The grinding method and grinding device use a resinoid bond diamond grinding wheel as the grinding wheel, in rotating a grinding wheel of which outer edge is molded in a free curved shape or a circular arc shape, pressing it onto work to move it relatively, and grinding the nonaxisymmetric and aspheric surface shape.例文帳に追加

外縁が自由曲面形状または円弧形状に成形された研削砥石を回転させ、ワークに押し付けて相対的に移動させ、非軸対称・非球面形状の研削加工を行うに当たり、研削砥石としてレジノイドボンドダイヤモンド砥石を用いる研削加工方法及びその加工装置。 - 特許庁

In the method for improving the corrosion resistance of a zinc plated steel sheet, the steel sheet obtained by applying zinc plating comprising, by mass, ≥30% zinc to the surface of a steel sheet is worked, and the worked part of the steel sheet is subjected to ultrasonic impact treatment.例文帳に追加

鋼板の表面に質量％で亜鉛を３０％以上含有する亜鉛系合金めっきを施した鋼板において、該鋼板を加工した後に、該鋼板の加工部分に、超音波衝撃処理を施すことを特徴とする亜鉛系合金めっき鋼板の耐食性改善方法である。 - 特許庁

Moreover, the electric double layer capacitor is obtained by the method for manufacturing the electric double layer capacitor electrode active material, wherein the atom ratio (H/C) of hydrogen to carbon is within the range of 0.35-0.42, further the specific surface area is within the range of 5-65.例文帳に追加

また、本発明に係る電気二重層キャパシタは、上記の電気二重層キャパシタ電極活物質の製造方法によって得られ、炭素に対する水素の原子比（Ｈ／Ｃ）が０．３５〜０．４２の範囲内に、さらに比表面積が５〜６５の範囲内にあることを特徴とする。 - 特許庁

The surface treatment method for an Si-base aluminum alloy consists of a stage for forming an anodically oxidized film 13 on the aluminum alloy containing Si by an electrolyte prepared by mixing phosphate and fluoride and a stage for forming a plating film 14 of an Ni-Cu alloy on the anodically oxidized film.例文帳に追加

Ｓｉ系アルミニウム合金の表面処理方法は、りん酸塩並びにふっ化物を混合した電解液でＳｉを含むアルミニウム合金に陽極酸化被膜１３を形成する工程と、陽極酸化被膜上にＮｉ−Ｃｕ合金のメッキ被膜１４を形成する工程とからなる。 - 特許庁

The method for manufacturing the liquid crystal display device has a process of forming transparent electrodes 7 for driving a liquid crystal on a counter substrate 11, a process of forming columnar spacers 10 on the transparent electrodes 7 and a process of forming an alignment layer 8 on the entire surface of the counter substrate 11.例文帳に追加

液晶表示装置の製造方法は、対向基板１１上に液晶駆動用の透明電極７を形成する工程と、透明電極７上に柱状スペーサ１０を形成する工程と、対向基板１１上全面に配向層８を形成する工程とをこの順に有する。 - 特許庁

The image forming method comprises transferring toner through an electrophotographic system onto the surface of an electrophotographic image receiving sheet having at least one heat insulating layer on a reflective support, primarily fixing the toner in a primary fixing step, and then secondarily fixing the toner to obtain a fixed image in a secondary fixing step.例文帳に追加

反射支持体上に少なくとも１層の断熱層を有する電子写真用受像シート表面に、電子写真方式によりトナーを転写し、一次定着工程により一次定着させた後、さらに二次定着工程により二次定着させ定着画像とする画像形成方法。 - 特許庁

In a molding method at the time of press molding a preform 60 using a metal mold 200, the pressing speed is reduced at a specified timing in order to suppress the generation of the damage on the surface of the optical element after being molded in a process of pressing the preform 60 using the metal mold 200.例文帳に追加

成形用金型２００でプリフォーム６０をプレス成形する際の成形方法であって、成形用金型２００でプリフォーム６０をプレスする過程において、成形後の光学素子の表面に生じる傷の発生を抑えるため、所定のタイミングでプレス速度を遅くする。 - 特許庁

To provide a method for reducing the occurrence of a crack or cutout due to the cutting of a hard coat treated article, especially, a hard coat film high in surface hardness or improved in curling or brittleness or a hard coat film with a functional thin film having an antireflection or anti-staining function.例文帳に追加

