To provide a porous cell support with a thickness of 2 mm or more, cells are easily seeded in the whole of the support, eliminating any possibility of applying a large force to the cells, and substantially accurately grasping the amount of cells in the support, and to provide a production method thereof.例文帳に追加

細胞を支持体の全体に容易に播種することができ、細胞に大きな力が加わることがなく、支持体内の細胞の量も略正確に把握することが可能な厚さ２ｍｍ以上の多孔質細胞支持体とその製造方法を提供する。 - 特許庁

In the gold ultra-fine particle carrier, an inorganic oxide having a specific surface area of 30 m^2/g or less according to BET method is used as the carrier and the carrier is carried with 3 pts.wt. or more of gold ultra-fine particles having an average particle diameter of 25 mm or less based on 100 pts.wt. of the inorganic oxides.例文帳に追加

ＢＥＴ法による比表面積が３０ｍ^2／ｇ以下の無機酸化物を担体として、該無機酸化物１００重量部に対して平均粒子径２５ｎｍ以下の金超微粒子が３重量部以上担持されてなる金超微粒子担持体。 - 特許庁

In a method for producing the filter medium, the clearance A of an escape part in a mold for the filter unit is 80-115% of the thickness of the filter medium, the clearance B of a grip part is 25-45% of the thickness of the filter medium, and the distance C to the grip part is 0.5-5 mm.例文帳に追加

フィルターユニットの金型における逃がし部のクリアランスＡが濾材厚みに対して８０〜１１５%、掴み部のクリアランスＢが濾材厚みに対して２５〜４５%，且つ，掴み部の距離Ｃが０．５〜５ｍｍであることを特徴とするフィルターユニットの製造法。 - 特許庁

This moisture-permeable and water-proofed cloth has a moisture- permeable and waterproof film applied to one face of a fabric having a cover factor of 1,850 or less and the thickness of the film 0.30 mm or less and the moisture permeability by JIS L 1099 (B-1) method of 25,000 g/m^2/24 hrs or more.例文帳に追加

カバーファクターが１８５０以下の織物の片面に透湿防水性皮膜を有し、厚さが０．３０ｍｍ以下、ＪＩＳ Ｌ １０９９（Ｂ−１）法の透湿度が２５０００ｇ／ｍ^2・２４時間以上であることを特徴とする透湿防水加工布帛。 - 特許庁

The polycarbonate resin film which has the thickness of from 0.05 to 0.5 mm and the thickness irregularities ΔTR of the film in the film extruding direction measured by the method mentioned in the main text, satisfies the following equation (1) 0.1≤ΔTR≤0.7 (1) [wherein ΔTR is the thickness irregularities of the film (μm)].例文帳に追加

ポリカーボネート樹脂フィルムの厚みが０．０５〜０．５ｍｍで、本文記載の方法で測定されたフィルムの押出方向の厚薄ムラΔＴ_Rが下記式（１） ０．１≦ΔＴ_R≦０．７ …（１） ［式中、ΔＴ_Rはフィルムの厚薄ムラ（μｍ）］を満足するポリカーボネート樹脂フィルム。 - 特許庁

The manufacturing method of the inorganic molding has at least processes of: forming granules having the average grain size of 0.5-25 mm by adding water to a powdery inorganic molding material; and press molding the granules by being charged in a molding die.例文帳に追加

少なくとも、粉体状の無機成形材料に水を添加して、平均粒径０．５〜２５ｍｍの造粒物を生成する工程と、該造粒物を成形型内に充填してプレス成形する工程と、を有することを特徴とする無機質成形体の製造方法。 - 特許庁

The cutting-resistant fabric is obtained by applying a silane-based coating agent to at least the surface of a fabric composed of a synthetic fiber and curing/solidifying the silane-based coating agent by action of a catalyst and has ≤15,000 mgf bending resistance (by Gurley method) per mm thickness.例文帳に追加

合成繊維から構成された布帛の少なくとも表面に、シラン系コート剤が塗布され、かつ該シラン系コート剤が触媒の作用で硬化・固化されており、かつ該布帛の厚さ１ｍｍ当りの剛軟度（ガーレ法）が１５，０００ｍｇｆ以下である耐切創性布帛。 - 特許庁

