より少ない数の光源を用い、従続変調を行うことで、少数の光ファイバ回線によって子局端末とＭＩＭＯ親局との間で送受信されるＭＩＭＯ方式の信号を伝送することができるようにする。 - 特許庁

There is provided the method for producing the leather-like sheet, including coating and drying a liquid obtained by foaming an aqueous polyurethane dispersion into a one and half to fourfold volume on at least one side of a substrate layer comprising a fiber-interlaced nonwoven fabric arbitrarily impregnated with a polyurethane to form a foamed coating layer, and then integrally laminating a polyurethane nonwoven fabric to the foamed coating layer.例文帳に追加

任意にポリウレタンが含浸された繊維絡合不織布からなる基体層の少なくとも一面に、ポリウレタン水分散液を１．５〜４倍に発泡させた液を塗布・乾燥して、発泡コート層を形成した後、該発泡コート層にポリウレタン不織布を積層一体化することを特徴とする銀付調皮革様シートの製造方法である。 - 特許庁

This method comprises forming through holes by a subulate needle with a predetermined space along the designed figure on the cloth and forming a feeling of full variety such as decoloring or napping by disarranging fiber condition around the through holes in a step of dying, washing or agitating in a liquid.例文帳に追加

布地に形成したい図案の形状に沿って、キリ状針で形成した貫通穴を所定間隔で形成し、次に、該布を染色、洗濯あるいは液体内での攪拌工程により貫通孔周辺の繊維状態を乱すことにより、脱染色あるいは毛羽立ち等の変化に富んだ風合いを形成するあるいはこの方法で製造された布地。 - 特許庁

The method for producing the protective sleeve having an opening part continuing in the longitudinal direction is obtained by braiding a fiber yarn by a braider to provide a braided sleeve, cutting up the braided sleeve in the longitudinal direction to afford the opening part, forming the diameter-reduced shape by overlapping the opening parts and holding the shape having the reduced diameter by subjecting the product to heat treatment.例文帳に追加

長さ方向に連続した開口部を有する保護スリーブについて、製紐機により繊維糸を編組して編組スリーブとし、該編組スリーブを長さ方向に切裂いて上記開口部を設け、該開口部を重ね合わせて上記保護スリーブを縮径した形状とし、熱処理を加えて縮径した形状を保持する保護スリーブの製造方法。 - 特許庁

To provide a method for producing a nonwoven fabric by which both of the formation of a fiber web into an uneven and/or hole-opened shape, and the formation of the nonwoven fabric are carried out simultaneously, and the simplification or the like of the production apparatus can be achieved because easily treatable air is used and the scattering of fibers is effectively prevented, and to provide the production apparatus.例文帳に追加

繊維ウエブに対する凹凸及び／又は開孔形状の賦形と不織布化とを同時に行うことができると共に、取り扱いの楽な空気を用いることや繊維の飛び散りを効果的に抑制することから、製造装置等の簡易化等を図ることもできる不織布の製造装置及び製造装置を提供すること。 - 特許庁

In this method, as the frictional resistance between the staple fibers and a cutting blade is reduced by oiling the filament bundles, the staple fibers are facilitated to discharge, and fiber fusing can be suppressed by forming coating film between the filaments, therefore the objective staple fibers having the above-mentioned advantages can be produced in large quantities in high productivity at low cost.例文帳に追加

この製造方法は、長繊維束に油剤を付与することにより、短繊維と切断刃との摩擦抵抗を減少させることで短繊維を排出しやすくし、また長繊維間に皮膜を形成させて切断による融着も抑制できるため、融着がなく分散性に優れる短繊維を大量かつ安価に生産性良く製造することができる。 - 特許庁

Copper or silver having a high antimicrobial effect is adhered in a range of 10-30 μg/cm^2 on at least one surface of a resin fiber screen made of a synthetic resin by a vapor deposition method, and stainless steel is adhered thereafter in a range of 8-24 μg/cm^2 on top of it.例文帳に追加

合成繊維からなる樹脂繊維網の少なくとも一方の面に、気相堆積法に従い、高い抗菌作用を有する銅または銀を１０μｇ／ｃｍ^２〜３０μｇ／ｃｍ^２の範囲で付着せしめ、続いてその上から、ステンレスを８μｇ／ｃｍ^２〜２４μｇ／ｃｍ^２の範囲で付着せしめることによって達成される。 - 特許庁