ハードコート処理物品、特に、表面の硬度が大きくカールや脆性を改良したハードコートフィルムや、反射防止、防汚などの機能を有する機能性薄膜付きハードコートフィルムなどの裁切断によるクラックや欠けの発生を減少させる方法を提供すること。 - 特許庁

To provide a steel pipe having excellent workability, which has satisfactory shape and surface properties, has excellent workability including a weld zone and is suitably usable for a steel pipe for structures purpose, piping or the like formed by tube drawing, bending, hydroforming or the like, and to provide a method for producing the same.例文帳に追加

形状や表面性状が良好で、溶接部も含めて優れた加工性を有し、特に、伸管、曲げ、ハイドロフォーミング等によって成形される構造用鋼管や配管等に好適に用いることが可能な、加工性に優れた鋼管及びその製造方法を提供する。 - 特許庁

In a manufacturing method of the glass substrate for the magnetic disk including a step for forming glass disks by cutting a cylindrical glass base material 3 vertically to the center axis thereof, a side surface part of the cylindrical glass base material 3 is grained or satin finished when the step is performed.例文帳に追加

円柱状ガラス母材３をその中心軸に対して垂直に切断処理してガラスディスクを作製する工程を含む磁気ディスク用ガラス基板の製造方法であって、円柱状ガラス母材３の側面部は、前記工程時に、砂目または梨地面となっている。 - 特許庁

To provide a photoelectric transfer element which can adopt Ge suitable for TPV generation as a material and adopt a back face electrode type as an electrode structure by a method wherein an element structure capable of fairly decreasing a recomobination loss of carriers on the surface is included.例文帳に追加

表面でのキャリアの再結合損失を大幅に減少させ得る素子構造を有することで、ＴＰＶ発電用に適したＧｅを材料として採用し且つ電極構造として裏面電極型を採用するのを可能にした光電変換素子を提供する。 - 特許庁

The method for manufacturing a droplet ejection head comprises a step of spray coating the nozzle plate surface before a nozzle 33 for ejecting droplets is formed with a water repellent containing a solvent and a fluororesin to form a coating film 48, wherein the solvent has a boiling point of 120°C or higher.例文帳に追加

液滴を吐出するためのノズル３３を形成する前のノズルプレート表面に、溶剤とフッ素樹脂とを含む撥水剤をスプレー塗布して塗膜４８を形成する塗布工程を有し、前記溶剤の沸点が１２０℃以上であることを特徴とする液滴吐出ヘッドの製造方法。 - 特許庁

Although irregularities of surfaces are generated by a CMP method in first copper wiring 103a of a broader width and second copper wiring 103b of a narrower width, the surface of a third insulating film 105 deposited on a second insulating film 104 is planarized by planarizing the second insulating film 104.例文帳に追加

ＣＭＰ法により幅の広い第１の銅配線１０３ａと幅の狭い第２の銅配線１０３ｂにおいて表面に凹凸が発生するが、第２の絶縁膜１０４を平坦化することにより第２の絶縁膜１０４上に堆積する第３の絶縁膜１０５の表面が平坦になる。 - 特許庁

This function recovering method of the pavement removes sediments clogged in the void inside of the water permeable pavement or the drainable pavement, by sprinkling water or hot water and sodium hydrogencarbonate or chemicals mainly composed of the sodium hudrogencarbonate on a surface of the water permeable pavement or the drainable pavement.例文帳に追加

透水性舗装または排水性舗装表面に、炭酸水素ナトリウムまたは炭酸水素ナトリウムを主成分とする薬剤と、水または温水とを散布して、透水性舗装または排水性舗装内部の空隙に詰まった土砂類を除去する舗装の機能回復方法である。 - 特許庁

To provide an inlaying panel material which can accurately form an inlaying pattern even if an inlaying pattern forming part of a surface decorative material has a curved three-dimensional shape and which improves mass productivity at a low manufacturing cost and to provide a method for shaping the same.例文帳に追加

表面化粧材の象嵌模様の形成部が曲面三次元の形状であっても、象嵌模様を高精度に形成できるようにするとともに、量産性を向上して製造コストを低くすることを可能とする象嵌パネル材およびその成形方法を提供する。 - 特許庁