To provide a porous cell scaffold of a 2 mm or more thickness and a production method thereof, easily seeding cells in its scaffold without applying any large force to the cells, and substantially accurately obtaining the amount of cells in the scaffold as well in seeding.例文帳に追加

細胞に大きな力が加えることなく細胞を支持体内全体に容易に播種することができ、播種時の支持体内の細胞の量も略正確に把握することが可能な厚さ２ｍｍ以上の多孔質細胞支持体とその製造方法を提供する。 - 特許庁

The correction method contains a correction buffing process Y3 wherein the weight unbalance of the tire T1 to which a reference buffing treatment has been executed is measured and the relief mark MA or MB which is on its important-point position K or closest to the important-point position K is buffed at a polishing amount of 0 to 5.0 mm.例文帳に追加

基準バフ処理されたタイヤＴ１の重量アンバランスを測定し、その重点位置Ｋ上又は重点位置Ｋに最も近い浮出しマークＭＡ又はＭＢを、０〜５．０ｍｍの研磨量Ｄでバフ掛けする修正バフ工程Ｙ３を含む。 - 特許庁

In the continuous casting method for the molten steel, in which the circular flow along the inner wall of the mold 14 is given by applying the electromagnetic stirring to the molten steel 11 in the mold 14, whirling flow is given from a meniscus 21 to the molten steel 11 at a position where thickness of the solidified shell is 20 mm.例文帳に追加

鋳型１４内の溶鋼１１を電磁攪拌して、鋳型１４の内壁に沿った旋回流を付与する溶鋼の連続鋳造方法において、旋回流をメニスカス２１から凝固シェル厚みが２０ｍｍの位置にある溶鋼１１に付与する。 - 特許庁

To provide a target of high-purity nickel or a nickel alloy for magnetron sputtering, which gives excellent uniformity (uniformity of film thickness) to a film and facilitates the ignition (ignition) of plasma even in a manufacturing process with the use of a wafer of 300 mm, and to provide a production method therefor.例文帳に追加

３００ｍｍウエハを用いた製造プロセスにおいても、膜のユニフォーミティ（膜厚の均一性）とプラズマのイグニッション（点弧）性を良好にすることができるマグネトロンスパッタリング用高純度ニッケル又はニッケル合金ターゲット及びその製造方法を提供する。 - 特許庁

To provide a cold tandem rolling method and cold tandem rolling equipment which enable a metallic strip even having a proof stress of 390 N/mm^2 or more to be stably rolled and an original sheet even having surface flaw to be rolled without causing problem due to the surface flaw after rolled.例文帳に追加

耐力が３９０Ｎ／ｍｍ^２以上の金属ストリップでも、安定した圧延および熱延原板の表面疵があっても圧延後は問題とならない圧延を可能にする、冷間タンデム圧延方法および冷間タンデム圧延設備を提供する。 - 特許庁

To provide a method for controlling a rolling shape in a continuous cold rolling mill, which accurately controls a malformation (wavy edges) caused at the tip end of a steel strip, when rolling a thin steel strip with a thickness of 0.3 mm or less by a continuous cold rolling mill.例文帳に追加

連続式冷間圧延機によって厚さ０．３ｍｍ以下の薄物鋼帯を圧延するに際して、鋼帯先端部の形状不良（耳伸び）を的確に抑止することができる連続式冷間圧延機における圧延形状制御方法を提供する。 - 特許庁

The tube is superior in flexibility and permeation resistance to gasoline, alcohol, or a mixed fuel of these, it has a meta-xylene base including polyamide resin layer 2 with a thickness of ≤0.3 mm and a polyolefinic resin layer 3, and it is formed by a simultaneous extrusion molding method.例文帳に追加

ガソリン、アルコール及びこれらの混合燃料に対する耐透過性、並びに柔軟性に優れているチューブであって、厚みが０．３mm以下のメタキシリレン基含有ポリアミド樹脂層２と、ポリオレフィン系樹脂層３とを有し、同時押出成形法により形成されている。 - 特許庁