To provide a composite textured yarn capable of providing woven or knitted products having proper bulky feeling, soft touch and proper glossy feeling, excellent in sufficient fiber form stability and having silky span-like feeling by imparting crimps, loops and twists to the composite textured yarn; to provide a production method of the textured yarn; and to provide woven or knitted products using the textured yarn.例文帳に追加

複合加工糸に捲縮とループ、及び撚りを付与することにより、適度なフクラミ感とソフトなタッチ及び適度な光沢感を有し、かつ十分な糸形態安定性に優れ、シルキースパン調風合いを有する織編物が提供できる複合加工糸と、その製造方法、並びにその加工糸を使った織編物を提供する。 - 特許庁

To provide a cleaning method effective for the cleaning of stains around ejection nozzles of a spinneret caused by kneeling phenomenon in the conjugated spinning of polymers having intrinsic viscosity difference and enabling the increase in cleaning interval, elongation of continuous work period of the spinneret face and the improvement of the process stability of the produced fiber in the following steps.例文帳に追加

極限粘度差のあるポリマーを複合して紡糸する際の、ニーリング現象による口金汚れ吐出細孔周囲の汚れに対する有効な洗浄方法を提供するものであり、清掃間隔の延長および、口金面連続使用時間の延長、紡糸した繊維の後工程での工程安定性の向上が可能となる。 - 特許庁

This invention is a manufacturing method of the polysulfone-based hollow fiber membrane characterized by maintaining at 70°C or less up to supplying a provided spinning solution to a spinning process, by preparing the spinning solution by dissolving at least three components composed of polyvinyl pyrolidone, a polysulfone-based high polymer and a common solvent of these at 70°C or less in an inert gas atmosphere.例文帳に追加

本発明は、ポリビニルピロリドン、ポリスルホン系高分子およびそれらの共通溶媒からなる少なくとも３成分を不活性ガス雰囲気下、７０℃以下で溶解して紡糸溶液を調製し、得られた紡糸溶液を紡糸工程に供給するまでの間７０℃以下に維持することを特徴とするポリスルホン系中空糸膜の製造方法である。 - 特許庁

To provide a method for producing a preform for a fiber-reinforced composite material in a complex three-dimensional shape to include a T-shaped structure which can easily revise the preform by peeling it when it can not be joined to a proper position in a production process without affecting the strength and durability of a finally obtained product.例文帳に追加

Ｔ字構造を含むような複雑な３次元形状の繊維強化複合材用プリフォームを、最終的に得られる製品の強度、耐久性に影響を及ぼすことなく、しかも製造過程において適切な位置に接合できなかった場合には剥がして、容易に修正できるプリフォームの製造方法及びプリフォームを提供する。 - 特許庁

The method for manufacturing the optical fiber assembly 1 includes: filling the inside of a molding die with optical fibers in which clad 4 formed of a thermoplastic resin is arranged in the periphery of cores 3 formed of at least a thermoplastic resin, in a plurality of bundle forms; and then joining the clad of the plurality of the optical fibers to each other by heating the molding die.例文帳に追加

少なくとも１つの熱可塑性樹脂からなるコア３の周囲に熱可塑性樹脂からなるクラッド４が配置されてなる光ファイバを成形型内に複数束状に充填したのち、前記成形型を加熱することにより前記複数の光ファイバのクラッドを互いに接合することを特徴とする光ファイバ集合体１の製造方法。 - 特許庁

Also the method for producing such synthetic leather like material is provided by needle-punching a web consisting of the synthetic fiber to form the non-woven fabric sheet, then processing at least one side of the nonwoven fabric by heating and compressing to form the grain surface skin film consisting of at least one kind selected from the sea component and the bonding component of the conjugate fibers.例文帳に追加

また、かかる合成皮革状物の製造方法は、該複合繊維からなるウエブをニードルパンチングして不織布シートを形成した後、該不織布シートの少なくとも片側を、加熱加圧加工して、該複合繊維の海成分および結合成分から選ばれた少なくとも１種で構成された銀面皮膜を形成することを特徴とするものである。 - 特許庁