A film made of polymeric material is formed on the entire surface of a lower electrode connected to a thin transistor by a coating method, and then is etched by etching by plasma, thereby allowing selective forming of a polymeric material layer.例文帳に追加

本発明は、薄膜トランジスタと接続される下部電極上に塗布法により全面に高分子系材料からなる膜を形成した後、プラズマによるエッチングによって高分子系材料からなる膜をエッチングし、高分子系材料層の選択的な形成を可能にするものである。 - 特許庁

To provide the manufacturing method of a semiconductor package which does not need a rear-surface tape conventionally required to fix a lead, and prevent the flow of sealing resin upon sealing the resin in the manufacturing process of an batch mold type semiconductor package, and which comprises a process capable of solving conventional problems.例文帳に追加

一括モールドタイプの半導体パッケージの製造工程で、従来必要とされたリード固定用、且つ、樹脂封止の際の封止用樹脂の流れ防止用の裏面テープを不要とし、従来の問題点を解決できる工程の半導体パッケージの製造方法を提供する。 - 特許庁

To provide a semiconductor substrate capable of suppressing the warpage occurring thereon due to high temperature processing without depending on a thick film on the substrate, even when high temperature processing is required after forming a contact electrode film that covers substantially the whole rear surface of the substrate, and to provide a manufacturing method therefor.例文帳に追加

基板裏面の略全面を覆うコンタクト電極膜の成膜後に高温処理を必要とする場合であれ、基板の膜厚によることなく同処理の加熱に起因する基板の反りを抑制することのできる半導体基板およびその製造方法を提供する。 - 特許庁

The method for forming this ink-repellent layer is characterized in that a material having the said derivative is surface-treated with an alcohol solution thereof to be applied.例文帳に追加

この撥インキ層を形成する方法は、極性領域が酸の特性を有する両親媒性有機化合物の少なくとも１つの誘導体を含む物質を、この物質のアルコール溶液を用いて表面を処理することによって塗布することを含んでいることを特徴としている。 - 特許庁

To provide a method for manufacturing a ceramic heater having excellent productivity capable of forming a laminate by screen printing without thinning of a printing element formed at a stepwise part even by screen printing a printing surface having a step and having excellent productivity.例文帳に追加

段差のある印刷面にスクリーン印刷を施しても、この段差部分に形成した印刷体の細りが発生したり、スクリーンが破損したりすることがなく積層体をスクリーン印刷にて形成することができ、生産性に優れるセラミックヒーターの製造方法を提供する。 - 特許庁

The manufacturing method of a light emitting element mounting wiring board 1 on which a light emitting element is mounted includes a bonding process of bonding a substrate part 2 on which the light emitting element is provided and an aluminum reflecting plate 3 undergoing mirror surface processing via a bonding sheet 5.例文帳に追加

発光素子が搭載される発光素子搭載用配線板１の製造方法であって、前記発光素子が設けられる基板部２と、鏡面加工されたアルミニウムからなる反射板３とを、接着シート５を介して接着する接着工程を含むことを特徴とする。 - 特許庁

To obtain a method of manufacturing a thin film solar battery for preventing deterioration of insulating resistance of a cell separation part or short circuit caused by generation of metal residue of a back surface electrode layer in cell separation, and manufacturing a thin film solar battery with excellent power generation efficiency and yield.例文帳に追加

セル分離時における裏面電極層の金属残渣の発生に起因したセル分離部の絶縁抵抗の低下や短絡の発生を防止して発電効率および歩留まりに優れた薄膜太陽電池を製造することができる薄膜太陽電池の製造方法を得ること。 - 特許庁

To reduce working man-hours in arranging resin foam blocks 2a in the lowermost stage by forming the whole upper face of foundation concrete 3 after erecting posts 1, as a flat surface in a lightweight banking method for vertically erecting the post 1 with a fixing base 4 provided at the lower end, using anchor bolts 5 embedded in the foundation concrete 3.例文帳に追加

下端に固定用基板４を備えた支柱１を基礎コンクリート３に埋め込んだアンカーボルト５を利用して垂直に建て込むようにした軽量盛土工法において、支柱１を建て込んだ後の基礎コンクリート３の上面をすべて平坦面となるようにする。 - 特許庁