The method includes supplying an ozone-containing gas of a 5-300 vol.ppm ozone concentration to water as bubbles of a ≤10 mm average bubble diameter and treating shellfishes with water having a 0.01-5 vol.% ozone-containing gas void rate in the water.例文帳に追加

本発明は、オゾン濃度５〜３００ｖｏｌｐｐｍのオゾン含有ガスを平均気泡径が１０ｍｍ以下の気泡として水に供給し、前記オゾン含有ガスの水中におけるボイド率を０．０１〜５体積％とした水で、貝類を処理することを特徴とする。 - 特許庁

In the method by which direct bilirubin in a sample is measured from the optical change of the sample by acting bilirubin oxidase to the sample, 100-800 mM potassium ions are made to coexist in the measurement.例文帳に追加

本発明は、試料にビリルビンオキシダーゼを作用させ、該試料の光学的変化により試料中の直接型ビリルビンを測定する方法において、１００ｍＭ〜８００ｍＭのカリウムイオンを共存させておくことを特徴とする直接型ビリルビンの測定方法を提供する。 - 特許庁

In its production method, a molten steel is solidified into a slab with a thickness of ≥50 mm by casting, shearing strain is imparted thereto in the hot rolling temperature range of 500 to 850°C, cold rolling is performed as the rolled structure is left, and recrystallization annealing is performed.例文帳に追加

その製法は、溶鋼を鋳造で厚さ５０ｍｍ以上の鋼片に凝固させ、圧延温度５００℃以上８５０℃以下の熱間温度域で剪断歪を付与し、この圧延組織を残存させたまま冷間圧延を行った後、再結晶焼鈍を行う。 - 特許庁

To provide a polishing cloth regenerating method which can reutilize a polishing cloth by improving again the deteriorated polishing property of the cloth surface of the polishing cloth, without changing with a new polishing cloth, and can use as the countermeasure of a polishing device for a large diameter wafer with the diameter more than 300 mm.例文帳に追加

新規な研磨布に張り替えなくても、低下していた研磨布の布表面の研磨性を再び高めて、研磨布を再利用することができ、３００ｍｍ以上の大口径ウェーハ用の研磨装置の対策にもなる研磨布再生方法を提供する。 - 特許庁

To provide a method for producing an alloying hot dip galvannealed steel sheet useful for an automobile steel sheet or the like, having a high strength satisfying a tensile strength (TS) in a class of 980 N/mm^2 and a high ductility satisfying an elongation (El) of ≥15%, and further having a sound plating quality.例文帳に追加

自動車用鋼板等として有用な、引張り強さ（ＴＳ）９８０Ｎ／ｍｍ^２級の高強度と伸び（Ｅｌ）１５％以上の高延性を具備すると共に健全なめっき品質を備えた合金化溶融亜鉛鋼板の製造方法を提供する。 - 特許庁

The method for producing a monofilament is to carry out a neck drawing to bring the monofilament to be a drawn filament having 0.0012-300 mm^2 cross sectional area by passing a preheated undrawn monofilament through a dice under drawing in drawing the undrawn monofilament after spinning.例文帳に追加

紡糸後の未延伸モノフィラメントを延伸するに際し、予熱された未延伸モノフィラメントを伸長しつつダイスを通過させてネック延伸することにより、断面積が０．００１２〜３００ｍｍ^２の延伸モノフィラメントとなすことを特徴とするモノフィラメントの製造方法。 - 特許庁

In the method for producing an inorganic solidified body by using ash yielded by incinerating municipal waste as the main material, smelting slag as a composition-adjusting agent is added to the main material; then, the mixture is crushed, granulated into granules with a granule size of about 5-20 mm, dried, and fired in a rotary kiln.例文帳に追加

都市ゴミを焼却して得られる灰を主原料とする無機質固化体の製造方法において、前記主原料に組成調整材として製錬スラグを添加し、粉砕後５〜２０ｍｍ程度に造粒し、乾燥させてロータリーキルンで焼成する。 - 特許庁