In the method for manufacturing the hollow fiber type blood cleaning membrane for discharging a spinning dope from a nozzle comprising a tube-in orifice with a hollow inner liquid, the nozzle having a length/diameter ratio of 0.5-2.5 is used to perform the spinning under the condition that the draft ratio of a falling part is not more than 2.0.例文帳に追加

紡糸原液をチューブインオリフィスよりなる紡糸口金より中空内液とともに吐出して紡糸する中空糸型血液浄化膜の製造方法であって、中空内液吐出部の長さ／径が０．５以上２．５以下である紡糸口金を使用して、落下部ドラフト率を２．０以下で紡糸することを特徴とする中空糸型血液浄化膜の製造方法。 - 特許庁

To provide a method for manufacturing a polyurethane fiber having excellent resistances to light and nitrogen oxide high heat-settability, fitting ability, a good appearance and excellent wearability, from a transparent polyurethane resin solution having excellent viscosity stability, without discoloring and viscosity increase, and causing no heat-degradation.例文帳に追加

透明で粘度安定性が良く、着色や増粘がなく、熱による解重合を起こさないポリウレタン樹脂溶液から耐光性、耐酸化窒素性などが高く、またかつヒートセット性が高い利点を有し、フィット性、良好な外観品位、優れた着用感が得られるポリウレタン繊維を得ることが可能なポリウレタン繊維の製造方法を提供する。 - 特許庁

This method comprises forming a hydrophilic film made from a monomer having radically polymerizable group at both ends, one end or on side chain of a main chain composed mainly of a polyalkylene oxide on a synthetic fiber fabric, to conduct dyeing and moreover to coat the outermost layer with a copolymer having a perfluoroalkyl group-containing acrylate, a perfluoroalkyl group-containing methacrylate or a comonomer therefor as at least one component.例文帳に追加

合成繊維布帛に、ポリアルキレンオキサイドを主体とする主鎖の両末端、片末端または主鎖の側鎖にラジカル重合性基を有する単量体からなる親水性皮膜を形成した後、染色し、さらに、パーフルオロアルキル基含有アクリレート、メタクリレート又はこれらに共重合し得る化合物との共重合体を最外層に被覆する。 - 特許庁

To provide an ultrafine fiber composite non-woven fabric which is produced by laminating and integrating ultrafine fibers with a spun-bonded non-woven fabric, is especially suitable as a wiping cloth for wiping and catching fine dusts or as a filter for removing fine dusts, is excellent in flexibility and is excellent in shape retainability, and to provide a method for producing the same.例文帳に追加

極細繊維とスパンボンド不織布とが積層一体化した複合不織布に関し、特には、微細な塵埃を清拭、捕捉するためのワイピングクロスとして好適な、あるいは微細な塵埃を除去するためのフィルタとして好適な、柔軟性に優れるとともに保形性に優れた極細繊維複合不織布、およびその製造方法を提供する。 - 特許庁

To provide a method for increasing stability without a large change of the temperature-sensitive point of the temperature-sensitive gel and can inhibit the secondary coagulation in the temperature-sensitive gel dispersion that is useful as a base material for a paint thickener, metal plating, a lubricant agent for cosmetics, a migration inhibitor, a fiber modification agent and a water-proofing agent for a submarine cable.例文帳に追加

塗料用増粘剤、金属メッキ、化粧品用潤滑剤、マイグレーション防止剤、繊維改質剤、海底ケーブル止水剤等の基材として有用な感温性ゲル分散液の、感温性ゲルの感温点を大きく変化させることなく安定性が向上し２次凝集が抑制できる安定化方法を提供する。 - 特許庁

This sort of a carbon electrode base can be manufactured appropriately by a method having a process for producing the carbon short fiber, a process for impregnating a thermosetting resin, a process for performing heating pressing, and a process for baking at a temperature of 1,200°C or higher in a nitrogen atmosphere while a porous plate is provided at the lower side of a steel plate used for the production.例文帳に追加

このような炭素電極基材は、抄造に用いる網板の下側に多孔板を設置した状態で、炭素短繊維を抄造する工程と、熱硬化性樹脂を含浸する工程と、加熱プレスする工程と、窒素雰囲気下１２００℃以上の温度で焼成する工程とを有する方法により好適に製造できる。 - 特許庁