To provide a CMP abrasive material which is easy in waste liquor treatment, capable of abrading the surface to be abraded of a silicon oxide film and the like at high speed without a mark, and renders a ratio of the abrasion rate of the silicon oxide film to that of silicon nitride film of not smaller than 10, and a method of abrading substrates by using these CMP abrasive materials.例文帳に追加

廃液処理が容易で、酸化珪素膜等の被研磨面を、傷なく、高速に研磨することが可能で、酸化珪素膜研磨速度と窒化珪素膜研磨速度の比を１０以上にするＣＭＰ研磨剤、及びこれらＣＭＰ研磨剤を使用した基板の研磨方法を提供する。 - 特許庁

To provide a continuous casting method for molten steel by which in the case of casting a slab, etc., by applying electromagnetic stirring to molten steel in a mold, defect such as scab and blister, caused by gas bubble and inclusion caught into the surface layer part of the cast slab, is prevented and the cast slab excellent in the quality characteristic is obtained in a good yield.例文帳に追加

鋳型内の溶鋼を電磁攪拌してスラブ等を鋳造する際に、鋳片の表層部に捕捉される気泡や介在物に起因するヘゲ疵やフクレ疵等の欠陥を防止し、歩留りを良くして品質特性に優れた溶鋼の連続鋳造方法を提供する。 - 特許庁

To provide a wall structure using a small piece-shaped member such as a brick or the like and its construction method capable of constructing a beautiful wall having the surface with high accuracy, also having high earthquake resistance, yet reducing the kinds of members to be used and having high workability for both plane section and corner section within a short period of time at a low cost.例文帳に追加

面精度がすぐれ、耐震性もよく、それでいて使用する部材種類も少なくかつ平面部およびコーナー部ともに施工性がよく、美麗な壁を短期間で安価に築造することができるレンガ等小片状部材を用いた壁構造およびその施工方法を提供する。 - 特許庁

In the continuous casting method using the immersion nozzle, the horizontal cross sectional shape of the outer shape of the immersion nozzle 1A disposed below the molten metal surface in a mold or the outer shape of a straightening plate 1B fitted to the immersion nozzle is formed asymmetrically with respect to the center line 11 in the longitudinal direction of the mold.例文帳に追加

浸漬ノズルを用いた連続鋳造方法において、鋳型内湯面下における浸漬ノズル１Ａの外形または浸漬ノズルに取り付けた整流板１Ｂの外形の水平断面形状を鋳型長手方向の中心線11に対して非対称形状とした。 - 特許庁

To provide an inspection method for foreign matter and a device capable of detecting fine foreign matter on the surface, even if a sheet-shaped inspection object has a large width size or comprises a non-translucent material, and of preventing dispersion of a detection sensitivity or a detection minimum size in the width direction of the inspection object.例文帳に追加

シート状の被検査物について、幅寸法が大きかったり、材質が非透光性であっても、表面の微小異物の検出が可能で、また被検査物幅方向における検出感度や検出最小サイズがばらつかない異物検査方法、装置を提供する。 - 特許庁

To provide a construction method of a continuous wall body, able to construct in a narrow land, low in cost, having a water shielding property, possible to clear to treat a pollutant soil at the position of the wall body, and equipped with a function for insolubilizing a pollutant material even if a ground-water containing the pollutant material penetrates from a surface of the wall body.例文帳に追加

狭い土地で施工可能で、安価で、遮水性能があり、壁体位置の汚染土壌を浄化して対応出来、汚染物質を含んだ地下水が壁体の表面から浸透しても汚染物質を不溶化させる機能を備えた連続壁体の築造工法。 - 特許庁

To provide a composite plated material which is obtained by forming a coating film comprising a composite material containing carbon particles in a silver layer on a base material, and which has a high content of carbon particles and contains a large quantity of the carbon particles in its surface part and thereby, has a low friction coefficient and excellent wear resistance; and to provide a method for producing the same.例文帳に追加

銀層中に炭素粒子を含有する複合材からなる皮膜が素材上に形成され、炭素粒子の含有量および表面の炭素粒子の量が多く、摩擦係数が低く且つ耐摩耗性に優れた複合めっき材およびその製造方法を提供する。 - 特許庁