In this process, important innovative technologies, clearly different from those in previous train-cars, as described in the following, came to be practically used only during several years from 1953: The new train-car base supporting high-speeds in addition to 'the Cardan driving method,' which enabled the suppression of vibration and contributed to making passengers feel more comfortable and to enabling high-speed operations, 'all-metal light body train-cars,' which enabled stress to be distributed to side plates and ceilings as well as floor chassis, 'the method of electrifying every train-car,' in which every train-car was equipped with an electric motor to increase acceleration performances, 'the electromagnetic straight brake mechanism,' which provided quick response abilities and allowed it to be handled easily, and 'the 1C8M method (MM unit method),' in which a control unit was shared by two electric power train-cars, contributing to reducing cost and to making the car bodies lighter. 例文帳に追加

この過程で、振動を抑制し、乗り心地改善と高速運転に資する「カルダン駆動方式」と高速対応の新型台車、床面シャーシだけでなく側板や天井にも応力を分散させた「全金属製軽量車体」、全車両にモーターを搭載して加速力を高める「全電動車方式」、反応速度が速い上に取り扱いが容易な「電磁直通ブレーキ機構」、制御装置1台を2両の電動車で共用して軽量化やコストダウンを実現する「1C8M方式（MMユニット方式）」など、それ以前の電車とは一線を画する重要な革新的技術が、1953年からわずか数年の間に実用化されて普及した。 - Wikipedia日英京都関連文書対訳コーパス

This method for manufacturing the toner for electrophotography is the method for obtaining the toner for electrophotography by crashing a chip-like mixture melted and hardened after a mixing process which is obtained by blending at least resin, a pigment and an electric charge control agent, and the micro Vickers hardness of the chip-like mixture is made to be 5 kg/mm^2 characteristically.例文帳に追加

本発明に係る電子写真用トナーの製造方法は、少なくとも樹脂、顔料、電荷制御剤を配合してなる、混練工程後の溶融固化したチップ状混練物を粉砕することにより電子写真用トナーを得る方法であって、前記チップ状混練物のマイクロビッカース硬度を５ｋｇ／ｍｍ^2 以上とすることを特徴とする。 - 特許庁

To provide a method for producing a plastic lens or an optical waveguide which can provide a cured material high in transparency even when its thickness is at least 0.2 mm by an optical imprint method, maintain a high throughput without lowering the illuminance of an exposure machine, sufficiently carry out curing even when a polydimethylsiloxane resin having oxygen permeability is used for a mold material, and can reduce the deterioration of a mold.例文帳に追加

光インプリント法で0.2mm以上の厚みでも透明性の高い硬化物が得られ、露光機の照度を落とすことがなく高スループットを維持でき、酸素透過性のあるポリジメチルシロキサン樹脂をモールド材料に用いた場合でも、十分に硬化出来、モールドの劣化を少なくすることができるプラスチックレンズ又は光導波路の製造方法を提供する。 - 特許庁

To provide a roll-like printing blanket which can precisely print an ink pattern on an uneven surface for printing with 5 to 16 mm in elevation difference, a manufacturing method of a printed body including the surface to be printed and the ink pattern precisely printed thereon, and the printed body manufactured by the manufacturing method.例文帳に追加

５〜１６ｍｍの高低差がある凹凸を有する被印刷面に対し、インキパターンを精密に印刷することのできるロール状印刷用ブランケット、上記被印刷面と、上記被印刷面に精密に印刷されたインキパターンとを備える印刷体の製造方法、およびこの印刷体の製造方法により製造される印刷体を提供すること。 - 特許庁

A constant-volume reinforcing fiber supply method and a short- fiber mixed reinforced earth spray work method characterized by using the slivers of short fibers temporarily twisted and wounded into a cheese form, and having less than 100 dtex of average filament denier, 50-200 mm of average fiber length and 10,000 - two million dtex of total denier.例文帳に追加

仮撚りをかけて、チーズ状に巻き取った、平均単繊維繊度１００ｄｔｅｘ以下、平均繊維長５０〜２００ｍｍ、総繊度１万〜２００万ｄｔｅｘで構成される短繊維のスライバーを使用することを特徴とする補強繊維の定量供給方法および短繊維混合土砂の吹き付け補強土工法。 - 特許庁

In a lubrication treatment method being a method of applying water-soluble lubricant to the surface of the work by dipping the work 2 into the water-soluble lubricant, when the work 2 is pulled up from the water-soluble lubricant after being dipped into the water-soluble lubricant in a lubricant applying tank 11, this pulling-up speed is set to ≤20 mm/sec.例文帳に追加

本発明の潤滑処理は、ワーク２を水溶性潤滑剤に浸漬させることで、ワーク表面に水溶性潤滑剤を塗布する方法であり、潤滑剤塗布槽１１の水溶性潤滑剤にワーク２を浸漬させた後、水溶性潤滑剤からワーク２を引き上げる際に、その引き上げ速度を２０ｍｍ／ｓｅｃ以下に設定している。 - 特許庁

The production method of a silicon single crystal 1 by Czochralski method by doping with carbon is disclosed, wherein the crystal 1 is grown by controlling the difference between an average growing rate of the crystal center portion 15 within a plane perpendicular to the crystal growth direction and an average growing rate of the crystal peripheral portion 16 to be within ±0.1 mm/min during growing the crystal.例文帳に追加

チョクラルスキー法により炭素をドープしてシリコン単結晶１を製造する方法において、結晶成長時に、結晶成長方向に対して垂直面内の結晶中心部１５が成長する平均速度と結晶周辺部１６が成長する平均速度との差を±０．１ｍｍ／ｍｉｎ以内となるようにして結晶１を成長する。 - 特許庁

This radiological image conversion panel having a stimulable phosphor layer on a support has a characteristic wherein the stimulable phosphor layer is formed by a vapor-phase method (namely, a vapor-phase deposition method) so as to have the film thickness of 50μm -1 mm and a protection layer having a thermoplastic resin is formed on the phosphor layer.例文帳に追加

支持体上に輝尽性蛍光体層を有する放射線画像変換パネルにおいて、輝尽性蛍光体層が気相法（気相堆積法ともいう）により５０μｍ〜１ｍｍの膜厚を有するように形成され、該蛍光体層上に熱硬化性樹脂を有する保護層が形成されることを特徴とする放射線像変換パネル。 - 特許庁

To provide a growing apparatus and method, by which a larger-diameter silicon single crystal ingot larger than 200 mm as well as a middle or small diameter silicon single crystal ingot having a uniform oxygen concentration in a longitudinal direction can be produced based on a Czochralski method and the flower phenomenon generated on the growth of a single crystal can be completely controlled; and to provide wafers produced from the ingot.例文帳に追加

チョコラルスキCZ法において、中、小口径だけでなく、200mm以上の大口径のシリコン単結晶インゴットの長手方向に酸素濃度が均一で、また単結晶の成長時に発生するフラワ現象を完全に制御することができる成長装置、成長方法及びそのインゴットから製造されたウエハを提供する。 - 特許庁

This pneumatic tire is characterized by projecting at least a part of the transponder coated with resin from the surface of the tire and arranging the transponder in a tire bead part within 100 mm at a tire radial outside from a rim flange height and this method is the manufacturing method for the pneumatic tire provided with projections fitted into recesses or through holes on a metallic mold.例文帳に追加

樹脂で被覆されたトランスポンダの少なくとも一部分をタイヤ表面から突出し、しかもリムフランジ高さからタイヤ半径方向外側に１００ｍｍ以内のタイヤビード部に配置したことを特徴とする空気入りタイヤ及び窪み又は貫通穴に嵌合する突起を金型に設けた空気入りタイヤの製造方法。 - 特許庁

To provide a method for producing a semiconductor single crystal by an FZ method where the degradation of a crystal shape is suppressed, resistivity distribution in a plane in a diameter direction is controlled and particularly the variation of the resistivity in the plane is reduced even if the semiconductor single crystal has a specially large diameter of 150 mm or more and to provide an apparatus for producing the semiconductor single crystal capable of performing the producing method.例文帳に追加