To provide a susceptor wherein the bottoms of counterbores are formed into spherical concaves which are close to a concave curved surface into which a workpiece is bent due to its dead weight, which can prevent the slippage of the workpiece when it is carried in and placed, and which can heat the workpiece with a high in-plane uniformity; and also to provide a method of manufacturing the same.例文帳に追加

ザグリ部の底面を被処理物が自重で撓んだ状態の凹曲面形状に近い球面凹形になすと共に、かつ被処理物の搬入載置時における滑りを回避し、更に被処理物の面内均一性の高い加熱ができるサセプタ及びその製造方法を提供する。 - 特許庁

To obtain a method for forming images by which the wear amount of the surface of a photoreceptor due to the deposition of a carrier or friction with a magnetic brush is decreased even when toner and carrier having smaller particle size are used, and moreover, the deposition of the carrier is prevented, damages in images or decrease in density are prevented even for long-term use.例文帳に追加

より小粒径のトナー及びキャリアを用いた場合にもキャリア付着や磁気ブラシ等の摩擦による感光体表面の減耗量を少なくし、さらには、キャリア付着を防止し、かつ、長期使用においても画像上のキズや濃度低下のない画像形成方法を得る。 - 特許庁

To provide a curable composition for an optical material exhibiting ≥100°C Tg and without causing deterioration such as discoloration on installing it on a surface, an optical material by using the same composition, a method for producing the optical material and a light-generating diode by using the same material.例文帳に追加

１００℃よりも高いＴｇを発現し、かつ、表面実装時に樹脂が着色等の劣化を起こさない光学材料用硬化性組成物、それを用いた光学用材料、光学用材料の製造方法、および光学材料を用いた発光ダイオードを提供することである。 - 特許庁

To provide a method allowing a further efficient and further complicated input, when an input device is provided on a back surface, in a portable electronic device such as a cellular phone, a portable game device or an electronic dictionary, in order to further enlarge a display device and the input device, compared with a conventional device of the same type.例文帳に追加

携帯電話・携帯ゲーム機器・電子辞書等の携帯電子機器において同型機器に比し表示装置及び入力装置をより広くする為に、背面に入力装置を設けた場合に、より効率的及びより複雑な入力を可能とする方法を提供する。 - 特許庁

In the temper mill for steel sheets with which the steel sheet is dryly rolled, this device is a touch mark preventing device of the temper mill for the steel sheet on which gas nozzles for blowing gas for cooling the roll toward the surface part outside the way of sheet of the work rolls are installed and the touch mark preventing method using the same is provided.例文帳に追加

鋼板をドライで圧延する鋼板の調質圧延機において、ワークロールの板道外の表面部分に向けてロール冷却用気体を吹き付ける気体ノズルを設置した鋼板の調質圧延機におけるタッチマーク防止装置、及びそれを用いたタッチマーク防止方法。 - 特許庁

The method for manufacturing the semiconductor device comprises the steps of mounting a solder ball 1 made of a tin-lead alloy containing a tin about 5 wt.% and a lead of about 95 wt.% at a central part 2 and the alloy containing tin 100 wt.% at a surface 3 on an electrode 6 provided on the semiconductor chip 5, and thereafter heating the ball 1 to 230 to 300°C.例文帳に追加

半導体チップ５に設けられた電極６上に、中心部２がスズ約５重量％および鉛約９５重量％の合金からなり、表面３がスズ１００重量％からなる半田ボール１を載置し、その後、これを２３０℃〜３００℃に熱する。 - 特許庁

In the method of coating the glass container, a first coating film containing a metal oxide is formed on the surface of the glass container by hot end coating, a second coating film containing silicon oxide or a silicate is formed on the coated film and, further, a third coating film containing a solid lubricant and a silane coupling agent is formed on the second coating film.例文帳に追加

ガラス容器表面に、ホットエンドコーティングにより金属酸化物を含む第一の被膜を形成し、該被膜上に酸化ケイ素又はケイ酸塩を含む第二の被膜を形成し、更に該第二の被膜上に固体滑剤及びシランカップリング剤を含む第三の被膜を形成する。 - 特許庁

To provide a sputtering target, a backing plate and an instrument in a sputtering device capable of preventing the peeling and scattering of deposit generated from the surface of the target, the backing plate and the instrument in the sputtering device, to which an unnecessary film is deposited, and to provide a roughening method using an electron discharge machining.例文帳に追加