特に１５０ｍｍ以上の大直径の半導体単結晶でも、結晶形状の悪化が抑えられ、径方向の面内抵抗率分布を制御することができ、特には面内での抵抗率のバラツキを低減することが可能なＦＺ法による半導体単結晶の製造方法、およびこのような製造方法を実施可能な半導体単結晶の製造装置を提供する。 - 特許庁

The production method of a cell for an electrochromic mirror includes a process of applying an epoxy sealing agent containing beads in predetermined position of the edge on at least one conductive substrate of two conductive substrates by a dispensing method or screen printing method and a process of stacking the two conductive substrates and laminating the substrates with the sealing width by a sealing agent controlled to ≤2 mm.例文帳に追加

二枚の導電性基板の少なくとも一方の導電性基板の面上周縁部の所定の位置にディスペンス方式あるいはスクリーン印刷方式によってビーズを含有するエポキシ系シール剤を塗布する工程、及び二枚の導電性基板を重ね合わせ、該シール剤によるシール幅が２ｍｍ以下となるように該基板同士を貼り合せる工程を含むことを特徴とするエレクトロクロミックミラー用セルの製造方法。 - 特許庁

To provide a web thin wide flange shape in which, even if controlled rolling is not performed, the wall thickness of a web is ≤20 mm and a difference in the wall thickness between the web and a flange is also wide, and which has high strength and also has an excellent shape, and to provide its production method.例文帳に追加

本発明は、制御圧延を実施しなくても、ウエブ肉厚が２０ｍｍ以下で、且つウェブとフランジとの肉厚差が大きく、高強度で、且つ形状が優れたウェブ薄肉Ｈ形鋼を提供すると共に、合わせてその製造方法をも提供することを目的としている。 - 特許庁

To provide an excellent embossed carrier tape which is preventive from generation of flow marks by a calendar forming method, excellent in smoothness and thickness accuracy of a surface, capable of using a desirable sheet of thickness between 50 μm to 1.2 mm, and capable of satisfying various physical property levels necessary for the embossed carrier tape.例文帳に追加

カレンダー成形法により、フローマークの発生を防止し、表面の平滑性や厚み精度に優れ、厚さ５０μｍ〜１．２ｍｍの範囲の望ましいシートを用いることができるとともに、エンボスキャリアテープとして必要な各種物性レベルを満足できる優れたエンボスキャリアテープを提供できる。 - 特許庁

To provide a stable method for producing a CNF (carbon nanofiber) aggregate suppressing a mixture of impurities such as graphite particles and catalyst metal, stably growing up to a height equal to or more than 10 mm from a substrate, with excellent reproducibility, and having a bulk density equal to or more than 0.08 g/cm^3.例文帳に追加

黒鉛粒子および触媒金属等の不純物の混入を抑制するとともに、安定して再現性よく基板から１０ｍｍ以上の高さに成長し、かつ０．０８ｇ／ｃｍ^3以上の嵩密度を有するＣＮＦ集合体の安定した製造方法の提供。 - 特許庁

In the treatment method of hydrogen chloride-containing gas, powder coke with particle sizes of 3-10 mm is added to and mixed with waste plastic containing a vinyl chloride resin in a ratio of 1:1-3:1 with respect to the waste plastic and the resulting mixture is subjected to dry distillation in a dry distillation furnace.例文帳に追加

前記乾留炉における塩化ビニル樹脂を含む廃プラスチックの乾留を、前記廃プラスチックに対し、粒径３ｍｍ〜１０ｍｍの粉コークスを１：１〜３：１の割合で添加混合し、この混合物を、前記乾留炉において不活性ガス雰囲気下で乾留することにより行う。 - 特許庁

This method is alternatively performed by granulating raw materials beforehand, which contain fuel with free carbon of 80 mass%, and a raw material with free carbon 5 mass % to 70 mass %, and with grains sizes of 1 mm or less 50 mass% or more in ratio, and employing the obtained grains for a part of a raw material for sintering.例文帳に追加

あるいは、フリーカーボン含有量80質量％以上の燃料とフリーカーボン含有量５質量％以上かつ70質量％以下で粒径−１mm比率50質量％以上の原料を予め造粒し、得られた造粒物を焼結原料の一部として使用する。 - 特許庁

In the seamless metal tube manufacturing method for obtaining a seamless metal tube by extruding a heated billet 16 from a space between a die 12 and a mandrel 13, a die having the bearing length set in a range of 6-11 mm is used for the die 12.例文帳に追加

この発明の継目無金属管の製造方法は、ダイス１２とマンドレル１３の隙間から加熱ビレット１６を押出して継目無金属管を得る製造方法において、前記ダイス１２として、ベアリング長さが６〜１１ｍｍの範囲に設定されたダイスを用いることを特徴とする。 - 特許庁

This method for producing the polypropylene terephthalate fiber is characterized in that the distance L from the spinneret surface to a cooling device is 50-200 mm and the interior of a quench stack just under the spinneret is an air atmosphere kept at 30-80°C dew point when melt spinning of the polypropylene terephthalate fiber is carried out.例文帳に追加

ポリプロピレンテレフタレート繊維を溶融紡糸するに際して、口金面から冷却装置までの距離Ｌを５０〜２００ｍｍとし、かつ口金直下の紡糸筒内を露点３０〜８０℃に保った空気雰囲気とすることを特徴とするポリプロピレンテレフタレート繊維の製造方法。 - 特許庁

The method is for mark engraving on a transmission belt having a mark, and the mark 10 whose depth is 0.1 to 1 mm is engraved by irradiating one side or both sides of the outermost side faces 9 of the belt with a laser beam 21 while adjusting the reflection angle by at least one scan mirror 24.例文帳に追加

マークを設けた伝動ベルトのマーク刻印方法であり、レーザ光２１を少なくとも１つのスキャンミラー２４によって反射角度を調節しながらベルト最外側面９の一方もしくは両方に照射して深さ０．１〜１ｍｍのマーク１０を刻印する。 - 特許庁

The method for preparation of cellulose acylate solution comprises dissolution of cellulose acylate particles having 22-43° of angle of repose, 0.30-0.75 g/cm^3 of bulk density and having ≤3 mass% of particles with ≥1.7 mm of particle diameter.例文帳に追加

安息角２２度以上４３度以下であり、嵩密度０．３０ｇ/cm^３以上０．７５g/cm３以下であり、粒径１．７ｍｍより大きい粒子の質量割合が３％以下であるセルロースアシレート粒子を有機溶媒に溶解することを特徴とするセルロースアシレート溶液の調製方法。 - 特許庁

To provide a method for measuring phase transition conditions such as a phase transition temperature and a measuring apparatus therefor, by which a measurement can be carried out with a sample having a thickness of around 1 μm and a size of around 1 mm, and even with a plurality of samples simultaneously.例文帳に追加

本発明は、相転移する試料は厚さ１μｍ程度、大きさ１ｍｍ角程度でも十分であり、さらには複数個の試料を同時に測定することもできる、相転移温度等の相転移条件の測定方法ならびにそのための測定装置を提供する。 - 特許庁

To prevent the waving of a polymer solution and the generation of a wind pattern on the surface of the solution in a mold and to provide a method for producing a seamless belt the thickness of which is 50 μm-1 mm, especially at least 80 μm, and can be uniform.例文帳に追加

金型内で高分子材料溶液が波打ったり、表面に風紋状の模様が生じるのを抑制防止し、厚さ５０μｍ以上、特には８０μｍ以上、通常１ｍｍ以下の厚いシームレスベルトの肉厚の均一化を図り得るシームレスベルトの製造方法を提供する。 - 特許庁

In the one side submerged arc welding method using 3 or 4 electrodes with flux as backing, welding is performed by making a V-shaped beveling for a material to be welded with a 25 to 60° groove angle and by applying sealing beads with a height of ≤8 mm to all the wires inside the beveling.例文帳に追加

フラックスを裏当てに使用し、３電極または４電極の電極を使用して行う片面サブマージアーク溶接方法において、被溶接材の開先角度を２５〜６０°のＶ形状の開先とし、該開先内に高さ８ｍｍ以下のシーリングビードを全線に施して溶接する。 - 特許庁