ターゲット、バッキングプレート、スパッタリング装置内の機器の、不要な膜が堆積する面から発生する堆積物の剥離・飛散を防止できるパーティクル発生の少ないスパッタリングターゲット、バッキングプレート又はスパッタリング装置内の機器及び放電加工による粗化方法を提供する。 - 特許庁

To provide a cooling device and a method of manufacturing an electronic device and the cooling device, capable of increasing the transporting amount of hydraulic fluid by improving the lyophilic characteristic of a channel surface with the hydraulic fluid, to increase the amount of vaporization heat in the device and to improve the heat efficiency.例文帳に追加

流路表面の作動液との親液性を向上させることにより作動液の輸液量の増加を可能にし、それによりデバイス内の気化熱量の上昇及び熱効率の向上を可能とする冷却装置、電子機器装置及び冷却装置の製造方法を提供すること。 - 特許庁

The manufacturing method of the solid decorative article 11a has the printing process for printing a wood grain pattern planarly modelled after a wood surface on the film 13a and the molding process wherein the film 13a printed in the printing process is inserted into the mold 41 and subjected to in-mold molding.例文帳に追加

立体加飾品１１ａの製造方法は、木材の表面を平面的に象った杢目柄をフィルム１３ａに印刷する印刷工程と、該印刷工程で印刷されたフィルム１３ａを金型４１内にインサートしてインモールド成形する成形工程とを備える。 - 特許庁

In the method for manufacturing an electrophotographic photoreceptor which forms a photosensitive layer on a conductive base surface with the aid of immersion coating by making a paint containing a photosensitive material overflow, a coating tank has an opening lid and a distance between the opening lid and a liquid level at which the paint overflows is ≤30 mm.例文帳に追加

感光材料を含有する塗料をオーバーフローさせて導電性支持体表面に感光層を浸漬塗布により形成する電子写真感光体の製造方法において、塗布槽が開口蓋を有し、開口蓋と塗料のオーバーフローする液面との距離を３０ｍｍ以下で行う。 - 特許庁

The manufacturing method for an intermediate transfer belt is to continuously carry out a process of extrusion molding of a rear surface rubber layer on a circular cross-sectional mandrel, a process for forming a reinforcing layer thereon, and a process for extrusion-molding of a sheathing rubber layer on the reinforcing layer.例文帳に追加

中間転写ベルトの製造方法において、断面円形のマンドレル上に裏面ゴム層を押出し成型する工程と、その上に補強層を形成する工程と、補強層上に被覆ゴム層を押出し成型する工程とを連続的に行うことを特徴とする。 - 特許庁

To provide a film deposition device for producing a gas barrier laminated body having excellent oxygen and water vapor barrier properties by solving difficulties of long run stability of arcing and the like due to contamination of an electrode and a chamber wall surface, securement of a large area and roll-to-roll securement, which are problems when using a CVD method.例文帳に追加

ＣＶＤ法を用いる場合に問題となる電極やチャンバー壁面の汚染によるアーキング等のロングランの安定性、大面積化、ロール・ツー・ロール化の困難さを解決し、酸素バリア性および水蒸気バリア性に優れた、ガスバリア性積層体を生産する成膜装置を提供する。 - 特許庁

To provide a moisture-proof agent for a dried fruit coated with an acid component, which excellently prevents an acid component from absorbing moisture in providing the surface of a dried fruit with the acid component, a dried fruit coated with acid component and a method for preventing a dried fruit coated with an acid component from absorbing moisture.例文帳に追加

乾燥果実表面に酸味成分を付与する際、酸味成分が吸湿することを防止するのに優れた、酸味成分被覆乾燥果実用の吸湿防止剤、酸味成分被覆乾燥果実及び酸味成分被覆乾燥果実の吸湿防止方法を提供する。 - 特許庁

To provide a method and equipment for shearing a gate which enable attainment of a high speed without necessitating an installation space solely for gate cutting equipment and to obtain a preform which has a smooth sheared surface and of which the residual amount of the gate is very small and uniform.例文帳に追加

ゲートカット装置単独での設置スペースを必要とせずに高速化を図ることができるゲートの剪断方法と装置を提供し、併せてこの装置を用いることよって剪断面が滑らかで、且つゲートの残り量が極めて少なく、また残り量が均一化されているプリフォームを得る。 - 特許庁